In situ preparation of polyaniline antistatic printing ink

An in-situ preparation, antistatic technology, applied in ink, household appliances, applications, etc., can solve the problems of serious pollution, high cost, and many processes, and achieve the effect of simple production process, low production cost, and short process.

Active Publication Date: 2010-11-03
SICHUAN DONGFANG INSULATING MATERIAL
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The use of such fibrous conductive polyaniline to prepare antistatic materials is conducive to reducing the content of conductive components in the film-forming resin and the amount of solvent used, reducing pollution and controlling production costs; on the other hand, after polyaniline is synthesized from aniline monomer Combined with film-forming resin to prepare antistatic ink, the process is many and cumbersome, the pollution is serious, and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A kind of in-situ preparation method of polyaniline antistatic ink, comprises the following steps:

[0029] (a) Synthesis of polyacrylate glue:

[0030] Weigh respectively 135g methyl methacrylate, 105g butyl acrylate, 15g hydroxyethyl methacrylate and 45g styrene and mix uniformly to obtain a mixed monomer, add 150g of mixed monomer and 0.24g benzoyl peroxide In the reactor equipped with a reflux condenser, heat and stir to 90-110°C, put the remaining 150g monomer and 0.36g benzoyl peroxide in the same funnel, after heating for 1.5h, start to drop the Cool the monomer and control the temperature at 90-110°C; when the temperature exceeds 110°C due to the high viscosity of the reactant, add 300g of xylene which is equal to the weight of the monomer through another funnel at the same time, and the temperature rises after the monomer is dropped Heat it at 120°C for 2 hours, and after cooling, it becomes a polyacrylate glue, in which the solid content (that is, the solid c...

Embodiment 2

[0035] A kind of in-situ preparation method of polyaniline antistatic ink, comprises the following steps:

[0036] (a) Synthesis of polyacrylate glue:

[0037] The solvent xylene is replaced by a mixed solvent of xylene, ethyl acetate and n-butanol in a weight ratio of 68:15:17, and the others are the same as in Example 1, with a solid content of 48.5% (by weight).

[0038] (b) Synthesis of polyaniline antistatic ink:

[0039] Change the polyacrylate glue into the synthetic glue that 112 grams of embodiment 1 makes, and other is with embodiment 1, omission, obtains polyaniline antistatic ink.

[0040] Experimental effect evaluation: Take 40 grams of the above-mentioned polyaniline antistatic ink and 24 grams of the above-mentioned polyacrylate glue, mix and stir evenly, coat the PET film with a coating machine, and dry it in an oven at 90 ° C. The surface resistivity is 10 7 ~10 8 Ω.

Embodiment 3

[0042] A kind of in-situ preparation method of polyaniline antistatic ink, comprises the following steps:

[0043] (a) Synthesis of polyacrylate glue:

[0044] Change monomer to 70g methyl methacrylate, 25g butyl acrylate and 15g hydroxyethyl methacrylate, change benzoyl peroxide to 0.2g, change xylene to 110g, add xylene and keep stirring for 3 hours, Other is slightly with embodiment 1, solid content 48.5%.

[0045] (b) Synthesis of polyaniline antistatic ink:

[0046] Change the polyacrylate glue to the synthetic glue prepared in step (a) of this embodiment, add 400 ml of xylene after the reaction, and the others are the same as in Example 1, to obtain polyaniline antistatic ink.

[0047] Experimental effect evaluation: Take 38 grams of the above-mentioned polyaniline antistatic ink and 30 grams of the above-mentioned synthetic polyacrylate glue, mix and stir evenly, coat the PET film with a coating machine, and dry it in an oven at 80 ° C. The surface resistivity is 10 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
adhesivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an in-situ preparation method of polyaniline antistatic printing ink The invention is characterized in that in the method, methyl methacrylate, butyl acrylate, hydroxyl ethyl acrylate, styrene and benzoyl peroxide are used as the materials under a dimethylbenzene solvent system for synthesizing polyacrylate glue; then in the double-phase solvent of dimethylbenzene and water with the existence of the polyacrylate glue, the water and deposits at a lower layer are removed through centrifugalizing, thus being capable of obtaining the greenblack polyaniline antistatic printing ink.. The method has the advantages of simple technique, easy operation and less pollution. The product prepared by the invention can be broadly applied to the products and fields of durable and stable antistatic performances and high dryness.

Description

technical field [0001] The invention belongs to a preparation method of ink, and relates to an in-situ preparation method of polyaniline antistatic ink. The product prepared by the invention is used in the field of antistatic. Background technique [0002] Conductive polyaniline is a new intrinsic conductive polymer material. The antistatic material prepared by conductive polyaniline has long-lasting and stable conductivity and is not easily affected by humidity and temperature. It is especially suitable for high dryness and high antistatic requirements. products and fields. In the prior art, conductive polyaniline antistatic materials are generally first synthesized polyaniline under acidic aqueous solution conditions, then dissolve and / or disperse conductive polyaniline doped with protonic acid in a suitable solvent, and then compound with film-forming resin , be prepared into a conductive ink that can be coated on the surface of the product that needs to be protected (t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/10C09D11/00
Inventor 吴学明杨波
Owner SICHUAN DONGFANG INSULATING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com