Anti-fouling nano easy-to-clean liquid and preparation method thereof, and preparation method of anti-fouling nano easy-to-clean ceramic

A nano- and small-molecule technology, applied in coatings and other directions, can solve the problems of less surface modification of silicone, anti-fouling and anti-fouling problems, etc.

Active Publication Date: 2022-04-15
FOSHAN CITY GANI CERAMICS CO LTD +2
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are relatively few researches on silicone surface modification in the field of ceramic antifouling, and there is no ceramic product with excellent antifouling performance on the market; especially for unglazed tiles, the problem of antifouling and antifouling has always been a problem. Pain points in the industry that have not been resolved so far

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-fouling nano easy-to-clean liquid and preparation method thereof, and preparation method of anti-fouling nano easy-to-clean ceramic
  • Anti-fouling nano easy-to-clean liquid and preparation method thereof, and preparation method of anti-fouling nano easy-to-clean ceramic
  • Anti-fouling nano easy-to-clean liquid and preparation method thereof, and preparation method of anti-fouling nano easy-to-clean ceramic

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037]Anti-fouling nano-cleaning liquid, its composition is: 60 parts of hexamethyldisiloxane, 30 parts of hydroxy silicone oil, 30 parts of ethanol silica sol, 1 part of dibutyltin dilaurate, 8 parts of 3-isocyanatopropyl triethyl Oxysilane, 20 parts of 3-mercaptopropyltrimethoxysilane.

[0038] First add hexamethyldisiloxane, hydroxy silicone oil, ethyl alcohol silica sol, 3-mercaptopropyltrimethoxysilane and dibutyltin dilaurate into the reaction kettle in sequence, and heat to 55°C under stirring conditions. After reacting for 2 hours, add 3-isocyanatopropyltriethoxysilane to the system, keep the temperature and stir for another 1 hour, stop stirring and cool to obtain the anti-fouling nano-cleaning liquid.

[0039] Apply the above-mentioned anti-fouling nano-easy-cleaning liquid evenly on the low-gloss tiles by polishing and wiping equipment, bake at 270°C for 10 minutes, and obtain anti-fouling nano-easy-cleaning tiles after cooling.

Embodiment 2

[0041] Anti-fouling nano-cleaning liquid, its composition is: 30 parts of hexamethyldisiloxane, 20 parts of dimethyldimethoxysilane, 20 parts of vinyltrimethoxysilane, 30 parts of hydroxyl silicone oil, 40 parts of ethyl alcohol silicon Sol, 3 parts of dibutyltin dilaurate, 15 parts of 3-isocyanatopropyltriethoxysilane, 30 parts of 3-mercaptopropyltrimethoxysilane.

[0042] First hexamethyldisiloxane, dimethyldimethoxysilane, vinyltrimethoxysilane, hydroxyl silicone oil, ethyl alcohol silica sol, 3-mercaptopropyltrimethoxysilane and dibutyltin dilaurate in order Add to the reaction kettle one by one, heat to 60°C under agitation, react for 2 hours, then add 3-isocyanatopropyl triethoxysilane to the system, keep the temperature and stir for another 1 hour, stop stirring and cool down Finally, the anti-pollution nanometer easy-to-clean liquid can be obtained.

[0043] Apply the above-mentioned anti-fouling nano-easy-cleaning liquid evenly on the low-gloss tiles by polishing and...

Embodiment 3

[0045] Anti-fouling nano-cleaning liquid, its composition is: 30 parts of hexamethyldisiloxane, 20 parts of dimethyldimethoxysilane, 20 parts of vinyltrimethoxysilane, 30 parts of hydroxyl silicone oil, 40 parts of ethyl alcohol silicon Sol, 2 parts of dibutyltin dilaurate, 20 parts of 3-isocyanatopropyl triethoxysilane, 20 parts of 3-mercaptopropyl triethoxysilane.

[0046] First hexamethyldisiloxane, dimethyldimethoxysilane, vinyltrimethoxysilane, hydroxyl silicone oil, ethyl alcohol silica sol, 3-mercaptopropyl triethoxysilane and dibutyltin dilaurate according to Sequentially added to the reaction kettle, heated to 60°C under stirring conditions, and reacted for 2 hours, then added 3-isocyanatopropyltriethoxysilane to the system, kept the temperature and stirred for 1 hour, stopped stirring and After cooling, the anti-pollution nanometer easy-to-clean liquid can be obtained.

[0047] Apply the above-mentioned anti-fouling nano-easy-cleaning liquid evenly on the low-gloss ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
penetration depthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of ceramic tile surface anti-fouling easy-cleaning materials, and particularly discloses an anti-fouling nanometer easy-cleaning liquid and a preparation method thereof, and an anti-fouling nanometer easy-cleaning ceramic preparation method, the anti-fouling nanometer easy-cleaning liquid comprises, by weight, 40-80 parts of micromolecule organosiloxane, 10-40 parts of hydroxyl silicone oil, 5-40 parts of ethanol silica sol, 0.1-5 parts of a catalyst, 5-30 parts of isocyanate silane, and 10-40 parts of a mercapto silane coupling agent. The invention further discloses a preparation method of the organic silicon nano easy-cleaning liquid and a method for preparing anti-fouling nano easy-cleaning ceramic from the organic silicon nano easy-cleaning liquid. The anti-fouling nano easy-to-clean liquid is simple in preparation process, safe, non-toxic, green, environment-friendly, durable and efficient in anti-fouling and easy-to-clean effect and long in service life, and caters to the pursuit of people for clean and comfortable living space.

Description

technical field [0001] The invention belongs to the field of anti-fouling and easy-cleaning materials for ceramic tile surfaces, in particular to an anti-pollution nanometer easy-cleaning liquid and a preparation method thereof, and a preparation method of an anti-fouling nanometer easy-cleaning ceramic. Background technique [0002] In daily life, many consumers are troubled by the difficulty of removing dirt on tiles. This is the same as accidentally staining a piece of oil on brightly colored clothes. are very concerned. In terms of anti-fouling performance, the national standard only divides glazed tiles into 5 levels, but there is no clear requirement for unglazed tiles. Although the water absorption rate of qualified porcelain polished tiles on the market is relatively close, the antifouling ability is quite different. The antifouling ability of the product is not only related to the closed porosity, but also related to other properties of the polished tiles, such as ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/84C09D183/08C09D183/04C09D7/61
CPCC04B41/5089C04B41/84C04B41/009C09D183/08C09D7/61C04B41/4961C04B41/4944C04B41/4922C04B41/49C04B41/0072C08L83/04C08K3/36
Inventor 李志林梁海潮
Owner FOSHAN CITY GANI CERAMICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com