Palladium-aluminium oxide catalyst and its preparation process

A technology of alumina and catalyst, applied in the field of palladium-alumina catalyst and its preparation, can solve the problems of complicated operation process, questionable firmness of the palladium plating layer, etc., and achieves the advantages of reducing the thickness of the Pd layer, saving costs, and reducing the amount of Pd. Effect

Inactive Publication Date: 2005-06-08
FUZHOU UNIV
View PDF3 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because this method uses a dry method to impregnate palladium salt, the firmness of the palladium coating is questionable, and the operation process is also complicated.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0010] The preparation method of the catalyst of the present invention adopts normal temperature (10-45°C) impregnation method, and is characterized in that the preparation process includes the following steps: (a) impregnating the alumina carrier with alkaline earth metal nitrate or acetate solution, and The temperature is 500-995°C (depending on the starting crystal phase of the alumina used) to convert the alkaline earth metal salts into oxides; (b) add an appropriate amount of palladium chloride and an equal weight of sodium chloride (or take the molar amount of sodium and palladium) Sodium chloride and palladium chloride with a ratio of 2:1) are dissolved in water to form sodium chloride palladium (NaCl 2 PdCl 4 ) aqueous solution, the temperature of the immersion solution is about 10-45°C; (c) a certain amount of dry pre-coated alkaline earth metal oxide with a BET surface area of ​​60-130m 2 / g of alumina is added to the sodium chloride palladium solution, or the sodiu...

Embodiment 1

[0017] Weigh 30g γ-Al 2 o 3 As a carrier, its shape and size are φ3×5-20 (mm) columnar, impurity Na 2 O2 / g in a 250ml glass beaker. Put 18ml concentration of 0.8271mol / L Mg(NO 3 ) 2 The aqueous solution is poured into the above-mentioned alumina and stirred to make it absorb evenly. will absorb Mg(NO 3 ) 2 The alumina after the aqueous solution is placed in an oven at about 80-120 ° C for about 60 minutes, then transferred to a high-temperature furnace and calcined at 900-995 ° C for ~ 10 hours in the atmosphere, and then lowered to room temperature. As a benchmark, the loading of MgO on the carrier is about 2%wt.

[0018] Place the alumina carrier after the above treatment in a 250ml glass beaker, and pour 70ml of Na 2 PdCl 4 solution, impregnated for 60 min under slow stirring, and after filtering out the catalyst and draining, washed with deionized water until the washing water was washed with 2% AgNO 3 until no chloride ions were detected in the solution. Filte...

Embodiment 2

[0022] Repeat the process of embodiment 1, just the Ca(CH 3 COO) 2 aqueous solution. Based on the weight of the alumina carrier, the weight content of CaO on the carrier is about 1%, the weight content of metal palladium is 0.205%, and the thickness of the palladium layer on the catalyst is 55 μm.

[0023] The catalyst activity was evaluated under the same conditions as in Example 1, and the evaluation results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
radiusaaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A Pd-aluminium oxide catalyst is composed of the Al2O3 as carrier which has been coated by the oxide of alkali earth metal and calcined, and the Pd a5 active component, and is prepared by dipping method. Its advantages are high catalytic activity and less consumption of Pd (0.2%).

Description

Technical field: [0001] The invention relates to a metal catalyst and a preparation method thereof, in particular to a palladium-alumina catalyst and a preparation method thereof. Background technique: [0002] Anthraquinone method is currently the world's largest production of H 2 o 2 the most widely used method. Palladium on alumina or other platinum group metal catalysts are the most commonly used hydrogenation catalysts for this process. In order to continuously improve the performance of catalysts and reduce the amount of expensive platinum group metals, people have done a lot of work on the impregnation process of platinum group metals (such as palladium) and the selection and modification of supports for a long time. [0003] It can be seen through searching that US Patent No. 4,061,598 (1977.12) discloses a preparation method of a palladium-alumina catalyst. The patent uses γ-Al 2 o 3 or δ-, θ-Al 2 o 3 As the carrier, first impregnate the alumina carrier with...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/44B01J37/02
Inventor 王榕李敏超林墀昌陈天文林建新
Owner FUZHOU UNIV
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com