Manufacturing method of composite three-dimensional woven fabric

A manufacturing method and a three-dimensional technology, which can be used in textiles and papermaking, textiles, fabrics, etc., and can solve problems such as uneven thickness of fabrics and discomfort in use.

Pending Publication Date: 2022-08-02
浙江巴贝纺织有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Three-dimensional fabrics mostly use surface bumps to achieve three-dimensional effect display, but there will be defects of uneven fabric thickness
Especially when applied to bedding and wearing, the unevenness of this structure can easily lead to discomfort

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of composite three-dimensional woven fabric
  • Manufacturing method of composite three-dimensional woven fabric
  • Manufacturing method of composite three-dimensional woven fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The present embodiment is a manufacturing method of a composite three-dimensional woven fabric, comprising the following steps:

[0032] (1) Weaving: using such as Figure 1-3 Weaving in the manner shown.

[0033] (2) Singeing: The fabric formed in step (1) is singeing to remove the hairiness on the upper and lower surfaces of the fabric.

[0034] (3) Cold heap: The singeed fabric is super-decomposable enzyme solution (Nobafex THN-20L, 1g / L, pH=4.5, T=35℃), and the feeding speed is 150m / min. The decomposing enzyme solution decomposes the surface material of the fabric, and makes the fabric swell to a certain extent at 30 °C for static treatment.

[0035] (4) Washing with water: washing with water at 70°C at a speed of 50m / min; removing impurities such as decomposing enzymes and decomposition products.

[0036] (5) Mercerizing: 180g / L of caustic soda is used to make the cloth surface bright. During this process, the cloth surface shrinks, the interweaving structure is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a manufacturing method of a composite three-dimensional woven fabric, and belongs to the technical field of lappet woven fabrics with special purposes. Comprising a three-dimensional part, a cotton pressing part and a metal wire part, the three-dimensional part and the cotton pressing part alternately appear in a cross mode, and the metal wire part is arranged between the interior of the cotton pressing part and the surface of the cotton pressing part in a light and shade mode. The method is applied to woven fabric processing, and the fabric can be endowed with a three-dimensional effect.

Description

technical field [0001] The application relates to a manufacturing method of a composite three-dimensional woven fabric, which belongs to the technical field of embossed woven fabrics with special purposes. Background technique [0002] Most of the three-dimensional fabrics rely on the surface unevenness to display the three-dimensional effect, but there will be defects of uneven thickness of the fabric. Especially when applied to bedding and taking, the unevenness of this structure can easily lead to discomfort in use. SUMMARY OF THE INVENTION [0003] In view of this, the present application provides a manufacturing method of a composite three-dimensional woven fabric with both concave-convex three-dimensional and flashing effects. [0004] Specifically, this application is achieved through the following solutions: [0005] A manufacturing method of a composite three-dimensional woven fabric, [0006] (1) Using multiple sets of weft yarns, multiple sets of first warp y...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D13/00D03D21/00D03D15/67
CPCD03D13/00D03D21/00D03D15/67
Inventor 王维扬