Cleanable pigment capable of being applied to silicone rubber and not prone to falling off and preparation method of cleanable pigment

A production method and technology of silicone rubber, which can be applied in the direction of pigment slurry, art paint, coating, etc., can solve the problems of difficult coloring, ineffective cleaning, poor painting performance, etc.

Inactive Publication Date: 2021-11-09
BEIJING DUXIANG EDUCATION TECH CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] For this reason, the embodiment of the present invention provides a pigment that can be painted on silicone rubber, is not easy to fall off and can be cleaned, and its production method, s

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cleanable pigment capable of being applied to silicone rubber and not prone to falling off and preparation method of cleanable pigment
  • Cleanable pigment capable of being applied to silicone rubber and not prone to falling off and preparation method of cleanable pigment
  • Cleanable pigment capable of being applied to silicone rubber and not prone to falling off and preparation method of cleanable pigment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The preparation method of the pigment that can be painted on the silicone rubber that is not easy to fall off and can be cleaned up in this embodiment comprises the following steps:

[0032] S1. Add 16.75% acrylic resin and 0.1% polyethylene glycol in sequence in the batching tank, turn on the high-speed disperser, control the speed at 1200r / min, and stir for 6 minutes;

[0033] S2, then add 15.5% titanium dioxide, 55.25% water, and disperse at high speed for 25 minutes;

[0034] S3, then add 1% propylene glycol, 0.2% triethanolamine, 0.1% sodium secondary alkyl sulfonate, 9.88% polymethacrylate, 0.4% polyether sulfonate, 0.25% branched chain alkyl Sodium benzenesulfonate, 0.4% fatty alcohol polyoxyethylene ether, 0.12% fatty alcohol polyoxyethylene ether carboxylate, 0.05% nonylphenol polyoxyethylene ether, stirred for 10 minutes, and stood still for 25 minutes.

Embodiment 2

[0036] The preparation method of the pigment that can be painted on the silicone rubber that is not easy to fall off and can be cleaned up in this embodiment comprises the following steps:

[0037] S1. Add 16.05% acrylic resin and 0.095% polyethylene glycol in sequence in the batching tank, turn on the high-speed disperser, control the speed at 1000r / min, and stir for 8 minutes;

[0038] S2. Make the fineness of Pigment Red P.R.112 reach 10-15 microns by grinding, add 0.6% Pigment Red P.R.112, and stir for 25 minutes;

[0039] S3, then add 15.6% titanium dioxide, 55.5% water, and disperse at high speed for 20 minutes;

[0040] S4, then add 0.8% propylene glycol, 0.125% triethanolamine, 0.077% sodium alkane sulfonate, 9.95% polymethacrylate, 0.38% polyether sulfonate, 0.25% branched chain alkyl Sodium benzenesulfonate, 0.4% fatty alcohol polyoxyethylene ether, 0.125% fatty alcohol polyoxyethylene ether carboxylate, 0.048% nonylphenol polyoxyethylene ether, stirred for 12 minut...

Embodiment 3

[0042] The preparation method of the pigment that can be painted on the silicone rubber that is not easy to fall off and can be cleaned up in this embodiment comprises the following steps:

[0043] S1. Add 16.5% acrylic resin and 0.05% polyethylene glycol in sequence in the batching tank, turn on the high-speed disperser, control the speed at 1500r / min, and stir for 6 minutes;

[0044] S2. Make the fineness of Pigment Yellow P.Y.151 reach 10-15 microns by grinding, add 1.0% Pigment Yellow P.Y.151, and stir for 20 minutes;

[0045] S3, then add 15.5% titanium dioxide and 55.2% water, and disperse at high speed for 20-30 minutes;

[0046] S5, then add 0.75% propylene glycol, 0.2% triethanolamine, 0.05% sodium alkane sulfonate, 9.87% polymethacrylate, 0.25% polyether sulfonate, 0.2% branched chain alkyl Sodium benzenesulfonate, 0.3% fatty alcohol polyoxyethylene ether, 0.075% fatty alcohol polyoxyethylene ether carboxylate, 0.055% nonylphenol polyoxyethylene ether, stirred for 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The embodiment of the invention discloses a cleanable pigment capable of being applied to silicone rubber and not prone to falling off and a preparation method of the cleanable pigment, and belongs to the technical field of pigments. The pigment is prepared from water, propylene glycol, titanium dioxide, acrylic resin, polymethacrylate, polyether sulfonate, branched chain sodium alkyl benzene sulfonate, fatty alcohol-polyoxyethylene ether, fatty alcohol-polyoxyethylene ether carboxylate, nonylphenol polyoxyethylene ether, secondary alkyl sodium sulfonate, polyethylene glycol and triethanolamine as raw materials. The pigment can be applied to silicon rubber, and has the characteristics of flexibility, difficulty in falling off and capability of being competent for the flexibility of the silicon rubber after being solidified. The silicon rubber is not dyed and can be repeatedly used after the pigment is cleaned, and the cost for purchasing a large number of silicon rubber substrates during silicon rubber painting is saved. The pigment fills the blank of pigment for silicon rubber, and has a wide market prospect.

Description

technical field [0001] The embodiments of the present invention relate to the technical field of pigments, in particular to a pigment that can be painted on silicone rubber, is not easy to fall off and can be cleaned, and a production method thereof. Background technique [0002] Silicone rubber refers to the rubber whose main chain is composed of silicon and oxygen atoms alternately, and there are usually two organic groups attached to the silicon atoms. Silicone rubber is divided into high-temperature silicone rubber and room-temperature silicone rubber. High-temperature silicone rubber is mainly used to manufacture various silicone rubber products, while room-temperature silicone rubber is mainly used as adhesives, potting materials or molds. Due to the low surface energy of silicone rubber, it is difficult to spread the prepared coating on its surface, and the adhesion effect is poor. [0003] At present, there are protective inks coated on silicone rubber on the market...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/04C09D17/00C09D5/06C09D7/20C09D7/61C09D7/65C09D7/63C09B67/20C09B67/36C08J7/04C08L83/04
CPCC09D133/04C09D17/008C09D5/06C09D7/20C09D7/61C09D7/65C09D7/63C09B67/0079C09B67/006C08J7/04C08L2205/025C08L2205/02C08L2205/035C08K2003/2241C08J2383/04C08L33/08C08L71/02C08K3/22C08K5/42C08K5/0041C08L83/04C09D17/00
Inventor 虎盈
Owner BEIJING DUXIANG EDUCATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka