Carbon-containing temperature measurement tube oxidation-resistance coating as well as preparation method and using method thereof

An anti-oxidation coating and temperature measuring tube technology, applied in the coating field, can solve the problems of short service life of temperature measurement, increased cost, easy cracking, etc., and achieve the effects of reducing adverse effects, preventing erosion, and not easy to foam

Active Publication Date: 2011-02-16
MAANSHAN IRON & STEEL CO LTD
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are also anti-oxidation coatings that separate the binder from the additives, but they need to be mixed on site before they are used, and they need to be dried before they can be used. The above reasons make the service life of the temperature measuring device not long, at most 23 hours, it is also easier to crack, which increases the cost of production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] First, 40% silicon dioxide, 39.9% kaolin powder, 11% boric acid, 2% aluminum dihydrogen phosphate, 3% silicon powder, 3.5% yellow dextrin, 0.5% chromium oxide, 0.1% milk Mix the turbidity agent evenly, then ball mill at high speed on the ball mill, the speed of the ball mill is 450rmp, ball mill for 15 hours, then mix the finely ground anti-oxidation coating with 10% water and spray it on the temperature measuring tube, use it directly after baking, bake The temperature is 90°C and baked for 10 hours.

[0021] The service temperature of the carbon-containing temperature-measuring tube coated with the anti-oxidation coating of the present invention reaches 1560° C., and the normal service life is 32 hours.

Embodiment 2

[0023] First, 50% silicon dioxide, 34% kaolin powder, 9% boric acid, 1.4% aluminum dihydrogen phosphate, 2% silicon powder, 3% yellow dextrin, 0.4% chromium oxide, 0.2% milk Mix the turbidity agent evenly, then ball mill at high speed on the ball mill, the speed of the ball mill is 480rmp, ball mill for 12 hours, then mix the finely ground anti-oxidation coating with 11% water and spray it on the temperature measuring tube, use it directly after baking, bake The temperature is 120°C and baked for 7 hours.

[0024] The temperature of the carbon-containing temperature measuring tube coated with the anti-oxidation coating of the present invention reaches 1560° C., and the normal service life is 31.5 hours.

Embodiment 3

[0026] First, 59.25% silicon dioxide, 27.5% kaolin powder, 8% boric acid, 1% aluminum dihydrogen phosphate, 1% silicon powder, 2.5% yellow dextrin, 0.35% chromium oxide, 0.4% milk Mix the turbidity agent evenly, then ball mill at a high speed on a ball mill, the speed of the ball mill is 500rmp, and ball mill for 10 hours, then mix the finely ground anti-oxidation coating with 12% water and spray it on the temperature measuring tube, use it directly after baking, and bake Bake at 150°C for 4 hours.

[0027] The temperature of the carbon-containing temperature measuring tube coated with the anti-oxidation coating of the present invention reaches 1560° C., and the normal service life is 30.2 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a carbon-containing temperature measurement tube oxidation-resistance coating which comprises the following compositions in percentage by weight: 40-59.9 percent of fillers, 40-59.9 percent of binder and 0.1-0.4 percent of opacifier, wherein the fillers is silicon dioxide, and the binder comprises the following compositions: 27.15-39.9 percent of kaolin micropowder, 8-11 percent of boric acid, 1-2 percent of aluminum dihydrogen phosphate, 1-3 percent of silicon micropowder, 2.5-3.5 percent of yellow dextrin and 0.35-0.5 percent of chromium oxide. A preparation method of the coating comprises the following steps of: uniformly mixing the 40-59.9 percent of the silicon dioxide, 40-59.9 percent of the binder and 0.1-0.4 percent of the opacifier, and then ball milling at high speed on a ball mill to prepare the oxidation-resistance coating. A using method of the oxidation-resistance coating comprises the following steps of: adding water to the oxidation-resistance coating, uniformly mixing, spraying the mixture on a temperature measurement tube, roasting and then directly using. Therefore, the service life of the oxidation-resistance coating is prolonged from 23h to 30h, and prolonged by 30 percent.

Description

technical field [0001] The invention relates to coatings, in particular to anti-oxidation coatings for carbon-containing temperature measuring tubes. Background technique [0002] The infrared optical temperature measuring tube is used to monitor the temperature of the molten steel in the tundish, and the operating temperature is required to be around 1560°C, and the service life is ≥24 hours. However, the surface of the temperature measuring tube must be coated with a layer of anti-oxidation paint to increase the service life of the temperature measuring tube. Because most of the binding agents used in the existing anti-oxidation coatings are chemical binding agents (such as sodium silicate, etc.), the stability of the coating is reduced. Such as Chinese patent CN1035121A "oxidation-resistant coating containing graphite refractory material", Chinese patent CN1066078A "oxidation-resistant coating of aluminum-carbon refractory material and its preparation method". There are...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
Inventor 刁常军魏云峰陈广言张丽丽
Owner MAANSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap