Thermal contracting directional memory polyvinyl chloride pipe and manufacture thereof

A polyvinyl chloride and manufacturing method technology, applied in the field of materials, can solve problems such as difficulty in forming memory, non-directional memory, and inability to promote the production of memory-type polyvinyl chloride pipes, etc., and achieve the effect of long service life and wide application range

Inactive Publication Date: 2007-07-18
徐益鑫
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method produces a PVC film with memory properties. The memory formed by the film is not directional, and it cannot be extended to the production of memory-type PVC pipes. Because the thickness of the pipe wall is much larger than that of the film, it is difficult to form during production. memory, especially directed memory

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1, radial heat shrinkable directional memory polyvinyl chloride pipe, the manufacturing method is first to extrude the polyvinyl chloride pipe, the two ends of the pipe are blocked, and a metal pipe with a diameter larger than the pipe material and a number of through holes is set on the radial pipe wall. Tube, the vertical length of the metal tube is the sum of the length of the tube, the length of the resistance head and the length of the air valve, which means that there is no room for longitudinal extension of the tube, fix the limit tube, soak it in a water bath at about 100°C to soften it, and inflate the tube while soaking , expanding the tube while softening, quenching to room temperature for setting, degassing and decompression, and withdrawing from the limiting tube.

Embodiment 2

[0013] Embodiment 2, longitudinal heat-shrinkable directional memory polyvinyl chloride pipe, the manufacturing method is to first extrude the polyvinyl chloride pipe with anti-aging agent, the two ends of the pipe are blocked, and the inner diameter of the ferrule is equal to the outer diameter of the pipe and radial A number of metal tubes with through-holes are set on the tube wall. The longitudinal length of the metal tube is greater than the control value of the tube length. Heat and soften in a water bath at about ℃, then cool the expanded tube to room temperature, release the pressure in the tube, and exit the limiting tube.

Embodiment 3

[0014] Embodiment 3, with reference to Examples 1 and 2, change the length and inner diameter of the limit metal pipe, and use the same method to manufacture a directional memory polyvinyl chloride pipe with shrinkage in the radial and longitudinal directions, wherein the formed polyvinyl chloride pipe When adding external additives such as antifungal agents and flame retardants, the plastic pipe is first softened with an oil bath at 110°C, then pressurized and expanded, cooled to room temperature and shaped, and the limiting metal pipe is removed after depressurization.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A polyvinyl chloride pipe with radial and / or longitudinal thermal directional shrinking memory function is prepared from polyvinyl chloride through shaping pipe, blocking both ends, arranging it in a limiter, filling high-pressure air in while heating it for expansion, cooling and releasing pressure.

Description

technical field [0001] The invention relates to the field of materials, in particular to a method for manufacturing polyvinyl chloride pipes with thermal shrinkage orientation memory. technical background [0002] Thermal shrinkage memory of polymer materials has been applied in many occasions. For example, two materials (steel and plastic) with different thermal expansion coefficients (steel and plastic) can be fixed and compounded by using thermal shrinkage memory. It can effectively prevent heat delamination during use. It is especially advantageous in pipe compounding. However, the existing heat-shrinkable materials are usually made of polyethylene, and they need to be irradiated with high-intensity rays to form memory. As described in Chinese patent 00122353.4, heat-shrinkable pipe fittings are made with polyethylene additives as raw materials. The pipe fittings are cross-linked and modified by gamma ray irradiation. Because ordinary polyethylene pipes do not have hea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F16L9/12B29C35/00
Inventor 徐益鑫
Owner 徐益鑫
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com