Fast cure EVA solar cell adhesive film

A solar cell and rapid curing technology, applied in circuits, adhesives, photovoltaic power generation, etc., can solve the problems of high production cost, low processing efficiency, large energy consumption, etc., to shorten lamination time, improve production efficiency, and reduce production cost Effect

Inactive Publication Date: 2010-10-27
诸暨市枫华光伏材料有限公司
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] But, existing EVA solar adhesive film still generally has following shortcoming: 1, EVA solar adhesive film needs higher lamination temperature in solar module lamination process, and energy consumption is big, and lamination pro

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The EVA solar cell glue film that can solidify rapidly, comprises the material of following parts by weight:

[0023] 100 parts of ethylene-vinyl acetate copolymer; 0.5-3 parts of silane coupling agent; 1-3 parts of peroxide crosslinking agent; 0.1-0.5 parts of antioxidant; Agent 0.05-0.2 part; In the above-mentioned peroxide type cross-linking agent, include peroxy-2-ethylhexanoic acid tert-butyl ester cross-linking agent. The weight fraction of tert-butyl peroxy-2-ethylhexanoate is 0.5-1 part. Wherein, the optimal weight fraction of tert-butyl peroxy-2-ethylhexanoate is 0.6-0.8 parts.

[0024] The peroxide crosslinking agent also includes any one or more of the following: 1,1-bis(tert-butyl peroxide)-3,3,5-trimethylcyclohexane; 2,5-bis Methylhexane-2,5-di-tert-butyl peroxide; 2,5-dimethyl-2,5-bis(benzoylperoxy)-hexane; dicumyl peroxide, bis( 2-tert-butylperoxycumyl)benzene; tert-butylcumene peroxide; di-tert-butyl peroxide; tert-amyl perbenzoate; ;di-tert-amyl per...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a fast cure EVA solar cell adhesive film, and overcomes the technical defects of unreasonable compatibility, slow crosslinking speed and the like in the prior art. The EVA solar cell adhesive film comprises the following matters in parts by weight: 100 parts of ethylene-vinyl acetate, 0.5-3 parts of silane coupling agent, 1-3 parts of peroxide cross-linking agent, 0.1-0.5 part of anti-oxidant, 0.1-0.5 part of heat stabilizer and 0.05-0.2 part of hindered amine light stabilizer, wherein the peroxide cross-linking agent comprises peroxide-2-ethyl hexanoic acid tert-butyl crosslinker. Compared with the prior art, the fast cure EVA solar cell adhesive film has the advantages that the temperature for lamination is lower, the lamination time is shortened and the crosslinking degree is not lowered; and fast curing can be realized, the production efficiency is effectively improved and the production cost is reduced.

Description

technical field [0001] The invention relates to the technical field of solar cell adhesive films, in particular to a fast-curing EVA solar cell adhesive film. Background technique [0002] If the solar cell is directly exposed to the air, its photoelectric conversion efficiency will drop quickly and lose its practical value. Therefore, the research and development of packaging materials for solar cells is very important. In order to achieve the purpose of isolation from the outside world, the solar cells are encapsulated with transparent, light-resistant, good adhesive performance, and can withstand atmospheric changes. The protective materials are bonded together to make up the solar cell module. [0003] EVA resin is a thermoplastic polymer material, which is a polymer with a linear molecular structure. Its heat resistance is poor, it is easy to extend and has low elasticity, and its creep resistance is poor, and it is easy to cause thermal expansion and contraction, wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J7/00C09J123/08C09J131/04H01L31/0203H01L31/048
CPCY02E10/50
Inventor 魏陆平周均华
Owner 诸暨市枫华光伏材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap