A resin-based, seam-filling technology, applied in the direction of adhesives, adhesive types, other chemical processes, etc., can solve the problems of short use time, difficult construction, and seam expansion, etc., to achieve high adhesion, improve softening point, The effect of improving road performance

Inactive Publication Date: 2010-09-22
安徽三缔沥青材料有限公司
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a high-efficiency resin-type joint glue, which solves the problems of difficult construction, short service time and expansion of joints caused by using modified asphalt.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Example 1: Preparation of a high-efficiency resin-type caulking glue

[0024] Components: by mass percentage, aromatic hydrocarbon: 20%; heavy traffic asphalt: 16%, modifier: 10%, petroleum resin: 50%, reinforcing agent: 2%, fluxing agent: 2%.

[0025] Preparation:

[0026] 1) Heating aromatics to 60°C;

[0027] 2) Add modifier and stir until liquid, then add reinforcing agent and flux;

[0028] 3) Heat the heavy traffic asphalt to 120°C and gradually add one or more resin mixtures, the liquid formed in step 2) is heated to 60°C; the liquid formed by heavy traffic asphalt and one or more resin mixtures, step 2 ) to form a liquid mixture, and form a uniform and stable mixture through advanced mechanical stirring, fully stir, cool to room temperature and store.

Embodiment 2

[0030] 1: Preparation of a high-efficiency resin-type caulking glue

[0031] Components: by weight percentage, aromatic hydrocarbon: 20%, heavy traffic asphalt: 17%, modifier: 6%, petroleum resin: 53%, reinforcing agent: 2%, fluxing agent: 2%.

[0032] Preparation:

[0033] 1) Heating aromatics to 65°C;

[0034] 2) Add modifier and stir until liquid, then add reinforcing agent and flux;

[0035] 3) Heat the heavy-duty asphalt to 115°C and gradually add one or more resin mixtures, the liquid formed in step 2) is heated to 65°C; the liquid formed by heavy-duty asphalt and one or more resin mixtures, step 2 ) to form a liquid mixture, and form a uniform and stable mixture through advanced mechanical stirring, fully stir, cool to room temperature and store.

Embodiment 3

[0037] 1: Preparation of a high-efficiency resin-type caulking glue

[0038] Components: by weight percentage, aromatic hydrocarbon: 18%, heavy traffic asphalt: 17%, modifier: 7%, petroleum resin: 55%, reinforcing agent: 1%, fluxing agent: 2%.

[0039] Preparation:

[0040] 1) Heating aromatics to 60°C;

[0041] 2) Add modifier and stir until liquid, then add reinforcing agent and flux;

[0042] 3) Heat the heavy traffic asphalt to 130°C and gradually add one or more resin mixtures, the liquid formed in step 2) is heated to 60°C; the liquid formed by heavy traffic asphalt and one or more resin mixtures, step 2 ) to form a liquid mixture, and form a uniform and stable mixture through advanced mechanical stirring, fully stir, cool to room temperature and store.

[0043] Test and detection: According to the industry standard of the People's Republic of China: T0605-1993, T0606-2000, T0662-2000, T0616-1993 in the test procedure for highway engineering asphalt and asphalt mixtur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high efficiency resin fissures cementation glue for pitch and cement road surface fissures cementation. The fissures cementation glue comprises the following components by weight percent: 10 to 15 percent of aromatic hydrocarbon, 3 to 10 percent of modifier, 1 to 3 percent of intensifier, 3 to 10 percent of cosolvent, 30 to 60 percent of resin mixture and 10 to 20 percent of heavy traffic pitch. The aromatic hydrocarbon is heated to 60 to 70 degrees centigrade, the modifier is added to be stirred for 30 minutes, the intensifier and the cosolvent are added slowly step by step, the resin and the pitch are added at last, the temperature is kept at 120 degrees centigrade for 30 minutes under stir circumstance, and then the resin fissures cementation glue with excellent performance can be obtained. In the invention, the aromatic hydrocarbon is used to form even mixture among the modifier, the resin and the pitch so that resin group and pitch group are bridged under the action of the modifier. When used on the road surface, the resin exerts the high bondability characteristic and the like. The modifier is used to improve the road performance, as improving softening point, low temperature ductility and the like. At the same time, the invention is good glue material.

Description

technical field [0001] The invention relates to a resin-type joint-filling glue for highway pavement, in particular to a high-efficiency resin-type joint-filling glue used for filling joints on asphalt and cement road surfaces. Background technique [0002] A large number of asphalt or cement is used as the pavement cementitious material for highway pavement. However, asphalt or cement is used as a cementitious pavement, due to the erosion of sunlight, wind, and water in nature, certain performance aging problems will occur; at the same time, due to the inherent characteristics of the material, cement cannot resist thermal expansion and contraction, and asphalt cannot resist comparison. High, concentrated pressure. Therefore, we can often see large or small cracks on the road surface. The existing construction is to directly fill the joints with modified asphalt, and the joints filled with modified asphalt are often damaged due to insufficient bonding force in March, and t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J157/02C09J195/00C09J11/08C09J11/04C09J11/06C09K3/10E01C23/09
Inventor 刘杨军李国涛
Owner 安徽三缔沥青材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap