Inorganic high temperature binder

Abstract

Inorganic high-temperature binder, which includes the following materials: 90-110 parts by weight of inorganic binder, 20-40 parts by weight of palygorskite powder, and 10-20 parts by weight of sepiolite wool; put the above three materials into the reaction kettle Stir and mix at high speed for 20-40 minutes to obtain the inorganic high-temperature binder of the present invention. The inorganic high-temperature binder of the present invention overcomes the shortcomings of existing inorganic binders such as low temperature resistance, high price, and narrow application range, and has the advantages of long-term use under the condition of -15 to 800°C, wide application range, environmental protection, and non-toxicity. Poison is harmless. The construction is convenient, the price is low, and the price is only 1 / 10 of that of similar adhesives.

Description

technical field [0001] The invention relates to an industrially used inorganic high-temperature binder. Background technique [0002] The existing binders are generally organic binders, or a kind of organic and inorganic mixed binders that only use inorganic substances as fillers. A separate inorganic binder is less. Such as Chinese Patent No. 98102783.0, a kind of inorganic binder for coke (coal). Although the materials used are relatively simple, they are not resistant to high temperatures (the effect is not good under high temperature conditions). Chinese patent 01128304.1, a kind of concrete interface inorganic binder, the materials used are relatively complicated, and the field of use is relatively narrow, it can only be used for concrete interface bonding, and it is not resistant to high temperature (the bonding effect is not good under high temperature conditions) . Contents of the invention [0003] The object of the present invention is to overcome the disadva...

AI Technical Summary

Problems solved by technology

Although the material is relatively simple, it is not resistant to high temperature (the effect is not good under high temperature conditions)

Chinese patent 01128304.1, a kind of concrete interface inorganic binder, the materials used are relatively complicated, and the field of use is relatively narrow, it can only be used for concrete interface bonding, and it is not resistant to high temperature (the bonding effect is not good under high temperature conditions)