Jade green Jun porcelain glaze

A technology of emerald green and Jun porcelain, applied in the field of Jun porcelain, can solve the problem of single glaze color, and achieve the effect of good fluidity, good gloss, and colorful glaze

Inactive Publication Date: 2018-11-16
温书强
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But whether it is Yue Kiln Celadon or Xing Kiln White Porcelain, their glaze color is single, either blue or white, without exception.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] An emerald green Jun porcelain glaze is prepared from the following raw materials in parts by weight: 15 parts of anorthite, 15 parts of calcite, 15 parts of quartz, 10 parts of chromium oxide and 2 parts of borax.

[0022] The preparation method of above-mentioned emerald green Jun porcelain glaze comprises the following steps:

[0023] (1) Weigh the above-mentioned anorthite, calcite, quartz, chromium oxide and borax into a ball mill to pulverize them, mix them evenly and sieve to obtain the mixture powder;

[0024] (2) Put the mixture powder in a crucible for smelting. The crucible is generally set on the flue between the kiln and the chimney, and a supplementary dye room is set under the furnace. When the heat of the flue gas is insufficient or the kiln stops burning, the It can be roasted in a supplementary combustion chamber. There is a small hole on the bottom of the crucible, which is blocked with a hard quartz ball. When the mixture powder is melted into a flui...

Embodiment 2

[0027] An emerald green Jun porcelain glaze is prepared from the following raw materials in parts by weight: 25 parts of anorthite, 25 parts of calcite, 25 parts of quartz, 15 parts of chromium oxide and 5 parts of borax.

[0028] The preparation method is the same as above.

Embodiment 3

[0030] An emerald green Jun porcelain glaze is prepared from the following raw materials in parts by weight: 20 parts of anorthite, 20 parts of calcite, 20 parts of quartz, 12 parts of chromium oxide and 3 parts of borax.

[0031] The preparation method is the same as above.

[0032] The calcination temperature in the crucible is 1040-1165°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a jade green Jun porcelain glaze, which is prepared from the following raw materials: anorthite, calcite, quartz, chromium oxide and borax. The formula adopted by the invention is different from the traditional formula, the natural raw materials cooperate with each other, and the prepared Jun porcelain glaze has stereoscopic impression, good fluidity and luster, and the Jun porcelain fired from the glaze provided by the invention has bright and smooth glaze color, and the glaze beauty is richer and more colorful.

Description

technical field [0001] The invention belongs to the technical field of Jun porcelain, and in particular relates to an emerald green Jun porcelain glaze. Background technique [0002] Jun porcelain originated in the Eastern Han Dynasty. It is one of the five famous kiln porcelains in the Song Dynasty. Famous for its unique kiln transformation art, it has the reputation of "gold is priceless and Jun porcelain is priceless" and "a family with a lot of money is not as good as a piece of Jun porcelain". It is a unique national treasure porcelain in Shenhou Town, Yuzhou City, Henan Province. With its simple shape, exquisite craftsmanship, complex glaze matching, and the magical kiln transformation of "one color in the kiln, a variety of colors in the kiln", the lakes and mountains, clouds and mist, humans and animals Flowers, birds, insects, fish, etc. are known as the first of China's "Five Famous Porcelains" for their infinitely changing graphic colors and wonderful charm. [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/02C03C8/14
CPCC03C8/02C03C8/14
Inventor 温书强
Owner 温书强
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com