New technology of valve sealing element vacuum induction pile-up welding hard alloy and improved equipment

A vacuum induction, valve sealing technology, applied in metal processing equipment, welding equipment, metal processing and other directions, to achieve the effect of reducing maintenance time, convenient maintenance and operation, and saving consumption

Inactive Publication Date: 2010-08-18
DALIAN DAGAO VALVE
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The invention provides a vacuum induction surfacing hard alloy process and improved equipment for valve seals to solve the shortcomings of the existing processes and devices

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • New technology of valve sealing element vacuum induction pile-up welding hard alloy and improved equipment
  • New technology of valve sealing element vacuum induction pile-up welding hard alloy and improved equipment
  • New technology of valve sealing element vacuum induction pile-up welding hard alloy and improved equipment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] An improved vacuum high-frequency induction surfacing equipment is connected to the GP60 high-frequency machine, and an example of the process of surfacing a valve seat of 3 / 4" (nominal passage 20mm).

[0018] The seat material is 1Cr13. Its main chemical components (mass fraction, %) are 0.10C, 1.00Mn, 1.00Si, 0.035P, 0.030S, 11.7Cr. The depth of the U-shaped groove on the pre-surfacing sealing surface is 2.0mm~2.2mm, and the wall thickness of the U-shaped groove is 0.8mm~1.0mm. The amount of surfacing welding is 15 per furnace each time. Choose 200 mesh (0.126mm) Stellite158D powder as surfacing flux, its chemical composition (mass fraction, %) is 0.50C, 22.7Cr, 2.4Fe, 0.01Mn, 0.01Mo, 2.2Ni, 1.7Si, 4.6W, Yu Co. Use 3 / 4” molds to be hand wiped and pressed, dried and then high-frequency sintered surfacing. The vacuum degree during surfacing is 10 -1 Pa~10 -2 pa, grid current 3.51A, anode current 1.6A, anode voltage 11KV, tank circuit voltage 5.5KV, surfacing temperature...

Embodiment 2

[0020] An improved vacuum high-frequency induction surfacing equipment is connected to the GP60 high-frequency machine, and an example of the process of surfacing a valve seat with a full diameter of 2" (outer diameter ￠58mm).

[0021] The valve seat material is 1Cr13, and its main chemical composition (mass fraction, %) is 0.10C, 1.00Mn, 1.00Si, 0.035P, 0.030S, 11.7Cr. The depth of the U-shaped groove of the pre-surfacing sealing surface is 2.0mm~2.1mm, the wall thickness of the U-shaped groove is 1.0mm~1.10mm, and the amount of surfacing welding is 6 per furnace. Choose 200 mesh (0.126mm) Co-L powder as the surfacing flux, and its chemical composition (mass fraction, %) of the surfacing flux is 0.70C, 0.95Si, 0.61B, 29.50Cr, 4.00W, 2.69Fe, residual Co. It adopts full-diameter 2" molds to be formed by hand rubbing, drying and then performing high-frequency sintering surfacing. The vacuum degree during surfacing is 10 -1 Pa~10 -2 pa. The grid current is 0.57A, the anode current ...

Embodiment 3

[0023] An improved vacuum high-frequency induction surfacing equipment is connected to the GP60 high-frequency machine, and a 11 / 4" (nominal passage 32mm) valve seat process example is surfacing.

[0024] The seat material is 1Cr13. Its main chemical components (mass fraction, %) are 0.10C, 1.00Mn, 1.00Si, 0.035P, 0.030S, 11.7Cr. The depth of the U-shaped groove on the pre-surfacing sealing surface is 2.0mm~2.2mm, and the wall thickness of the U-shaped groove is 0.9mm~1.10mm. The amount of surfacing welding per furnace is 12 each time. Choose 200 mesh (0.126mm) Stellite158D powder as surfacing flux, its chemical composition (mass fraction, %) is 0.50C, 22.7Cr, 2.4Fe, 0.01Mn, 0.01Mo, 2.2Ni, 1.7Si, 4.6W, Yu Co. Use 1 1 / 4" molds to be pressed and formed by hand, drying and then performing high-frequency sintering surfacing. The vacuum degree during surfacing is 10 -1 Pa~10 -2 pa, grid current 0.54A, anode current 1.7A, anode voltage 11.2KV, tank circuit voltage 6.2KV, surfacing t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a new process for vacuum induction surfacing hard alloy on seal component of valve and its improved equipment. Said invention adopts the following technical measures: optimizing surfacing process: regulating U-shaped groove depth and groove wall thickness of sealing surface of sealing component to be surfaced; adopting cheap Stellite 158D and Co-L alloy powder; optimizing technological parameters of surfacing current, surfacing temperature, vacuum degree and valve seat rotating speed; improving surfacing equipment: adding and welding connecting plate and cooling device of furnace cover cooling system; intrafurnace workpiece and induction coil flange sealed position adopt heat-insulating material; a reflective mirror is mounted in the sighting window position; and on the vacuum pipeline system a leakage-detecting interface is added.

Description

Technical field [0001] The invention relates to a vacuum induction surfacing process and equipment, more specifically to a new process and improved equipment for vacuum induction surfacing of hard alloys of valve seals. Background technique [0002] At the end of the last century, manual surfacing methods were generally used for valve sealing surfaces: flame, plasma or non-melting argon arc welding surfacing CoCrW hard alloy to improve the valve's corrosion resistance, wear resistance, heat resistance and surface size formability. However, the above-mentioned surfacing method has relatively high operating difficulties, high labor intensity, high material consumption, and large splashes of smoke (dust) during welding, which not only pollutes the environment but also easily causes damage to the operator’s body. At the same time, the workpiece is oxidized seriously, so Large machining allowances result in time-consuming and labor-intensive mechanical processing; moreover, the surfac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B23K1/002B23K3/00B23K3/08
Inventor 肖箭
Owner DALIAN DAGAO VALVE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap