Brush bristle material and brush

A technology of bristles and brushes, applied in the field of bristle materials and a kind of brush, can solve the problems of inaccessibility to workpieces and scattered bristles, and achieve the effect of easy operation and enhanced grinding performance

Inactive Publication Date: 2008-02-06
新崎 优一郎 +1
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Furthermore, conventional bristle materials may cause the bristles to spread out so that the distal portion of the bristle cannot contact the workpiece

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Brush bristle material and brush
  • Brush bristle material and brush
  • Brush bristle material and brush

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] 1(a)-1(j) are perspective views showing Embodiment 1 of the present invention, respectively showing a bristle material formed by combining a synthetic resin material and a metal material with each other. The bristle material shown in FIG. 1( a) is a circular strip, and is formed by combining metal material 11 and synthetic resin material 12 by thermocompression bonding or thermal welding. The bristle material shown in Figure 1(b) is a circular strip, and the synthetic resin material 121 is inserted between two metal materials 111 that are close to flat plates, and the other synthetic resin material is placed on the metal material like a sandwich. 111 formed on the other side.

[0049] The bristle material shown in Fig. 1 (c) is a circular strip, which is composed of two metal materials 112 each accounting for a quarter circle of the cross section, one also accounting for a quarter circle of the cross section and It is made of a synthetic resin material 13 that contains...

Embodiment 2

[0054] 2(a) to 2(d) are cross-sectional views of Embodiment 2 of the present invention, each showing a mixture of abrasive particles in a synthetic resin material. The bristle material of Fig. 2 (a) is a kind of approximately circular strip, is that the synthetic resin material 12 that each cross section is semicircle and the same metal material 11 that cross section is semicircle are mutually combined and formed. The bristle material shown in FIG. 2(b) is formed by mixing honing grains, grinding grains, flavoring grains or other similar substances in a synthetic resin material 21 having a semicircular cross section. The particles mixed into the synthetic resin material can optionally have different shapes and material qualities depending on the grinding purpose. The material quality type and / or quantity of the substance mixed into the synthetic resin material 21 to 23 can be selected from abrasive grains 21, diamond grains 22, abrasive grains and diamond grains as shown in Fi...

Embodiment 3

[0056] 3( a )- FIG. 3( l ) are cross-sectional views of Embodiment 3 of the present invention, each showing a state in which abrasive particles are attached to the periphery of the metal material. The form of the bristle material shown in FIG. 3( a ) is that, for example, abrasive particles 32 are attached to a metal material 31 with a semicircular cross-section by means such as electrodeposition, welding, electroplating or vapor deposition. Then, the metallic material 31 coats the abrasive grains 32 on its surface as if by electroplating. The cladding may be applied to the metal material 31 at a uniform thickness, although not shown. The bristle material of the bar-shaped body, which is made of the metal material 31 and the synthetic resin material 12 through mutual bonding, is similar to the bristle material shown in FIG. 2 . The bristle material shown in Fig. 3(b) is a strip, which is composed of a synthetic resin material 21 with abrasive particles inside and a metal mate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The brush bristle material of this invention has a synthetic resin material and a metallic material integrated into one or more pieces. The synthetic resin material and the metallic material mentioned above are made of nearly plate bar members and are integrated in the form of a plate or a bar or in any proper form by being mutually combined like a sandwich. The brush bristle material integrated by mutual combination of the component materials is enabled to combine the characteristic properties of the synthetic resin material and the metallic material and acquire proper hardness, elastic force and frictional force suited to a given workpiece, the shape of the workpiece and the purpose of use of the workpiece. This invention concerns a brush bristle material obtained by combining in a varying manner brush bristle materials made of raw materials differing in nature into one piece and enabled to produce a polish conforming to the hardness, shape and object of polishing of a workpiece and a brush manufactured of such brush bristle material.

Description

technical field [0001] The present invention relates to a bristle material which combines the characteristics of both synthetic resin material and metal material and a brush thereof. More specifically, the present invention relates to such a bristle material and a brush, the bristle material is produced by combining bristle materials of different properties into a single piece, the bristle material is capable of grinding workpieces so as to match the hardness, shape and In line with the purpose, the metal bristle material is broken to ensure safe use by avoiding spillage accidents. Background technique [0002] The brush disclosed in JP-A 2003-164332 is manufactured by sandwiching one kind of wire in three other wire materials and twisting them together. A metal hollow tube was inserted into the twisted portion of the brush and fixed by drawing the outer periphery of the brush. [0003] Whereas the brush disclosed in JP-A 2002-254277 is manufactured by dipping bundled yarn...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B24D11/00B24D3/32B24D15/04B24D18/00
CPCA46D1/00Y10T428/2913Y10T428/2938Y10T428/294Y10T428/2973
Inventor 新崎优一郎新崎朋子新崎优仁人
Owner 新崎 优一郎
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap