Starry sky glaze formula and firing manufacturing method

A production method and glaze technology, which is applied in the field of ceramics, can solve the problems of difficult to achieve good application of starry sky glaze, few preparation methods, high product scrap rate, etc., and achieve the effect of simple and reliable firing method, high ornamental value and high gloss

Pending Publication Date: 2022-03-08
郑小平 +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Glaze has been widely used in people's daily life because of its good smoothness. The key to Jun porcelain lies in the glaze. Different firing processes produce different changes in glaze color, and the formula of glaze also affects the outer color of Jun porcelain. An important factor is also the key factor that causes Jun porcelain to enter the kiln with one color and exit the kiln with various colors. In the prior art, there are few formulas and preparation methods for star...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] In order to make the technical means, creative features, goals and effects achieved by the present invention easy to understand, the present invention will be further described below in conjunction with specific embodiments.

[0013] This specific embodiment adopts the following technical scheme: a starry sky glaze, including a bottom glaze glaze and a surface glaze glaze, and the bottom glaze glaze is composed of the following raw materials in weight percentage: potassium feldspar 15%, albite feldspar 15%, quartz 23%, kaolin 7.5%, dolomite 3%, calcium carbonate 5.5%, barium carbonate 5%, glass 8%, zirconium silicate 9%, black material 9%; described surface glaze glaze is composed of the following Raw material composition in weight percent: A-38 feldspar 16%, albite 16%, Hunan black clay 3.6%, zinc oxide 1%, talc 3%, magnesium carbonate 2%, calcium borate 1.2%, ashes 40%, oxide Iron 4%, cerium oxide 3.2%, boron carbonate 4%, phosphorescent powder 6%.

[0014] A starry ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a starry sky glaze formula and a firing manufacturing method, the starry sky glaze formula comprises a ground glaze material and a cover glaze material, the ground glaze material comprises the following raw materials in percentage by weight: 15% of potassium feldspar, 15% of albite, 23% of quartz, 7.5% of kaolin, 3% of dolomite, 5.5% of calcium carbonate, 5% of barium carbonate, 8% of glass, 9% of zirconium silicate and 9% of black pigment; the cover glaze is prepared from the following raw materials in percentage by weight: 16% of A-38 feldspar, 16% of albite, 3.6% of Hunan black pottery clay, 1% of zinc oxide, 3% of talc, 2% of magnesium carbonate, 1.2% of calcium borate, 40% of bone ash, 4% of ferric oxide, 3.2% of cerium oxide, 4% of boron carbonate and 6% of phosphorescent powder. The preparation method is simple, the surface of the prepared starry sky glaze jun porcelain can refract a colorful glaze effect under light, the yield is high, and the ornamental value is high.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a starry sky glaze formula and a firing production method. Background technique [0002] Glaze has been widely used in people's daily life because of its good smoothness. The key to Jun porcelain lies in the glaze. Different firing processes produce different changes in glaze color, and the formula of glaze also affects the outer color of Jun porcelain. An important factor is also the key factor that causes Jun porcelain to enter the kiln with one color and exit the kiln with various colors. In the prior art, there are few formulas and preparation methods for starry sky glaze, which is not easy to fire, and the product scrap rate is high. The product has low mechanical strength, high energy consumption, high production cost, and it is difficult to realize the good application of starry sky glaze on Jun porcelain, thereby limiting the artistic appreciation and commercial value of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/00C04B41/89
CPCC03C8/00C04B41/89C04B41/52C04B41/5022C04B41/4535C04B41/0072
Inventor 郑小平郑海峰
Owner 郑小平
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products