Light ageing resisting finishing method for aromatic polyamide fabric

An aromatic polyamide, anti-photoaging technology, used in fiber processing, fiber types, textiles and papermaking, etc., can solve problems such as chemical bond damage, polymer aging, etc., to achieve safe industrial use, improved radiation resistance, UV resistance Performance-enhancing effects

Inactive Publication Date: 2008-07-09
海安县福兴织造有限公司
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Thus causing the destruction of chemical bonds,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Light ageing resisting finishing method for aromatic polyamide fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment one: get U.S. DuPont company aramid fiber (commercial brand: M100) fabric 100KG, in the high-temperature high-pressure dyeing machine commonly used, clean the oil stain on the fabric surface with the nonionic surfactant of 0.5g / l (commonly referred to as pretreatment ), after the pretreatment, add 20KG anti-aging reagent emulsion to the dyeing solution, slowly raise the temperature to 120°C, and dye for 1.5h. After dyeing, it is washed with 0.1g / l surfactant, and after drying, a flame-retardant fabric with excellent anti-aging performance can be obtained. The comparison of the mechanical properties of the fabric before and after anti-aging treatment is shown in Table 1.

[0017] Table 1 Comparison of mechanical properties of aromatic polyamide fabrics before and after anti-aging treatment

[0018] Breaking strength (N)

[0019] Note: The aging conditions here are: 360W, 280~350nm wavelength ultraviolet light source, [UV irradiation intensity is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an anti-light ageing finishing method of aromatic polyamidoester fibre cloth, and the method comprises processing aromatic polyamidoester fibre cloth in anti-light ageing finishing agent for 90+-5 minutes under the temperature of 120+-2 DEG C, washing cloth with surface active agent and drying after finishing, wherein the mass ratio of aromatic polyamidoester fibre cloth and anti-light ageing finishing agent is 100:20+-1, the anti-light ageing finishing agent is emulsion whose solid content is 20+-1% and is formed by N,N-diethylm-toluidine, alkyl phenol polyoxyethylene ether and alkylbenzene polyoxyethylene ether which are dissolved in water according to the mass ration which is 80+-0.5:15+-0.5:5+-0.5. The method can lead the intensity after aramid fiber cloth is aged through ultraviolet to reach 87%, and the method has no influence to the physical and chemical property of aramid fiber cloth, and the mechanical property after finishing has no loss. The method of the invention has the advantages of simple technique, strong operability, convenient operation and low production cost.

Description

technical field [0001] The invention relates to an anti-light aging finishing method of aromatic polyamide fiber fabric. Background technique [0002] The aromatic polyamide fiber (known as aramid fiber) first developed by DuPont in the United States is an organic fiber whose macromolecular chain is composed of aromatic rings and amide bonds. It has high strength, high modulus, and low density. Performance, its strength is higher than that of carbon fiber, its quality is lighter than that of glass fiber and carbon fiber, its thermal expansion coefficient is low, and its fatigue resistance is good. Therefore, it is widely used in aerospace, national defense, automobile industry, protective clothing, sports equipment and so on. However, aramid materials are prone to photoaging degradation under ultraviolet radiation, resulting in a gradual decline in the mechanical properties of the product, resulting in brittleness, cracking, and yellowing, and even damage, making it unusabl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M13/165D06M13/415D06M101/36
Inventor 唐志勇张德仁孙晋良刘丽刘杰霞任慕苏张家宝杨敏
Owner 海安县福兴织造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap