Recyclable prefabricated runway as well as preparation method and recycling method thereof

A prefabricated, runway technology, applied to chemical instruments and methods, roads, roads, etc., can solve the problems of unrecyclable and difficult to recycle, and achieve high efficiency of on-site paving, safe, non-toxic and environmentally friendly production process, and high production efficiency high effect

Inactive Publication Date: 2021-12-21
湖南盛亚体育实业有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the vulcanized rubber roll runway itself is a thermosetting material, which cannot be recycled; polyurethane slurry and other auxiliary materials are also difficult to recycle when paving the runway on site because of the addition of thermosetting materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Recyclable prefabricated runway as well as preparation method and recycling method thereof
  • Recyclable prefabricated runway as well as preparation method and recycling method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0067] A method for preparing a recyclable prefabricated runway described in any one of the above, comprising the following steps:

[0068] Weighing surface layer raw materials by weight, mixing and granulating to obtain surface layer granules;

[0069] Weighing the bottom layer raw materials by weight, mixing and granulating to obtain the bottom layer particles;

[0070] The surface layer particles and the bottom layer particles are extruded separately under heating conditions to obtain the surface layer and the bottom layer, which are compounded to form a double-layer film;

[0071] The double-layer film is cut, rolled, cooled, trimmed to obtain the finished product.

[0072] The application also provides the preparation method of the above-mentioned recyclable prefabricated runway, which has simple process, low energy consumption, adopts normal pressure thermoplastic processing technology, can be used without vulcanization, can be continuously produced on the assembly line...

Embodiment 1

[0096] A recyclable prefabricated runway roll, including a prefabricated surface layer and a bottom layer;

[0097] Wherein the surface layer is mainly prepared from the following ingredients in parts by weight:

[0098]50 parts by weight of polyurethane elastomer, 50 parts by weight of SEBSYH-503T, 25 parts by weight of polypropylene, 15 parts by weight of PP-g-MAH, 200 parts by weight of calcium carbonate, 35 parts by weight of emery, 55 parts by weight of white oil, stearin 3 parts by weight of acid, 3 parts by weight of polyethylene wax, 1 part by weight of antioxidant 1010, 2 parts by weight of antioxidant 168, 0.5 part by weight of light stabilizer UV-770DF, 0.5 part by weight of light stabilizer UV-326, oxidation 30 parts by weight of iron red;

[0099] The bottom layer is mainly prepared from the following ingredients in parts by weight:

[0100] 50 parts by weight of polyurethane elastomer, 50 parts by weight of SEBSYH-503T, 25 parts by weight of polypropylene, 15 p...

Embodiment 2

[0110] A recyclable prefabricated runway roll, including a prefabricated surface layer and a bottom layer;

[0111] Wherein the surface layer is mainly prepared from the following ingredients in parts by weight:

[0112] 50 parts by weight of polyurethane elastomer, 50 parts by weight of SEBSYH-503T, 25 parts by weight of polypropylene, 15 parts by weight of PP-g-MAH, 200 parts by weight of calcium carbonate, 20 parts by weight of emery, 55 parts by weight of white oil, stearin 3 parts by weight of acid, 3 parts by weight of polyethylene wax, 1 part by weight of antioxidant 1010, 2 parts by weight of antioxidant 168, 0.5 parts by weight of light stabilizer UV-770DF, 0.5 parts by weight of light stabilizer UV-327, oxidation 30 parts by weight of iron red;

[0113] The bottom layer is mainly prepared from the following ingredients in parts by weight:

[0114] 50 parts by weight of polyurethane elastomer, 50 parts by weight of SEBSYH-503T, 25 parts by weight of polypropylene, 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
elastic recovery rateaaaaaaaaaa
elastic recovery rateaaaaaaaaaa
Login to view more

Abstract

The invention discloses a recyclable prefabricated runway. The runway comprises a surface layer and a bottom layer which are compounded after prefabrication and molding, wherein the surface layer comprises a polyurethane elastomer, an SEBS thermoplastic elastomer, polypropylene, maleic anhydride grafted polypropylene, calcium carbonate, emery, white oil, stearic acid, polyethylene wax, an antioxidant, a light stabilizer and a pigment in specific parts by weight; the bottom layer is prepared from a polyurethane elastomer, an SEBS thermoplastic elastomer, polypropylene, maleic anhydride grafted polypropylene, polyethylene vinyl acetate, calcium carbonate white oil, stearic acid, polyethylene wax, an antioxidant, an AC foaming agent and pigment in specific parts by weight. The invention also provides a preparation method and a recycling method of the recoverable prefabricated runway. According to the recyclable prefabricated runway and the preparation method and the recycling method thereof, the performance is excellent, safety and environment friendliness are achieved, and all old runways can be recycled and reprocessed.

Description

technical field [0001] The application relates to the technical field of sports ground materials, in particular to a recyclable prefabricated runway and its preparation method and recycling method. Background technique [0002] Plastic track, also known as all-weather track and field track, is usually composed of polyurethane prepolymer, mixed polyether, waste tire rubber, EPDM rubber particles or PU particles, and pigments, additives, fillers, etc. The plastic runway has the characteristics of good flatness, high compressive strength, appropriate hardness and elasticity, and stable physical properties. It has certain anti-ultraviolet ability and aging resistance. It is internationally recognized as an excellent all-weather outdoor sports floor material. [0003] At present, polyurethane plastic runways are generally made of EPDM rubber particles, polyurethane slurry and other auxiliary materials on-site pouring and paving. However, the on-site pouring and paving construct...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/04C08L53/02C08L23/12C08L51/06C08L91/00C08L23/06C08K3/26C08K3/34C08K5/09C08J9/10C08L23/08B32B25/04B32B25/08B32B25/14B32B27/08B32B27/40E01C13/04
CPCC08L75/04C08L53/025C08J9/103C08J9/0061C08J9/0023C08J9/0066C08J9/0095B32B25/14B32B25/042B32B25/08B32B27/40B32B27/08E01C13/045B32B2250/24C08K2003/265C08J2375/04C08J2353/02C08J2423/12C08J2451/06C08J2423/08C08J2491/00C08J2423/06C08J2203/04C08L23/12C08L51/06C08L91/00C08L23/06C08K3/26C08K3/34C08K5/09
Inventor 郭合平易屏郭小平郭瑞郭志方易芳
Owner 湖南盛亚体育实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap