Magnesium alloy radiator and mfg. method thereof
The technology of a heat sink and its manufacturing method, which is applied in the field of magnesium alloy heat sink and its manufacturing, can solve the problems of large specificity and low comprehensive heat dissipation capacity of aluminum alloy heat sink, and achieve the effect of light weight and good heat dissipation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment Construction
[0007] As mentioned above, a semi-continuous cast ingot of magnesium alloy is first prepared, its composition is: Mg88%, Al9%, Zn0.5%, Mn0.2%, RE2%, other composition requirements meet the content of the invention The stated range of ingredients. The diameter of the semi-continuous cast ingot is 100 mm, which is cut into a length of 400 mm and used as an extruded ingot for the next step of production. For the alloy of this composition, the extrusion parameters are: extrusion temperature 300 degrees, extrusion cylinder temperature 220 degrees, exit speed 5 m / min, extrusion ratio 80:1. The extruded profile semi-finished product can then be cut and processed to complete the production of magnesium alloy radiator fins.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap