Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Process for manufacturing super capacitor battery

A supercapacitor battery and supercapacitor technology, applied in the field of electrochemistry, can solve the problems of supercapacitor battery electrode slurry preparation and electrode coating difficulties, large differences in physical and chemical properties, etc., achieve excellent cycle stability, and avoid uneven ratio The effect of accurate and excellent ultra-high rate charge and discharge capabilities

Inactive Publication Date: 2010-02-17
CENT SOUTH UNIV
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In view of the large difference in physical and chemical properties between lithium-ion battery electrode materials and supercapacitor electrode materials in supercapacitor batteries, the solvent, binder, solid content, and even the drying temperature and speed are affected during the preparation and coating of electrode materials. Requirements are not the same, thus the electrode slurry preparation of supercapacitor battery and the problem of electrode coating difficulty, the invention provides a kind of manufacturing method of supercapacitor battery electrode and supercapacitor battery, concrete steps are as follows:

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for manufacturing super capacitor battery
  • Process for manufacturing super capacitor battery
  • Process for manufacturing super capacitor battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] LiFePO 4 As a positive electrode active material for lithium-ion batteries, it is mixed with binders, conductive agents, additives, solvents, etc. to prepare LiFePO 4 Positive slurry. Graphite is used as the negative electrode active material of lithium-ion batteries, mixed with binders, conductive agents, additives, solvents, etc. to prepare graphite negative electrode slurry. Activated carbon is used as the supercapacitor electrode active material, mixed with binders, conductive agents, additives, solvents, etc. to prepare activated carbon slurry.

[0033] With aluminum foil as the current collector, according to the attached figure 1 ways to alternately coat LiFePO 4 Positive electrode slurry and activated carbon slurry, control the mass ratio of lithium-ion battery electrode material to supercapacitor electrode material to 1, then dry, roll film, and cut to make positive electrode sheet of supercapacitor battery.

[0034] With copper foil as the current collecto...

Embodiment 2

[0039] LiFePO 4 As a positive electrode active material for lithium-ion batteries, it is mixed with binders, conductive agents, additives, solvents, etc. to prepare LiFePO 4 Positive slurry. Graphite is used as the negative electrode active material of lithium-ion batteries, mixed with binders, conductive agents, additives, solvents, etc. to prepare graphite negative electrode slurry. Activated carbon is used as the supercapacitor electrode active material, mixed with binders, conductive agents, additives, solvents, etc. to prepare activated carbon slurry.

[0040] The lithium-ion battery electrode LiFePO 4 The positive electrode slurry and the graphite negative electrode slurry are coated on aluminum foil and copper foil respectively, and after drying, rolling, and cutting, they are respectively made into positive electrode sheets and negative electrode sheets of lithium-ion batteries, and assembled with separators to form lithium-ion battery roll cores .

[0041] The act...

Embodiment 3

[0046] LiFePO 4 As a positive electrode active material for lithium-ion batteries, it is mixed with binders, conductive agents, additives, solvents, etc. to prepare LiFePO 4 Positive slurry. Graphite is used as the negative electrode active material of lithium-ion batteries, mixed with binders, conductive agents, additives, solvents, etc. to prepare graphite negative electrode slurry. Activated carbon is used as the supercapacitor electrode active material, mixed with binders, conductive agents, additives, solvents, etc. to prepare activated carbon slurry.

[0047] With aluminum foil as the current collector, according to the attached figure 1 ways to alternately coat LiFePO 4 Positive electrode slurry and activated carbon slurry, control the mass ratio of lithium-ion battery electrode material and supercapacitor electrode material to 20, then dry, roll film, and cut to make positive electrode sheet of supercapacitor battery.

[0048] With copper foil as the current collec...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a novel energy storage device synchronously provided with characteristics of a super capacitor and a lithium ion battery, and a method for producing the same. The invention hasthe following steps that: a lithium ion battery material and a super capacitor electrode material are separately prepared into pastes, and are alternatively coated to produce a super capacitor battery electrode plate; or a lithium ion battery electrode plate and a super capacitor electrode plate are respectively produced and are wound, then a lithium ion battery roll core and a super capacitor roll core are connected in parallel to form a super capacitor battery roll core cluster, then the super capacitor battery roll core cluster is placed into a battery case and welded, the drying and dehydration are performed, electrolyte is injected, and the novel energy storage device with high energy density and high power density, namely a super capacitor battery is obtained through charge and discharge activation.

Description

technical field [0001] The invention relates to a manufacturing method of an energy storage device having the characteristics of a supercapacitor and a lithium ion battery, belonging to the field of electrochemistry. Background technique [0002] Energy crisis, resource shortage, and environmental pollution are severe challenges facing human existence. Finding clean, renewable, and resource-saving secondary energy is an urgent task to achieve sustainable development of human society. [0003] Lithium-ion batteries have the advantages of high working voltage, high energy density, long cycle life, low self-discharge rate, and environmental protection, and have become the development trend of secondary batteries. It has been widely used in the power supply of portable electrical appliances such as wireless communications, digital cameras, and notebook computers, and has a wide range of electric power sources for mopeds, electric bicycles, electric motorcycles, miner's lamps, el...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01G9/04H01G9/28H01G13/00H01M12/00H01M10/0587
CPCY02E60/122Y02E60/13
Inventor 郭华军李新海王志兴彭文杰胡启阳张云河刘久清
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com