Multilayer barrier film
A technology of barrier film and core layer, applied in the direction of layered products, synthetic resin layered products, containers with multiple items, etc., can solve the problems of low mechanical properties, tear strength and impact strength, sealing properties, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0085] Embodiment 1——Comparative example
[0086] Films were produced on a three-layer coextrusion film line manufactured by Brampton Engineering. A three-layer film was prepared with a total thickness of 2 mils using a blow-up ratio (BUR) of 2 / 1. A three-layer film was prepared with a total thickness of 1 mil using a BUR of 1.5 / 1.
[0087] The "sealant" layer (ie one of the skin layers indicated as layer C in Tables 2.1 and 2.2) was prepared from a conventional high pressure low density polyethylene homopolymer having a melt index of about 2 g / 10 min. Such low density homopolymers are commercially available widely and typically have a density of about 0.915 to 0.930 g / cc. This resin is indicated in the table as "Sealant LD". In all examples, the amount of the sealant layer was 15 wt%.
[0088] The core layer (Layer B in Tables 2.1 and 2.2) is a conventional high density polyethylene homopolymer (NOVA Chemicals under the trademark 19G), referred to in these examples as...
Embodiment 2
[0102] Embodiment 2 - the present invention
[0103] 1 mil and 2 mil films were prepared in the same manner as described in Example 1.
[0104] The core layers of all films were prepared with a combination of "HDPE Blend" and Nucleating Agent 1 (1000 parts per million by weight).
[0105] The sealant layers of all films were prepared with 15% by weight of the LD sealant resin used in Example 1.
[0106] Another skin layer was prepared using the same resin as used in Example 1, the contents of which are shown in Tables 3.1 and 3.2.
[0107] chart 3.1
[0108] 1 mil film of the present invention
[0109]
[0110]
[0111] Table 3.2
[0112] 2 mil film of the present invention
[0113]
[0114]
PUM
Property | Measurement | Unit |
---|---|---|
melt flow index | aaaaa | aaaaa |
melt flow index | aaaaa | aaaaa |
melt flow index | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap