Preparation method of zinc ferrite desulfurization porous ceramic

A technology of porous ceramics and zinc ferrite, applied in ceramic products, chemical instruments and methods, iron compounds, etc., can solve the problems of secondary pollution, low desulfurization efficiency, etc., achieve high service temperature, large sulfur capacity, and avoid secondary pollution pollution effect

Inactive Publication Date: 2012-03-28
SHANDONG UNIV OF TECH
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above method has low desulfurization efficiency and produces secondary pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] 1. Preparation of zinc ferrite:

[0016] Will (NH 4 ) 2 Fa(SO 4 ) 2 ·6H 2 O and Zn(SO 4 ) 2 dissolved in distilled water to form a solution, (NH 4 ) 2 Fe(SO 4 ) 2 ·6H 2 O and Zn(SO 4 ) 2 The molar ratio is 1:1, (NH 4 ) 2 CO 4 ·H 2 O is dissolved in distilled water alone to form a solution, and then the two solutions are heated to 75°C and mixed, wherein (NH 4 ) 2 Fe(SO 4 ) 2 ·6H 2 O and Zn(SO 4 ) 2 with (NH 4 ) 2 CO 4 ·H 2 The molar ratio of O is 1:1.1, stirring at 95 ° C, a yellow precipitate is generated; after cooling, the yellow precipitate is filtered and cleaned until the SO in the cleaning solution 4 2- and NH 4 + The concentration is less than 100ppm; then transfer the cleaned yellow precipitate to an oven at 100°C for drying, soak it in ammonia water after drying, thoroughly stir and wash, filter, and remove the zinc oxide impurities in it until the cleaning solution Middle NH 4 + Till it is less than 100ppm; then dry the washed...

Embodiment 2

[0024] 1. Zinc ferrite preparation:

[0025] Will (NH 4 ) 2 Fe(SO 4 ) 2 ·6H 2 O and Zn(SO 4 ) 2 dissolved in distilled water to form a solution, (NH 4 ) 2 Fe(SO 4 ) 2 ·6H 2 O and Zn(SO 4 ) 2 The molar ratio is 1:1, (NH 4 ) 2 CO 4 ·H 2 O is dissolved in distilled water alone to form a solution, and then the two solutions are heated to 75°C and mixed, wherein (NH 4 ) 2 Fe(SO 4 ) 2 ·6H 2 O and Zn(SO 4 ) 2 with (NH 4 ) 2 CO 4 ·H 2 The molar ratio of O is 1:1.1, stirring at 95 ° C, a yellow precipitate is generated; after cooling, the yellow precipitate is filtered and cleaned until the SO in the cleaning solution 4 2- and NH 4 + The concentration is less than 100ppm; then transfer the cleaned yellow precipitate to an oven at 100°C for drying, soak it in ammonia water after drying, thoroughly stir and wash, filter, and remove the zinc oxide impurities in it until the cleaning solution Middle NH 4 +Till it is less than 100ppm; then dry the washed yel...

Embodiment 3

[0033] 1. Preparation of zinc ferrite:

[0034] Will (NH 4 ) 2 Fe(SO 4 ) 2 ·6H 2 O and Zn(SO 4 ) 2 dissolved in distilled water to form a solution, (NH 4 ) 2 Fe(SO 4 ) 2 ·6H 2 O and Zn(SO 4 ) 2 The molar ratio is 1:1, (NH 4 ) 2 CO 4 ·H 2 O is dissolved in distilled water alone to form a solution, and then the two solutions are heated to 75°C and mixed, wherein (NH 4 ) 2 Fe(SO 4 ) 2 ·6H 2 O and Zn(SO 4 ) 2 with (NH 4 ) 2 CO 4 ·H 2 The molar ratio of O is 1:1.1, stirring at 95 ° C, a yellow precipitate is generated; after cooling, the yellow precipitate is filtered and cleaned until the SO in the cleaning solution 4 2- and NH 4 + The concentration is less than 100ppm; then transfer the cleaned yellow precipitate to an oven at 100°C for drying, soak it in ammonia water after drying, thoroughly stir and wash, filter, and remove the zinc oxide impurities in it until the cleaning solution Middle NH 4 + Till it is less than 100ppm; then dry the washed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a zinc ferrite desulfurization porous ceramic. The method comprises the following steps of preparation, molding and burning of power body and is characterized in that zinc ferrite power is prepared by a solid-phase reaction method, the zinc ferrite power is mixed with a pore agent according to a certain proportion to form zinc ferrite ceramic power, the zinc ferrite ceramic power is prepared into a zinc ferrite ceramic pellet with a certain aperture and air porosity or zinc ferrite ceramic particle billet, the zinc ferrite ceramic pellet or the zinc ferrite ceramic particle billet is burned at a certain temperature to form a zinc ferrite ceramic pellet or a zinc ferrite ceramic particle, and the zinc ferrite ceramic pellet or the zinc ferriteceramic particle is taken as the raw material to be prepared into the zinc ferrite desulfurization porous ceramic. The invention adopts the zinc ferrite to prepare the porous ceramic with desulfurization, and since the zinc ferrite ceramic pellet or the zinc ferrite ceramic particle and the zinc ferrite desulfurization porous ceramic respectively have higher apparent porosity, the invention has the advantages of high desulfurization efficiency, high sulfur capacity, high temperature resistance, easy regeneration and reutilization.

Description

technical field [0001] The invention relates to a preparation method of zinc ferrite desulfurization porous ceramics, belonging to the technical field of porous ceramics preparation. Background technique [0002] Sulfur compounds in waste (gas, liquid and solid) have caused great pollution to the environment and are one of the focuses of people's attention. At present, there are many ways to control sulfide pollution, such as: (1) through the structural design of the desulfurization device; (2) through liquid absorption; (3) through sulfur fixation, that is, to make the solid desulfurizer react with the sulfide displacement. The above method has low desulfurization efficiency and produces secondary pollution. Contents of the invention [0003] The object of the present invention is to provide a kind of preparation method of zinc ferrite desulfurization porous ceramics that can overcome the above-mentioned defects, adapt to a wide range of working temperature and have exce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/06C01G49/00C04B35/622C04B35/26
Inventor 唐竹兴田贵山
Owner SHANDONG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com