Expansion type flame-retardant coatings glue and use thereof in textile finishing

A flame retardant coating and fabric finishing technology, applied in fiber type, fiber treatment, plant fiber, etc., can solve the problems of loss or degradation of flame retardants, fabrics that cannot be washed, and easy decline in flame retardant performance, so as to improve the durability Washable, realizes multi-functionality, and has good washing resistance

Active Publication Date: 2011-05-18
传化智联股份有限公司 +2
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the textile field, traditional intumescent flame retardants are not widely used. If traditional intumescent flame retardants composed of ammonium polyphosphate (APP) and pentaerythritol or dipentaerythritol and melamine (MEL) are used on fabrics, The fabric is not resistant to washing, blisters, and migration. Under the action of light, heat, humidity, and external mechanical forces, the flame retardant will be lost or degraded, and the flame retardant performance will easily decline.
[0003] In order to improve the water resistance of intumescent flame retardants, a large number of documents and patents have proposed various methods of coating modified ammonium polyphosphate, but ammonium polyphosphate is only one of the components of flame retardants, and coating modified ammonium polyphosphate Finally, for pentaerythritol and dipentaerythritol with certain water solubility and melamine that dissolves very slightly in water, there will still be problems of not being resistant to blisters and washing, and not resistant to migration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Expansion type flame-retardant coatings glue and use thereof in textile finishing
  • Expansion type flame-retardant coatings glue and use thereof in textile finishing
  • Expansion type flame-retardant coatings glue and use thereof in textile finishing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] 100 grams of Type II APP (product of Sichuan Shifang Changfeng Chemical Co., Ltd., CF-APP201), 30 grams of MEL, 2.5 grams of 4A zeolite, the average particle size of the three components is about 2.0-15.0 microns, add to 250 grams of 95% In ethanol, stir evenly, add 0.75 g of γ-glycidoxypropyltrimethoxysilane (KH-560), and then add 0.10 g of ammonia. Under uniform stirring, heat from room temperature to 79°C, reflux for 1.5 hours, and cool to 70 ℃, add 1.2 grams of γ-aminopropyltriethoxysilane (KH-550) dropwise, heat to 79℃, reflux for 1.5 hours, cool to 70℃, add 2.0 grams of γ-glycidoxypropyltrimethoxysilane (KH-560), add 0.10 g of ammonia, reflux at 80°C for 2.5 hours, cool down, remove the solvent, and dry at 110°C for 0.5 hours to obtain a coated modified composite flame retardant (see figure 2 ), the surface of the uncoated ammonium polyphosphate is regular and smooth, with distinct edges and corners, and a regular square shape. The coated flame retardant has blurr...

Embodiment 2

[0038] 105 grams of melamine modified type II APP (product of Changfeng Chemical Co., Ltd., Sichuan Shifang City, CF-APP202), 35 grams of MEL, 3.5 grams of 4A zeolite, the average particle size of the three components is about 2.0-15.0 microns, add To 250 grams of 95% ethanol, stir evenly, add 0.80 grams of γ-glycidoxypropyltrimethoxysilane (KH-560), and then add 0.10 grams of ammonia, heat from room temperature to 79 ℃ under uniform stirring, reflux 1.5 After hours, the temperature is lowered to 70°C, 1.0 g of γ-aminopropyltriethoxysilane (KH-550) is added dropwise, heated to 79°C, refluxed for 1.5 hours, and the temperature is lowered to 70°C, 1.5 g of KH-550 is added, and heated to Reflow at 80°C for 2.5 hours, cool down, remove the solvent, and dry at 110°C for 0.5 hours to obtain a coated modified composite flame retardant.

[0039] Weigh 100 grams of the coated and modified composite flame retardant, add 80 grams of water, 1.0 grams of non-ionic surfactants (add 0), 125 gra...

Embodiment 3

[0042] 150 grams of epoxy resin coated Type II APP (product of Sichuan Shifang Changfeng Chemical Co., Ltd., CF-APP204), 30 grams of MEL, 5.0 grams of 4A zeolite, the average particle size of the three components is about 2.0-15.0 microns, add To 300 grams of 95% ethanol, stir evenly, add 1.5 grams of γ-glycidoxypropyltrimethoxysilane (KH-560), and then add 0.10 grams of ammonia, heat from room temperature to 79°C under uniform stirring, and reflux for 1.5 After hours, the temperature is lowered to 70°C, 1.5g of γ-aminopropyltriethoxysilane (KH-550) is added dropwise, heated to 79°C, refluxed for 1.5 hours, cooled to 70°C, 1.5g of γ-methacryloyl Oxypropyltrimethoxysilane (KH-570), heated to 80°C, then refluxed for 2.5 hours, cooled down, removed the solvent, and dried at 110°C for 0.5 hours to obtain a coated modified composite flame retardant.

[0043] Weigh 150 grams of the coated and modified composite flame retardant, add 100 grams of water, 1.0 grams of non-ionic surfactant ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to view more

Abstract

The invention discloses an intumescent flame retardant coating gum and the application thereof on fabric finishing. When the traditional intumescent flame retardant is applied to fabric, the fabric is not resistant to water rinse, water immersion or transfer, the flame retardant can lose or degrade under the action of luminous rays, heat, moisture and mechanical external force, and the flame retardant properties are reduced. The intumescent flame retardant coating gum comprises a flame retardant coating base gum and a carbon source, and is characterized in that the flame retardant coating base gum is prepared by mixing ammonium polyphosphate, melamine and 4A zeolite, adding organic alcohol, coating the mixture by more than two silane coupling agents for modification, drying the mixture after removing the organic alcohol to obtain a composite flame retardant, adding water, a non-ionic surface active agent, a binding agent and a cross-linking agent to the composite flame retardant, and grinding and dispersing the mixture; the carbon source is aqueous polyacrylic ester containing hydroxyl groups or aqueous polyurethane containing hydroxyl groups or a modifier of the former two. The invention obviously improves the performance of the flame retardant coating gum on flame retardant fabric for resistance to water rinse, transfer, light, heat and friction.

Description

Technical field [0001] The invention relates to the field of textile auxiliaries, in particular to an intumescent flame-retardant coating glue and its application in fabric finishing. Background technique [0002] Intumescent flame retardants have been widely used in the field of coatings, and they have also been explored and promoted in plastics. In the textile field, traditional intumescent flame retardants are not widely used. If traditional intumescent flame retardants with ammonium polyphosphate (APP) and pentaerythritol or dipentaerythritol and melamine (MEL) as components are applied to fabrics, The fabric is not resistant to washing, blisters, and even less resistant to migration. Under the action of light, heat, humidity, and mechanical external forces, the flame retardant will be lost or degraded, and the flame retardant performance will easily decrease. [0003] In order to improve the water resistance of intumescent flame retardants, a large number of documents and pat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D06M11/71D06M13/358D06M15/263D06M15/564D06M23/00D06M101/32D06M101/06
Inventor 曾军罗运军王胜鹏罗巨涛傅幼林
Owner 传化智联股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap