Urushiol boron resin and preparation method thereof

Inactive Publication Date: 2010-06-23
中华全国供销合作总社西安生漆涂料研究所
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, many people have modified it, including urushiol epoxy resin, urushiol metal chelate, and formed some achievements, but for the preparation of urushiol borate, currently reported in the literature has Lin Jinhuo and others using urushiol Synthesized by reacting with butyl borate to produce urushiol borate monomer, which has a low molecular weight and is easily hydrolyzed. No application report has been seen

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Urushiol boron resin of the present embodiment, its weight percentage formula is as follows:

[0024] component name

weight percentage (%)

urushiol

30

formaldehyde

6

Butyl borate

1

epoxy resin

20

catalyst

0.5

Xylene

30

Butanol

22.5

[0025] The urushiol is selected from one or more of the lacquers produced in Ankang, Hanzhong, Chengkou, Maoba, Qinling and other areas, so that the frying pan fraction of the urushiol solution is more than 65%, and the urushiol content more than 50%.

[0026] According to the above mass ratio formula, heat the urushiol solution to 60°C, keep it warm, add formaldehyde and catalyst to react for 2.5 hours, heat up and dehydrate after the reaction; after dehydration, wait until the system temperature drops to 110°C, add butyl borate, epoxy Resin, butanol and xylene were reacted for 1 hour to obtain urushiol boron resin.

Embodiment 2

[0028] Its weight percentage formula of urushiol boron resin of the present embodiment is as follows:

[0029] component name

weight percentage (%)

urushiol

20

Furfural

4

catalyst

0.5

epoxy resin

20

Methyl borate

1.5

Xylene

30

ethanol

24

[0030] The urushiol is selected from one or more of the lacquers produced in Ankang, Hanzhong, Chengkou, Maoba, Qinling and other areas, so that the frying pan fraction of the urushiol solution is more than 65%, and the urushiol content more than 50%.

[0031] According to the above mass ratio formula, heat the urushiol solution to 60°C, keep it warm, add furfural and catalyst to react for 2.5 hours, and then heat up and dehydrate after the reaction; after dehydration, wait until the temperature of the reactants drops to 110°C, add methyl borate, cyclo Oxygen resin, ethanol and xylene were reacted for 3 hours to obtain urushiol boron re...

Embodiment 3

[0033] Its weight percentage formula of urushiol boron resin of the present embodiment is as follows:

[0034] component name

weight percentage (%)

urushiol

40

Formaldehyde (paraformaldehyde)

6

catalyst

1

Borax

1

epoxy resin

10

ethanol

2

Xylene

40

[0035] The urushiol is selected from one or more of the lacquers produced in Ankang, Hanzhong, Chengkou, Maoba, Qinling and other areas, so that the frying pan fraction of the urushiol solution is more than 65%, and the urushiol content more than 50%.

[0036] According to the above mass ratio formula, heat the urushiol solution to 100°C, keep it warm, add paraformaldehyde (formaldehyde) and catalyst, and react for 2.5 hours. Borax, epoxy resin, diluent ethanol and xylene were reacted for 3 hours to obtain urushiol boron resin.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an urushiol boron resin and a preparation method thereof. The urushiol boron resin comprises the following raw materials in percentage by mass: 20-40% of urushiol, 4-8% of aldehyde compound, 0.5-1% of boron compound, 10-20% of epoxy resin, 0.5-1% of catalyst and 40-60% of thinner. The urushiol boron resin has the characteristics of high temperature resistance, alkali resistance, water resistance, oil resistance, wear resistance and strong adhesive force, and can be directly coated on an object. The varnish film has the advantages of excellent heat resistance, water resistance and strong chemical resistance. The product of the invention is suitable for aerospace, electronic information, automobile industry, household appliances and the like.

Description

technical field [0001] The invention relates to an urushiol-based coating, in particular to an urushiol-boron resin and a preparation method thereof, which are mainly used in aerospace, electronic information, automobile industry, household appliances, military industry, petrochemical industry and the like. Background technique [0002] Raw lacquer is a special product in my country, with a history of 8,000 years of use. Raw lacquer film has excellent performance, but the construction conditions and construction technology requirements are relatively high. In order to further develop the use value of lacquer, carry forward the quintessence of the country, meet the requirements of social development, and keep pace with the times. Therefore, many people have modified it, including urushiol epoxy resin, urushiol metal chelate, and formed some achievements, but for the preparation of urushiol borate, currently reported in the literature has Lin Jinhuo and others using urushiol ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G8/28C08G81/00C09D161/14C09D187/00
Inventor 张飞龙贺娜
Owner 中华全国供销合作总社西安生漆涂料研究所
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap