Method for producing inorganic film central layer

An intermediate layer, inorganic membrane technology, applied in the field of chemical engineering, can solve the problems of separation membrane performance damage, membrane cracking, defects, etc., and achieve the effect of narrow pore size distribution and strong generality

Inactive Publication Date: 2009-02-25
DALIAN UNIV OF TECH
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The widely used intermediate layer material is γ-Al 2 o 3 , γ-Al 2 o 3 Corrosion resistance to strong acids and alkalis is poor, and according to the Swedish > (Key Engineering Materials) 1991 61-62 volume 383 report, γ-Al 2 o 3 film above 850°C from γ-Al 2 o 3 to α-Al 2 o 3 phase change, the pore size of the intermediate layer increases abnormally, leading to the destruction of the performance of the separation membrane
With regard to the preparation method of the film, researchers such as A.J.Burggraaf in the Netherlands and C.J.Brinker in the United States all use the method of applying at normal temperature, such as the pulling method or the method of rotating the way. A separate process, drying is a slow process. In the later stage of drying, due to the existence of capillary cohesion, the film is easy to crack and has defects, and due to the slow drying speed, the prepared film is thick.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] Specific embodiments of the present invention will be described in detail below in conjunction with technical solutions.

[0018] The preparation of a silicon oxide interlayer on a coarse-porous substrate with an average pore diameter of 2 μm is described below as an example.

[0019] 1. Preparation of SiO with final oxide concentration of 2wt%, 1.5wt%, 1.0wt% 2 Sol gel solution

[0020] Dissolve 10, 7.5, 5, and 2.5g of TEOS in 5g of ethanol respectively, add them dropwise under stirring to 500ml conical flasks containing 173.3, 129.6, 86.4, and 43.2g of deionized water, and then pour them into the conical flasks respectively 0.5 g of concentrated nitric acid was added dropwise to obtain a precursor solution. The precursor solution was hydrolyzed in an ice bath for 1 hour. SiO2 sol solutions of various concentrations were obtained. Thereafter, water was added to 500 ml and 1.5 g of concentrated nitric acid to each sol, boiled under strong stirring, and refluxed for ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a method for preparing for inorganic membrane interface layer and belongs to the technical field of chemical engineering. The present invention is characterized by developing a heat coating method, carrying out two separated traditional processes of coating and drying instantly and synchronously and overcoming the disadvantages that the traditional coating method for manufacturing membrane is chapped easily, has disadvantage and has thick membrane layer; the present invention prepares the inorganic membrane interface layer that the aperture can be adjusted within the range between 50 and 2nm and mainly relates to the preparation of sol gel, a new method for coating the sol gel and the adjustment and control of the aperture of the interface layer. The method has very strong popularity and is used for preparing the adaptive interface layer which synthesizes chemical atmosphere such as alkalescence or acidity towards a separation layer by selecting suitable ceramic material, and the method can meet the requirement of the preparation of the separation layer by adjusting and controlling the aperture. The present invention can be used for preparing the interface layer of the materials such as disilicon trioxide, dizirconium trioxide, dititanium trioxide, the composite oxide thereof, and the like, by dense or porous ceramic, quartz, glass, silicon chip or metal material substrate.

Description

technical field [0001] The invention belongs to the technical field of chemical engineering, relates to inorganic molecular sieve membrane and sol-gel technology, in particular to the preparation of inorganic membrane mesoporous intermediate layer and its application in preparing high-performance and high-quality inorganic membrane. technical background [0002] Due to its good chemical, thermal stability and mechanical strength, inorganic membranes are used in the harsh medium and high temperature catalytic reactions of petrochemical operations, the separation of biochemical products, the separation of organic chemical products, the finishing treatment of beverages and drinking water, the electronics industry, etc. There are potential applications. Generally, a layer of membrane with a pore size of 0.1-1 μm prepared on a coarse-porous ceramic support as the bottom layer is called a microfiltration membrane, and a layer of a membrane layer with a pore size of 2 nm to 100 nm ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01D69/12B01D69/10B01D71/02
Inventor 杨建华王金渠鲁金明孔春龙初乃波周志辉殷德宏张艳
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products