High-property polyhydroxyalkanoates (PHAs)/polybutylene succinate (PBS)/poly lactic acid (PLA) blend alloy

A high-performance, mixed-gold technology, applied in the field of materials, can solve the problems of low rigidity, poor toughness, and unsatisfactory mechanical properties, and achieve the effect of excellent comprehensive performance.

Active Publication Date: 2011-03-23
SHENZHEN ECOMANN BIOTECH
View PDF4 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Disclosed as Chinese patent CN1470553A the preparation method of poly 3-hydroxyalkanoate/carbon dioxide-propylene oxide copolymer/starch blend, although the material it discloses has a wide range of processing, its rigidity is not high
For example, Chinese patent CN101205356 discloses a blend modification of polyhydroxyalkanoate and its copolymer and polylactic acid, and a material with better processing performance and toughness is obtained, but because the compatibility between the two is not very good, So the mechanical properties are not very ideal
And Chinese patent CN101045810A disclos

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-property polyhydroxyalkanoates (PHAs)/polybutylene succinate (PBS)/poly lactic acid (PLA) blend alloy
  • High-property polyhydroxyalkanoates (PHAs)/polybutylene succinate (PBS)/poly lactic acid (PLA) blend alloy

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] Example 1:

[0020] The weight was 50 parts of P3HB4HB (4HB molar content is 15%, weight average molecular weight is 1.2 million), 8.5 parts of PBS (molecular weight is 180,000), 40 parts of PLA (molecular weight is 250,000), 0.6 parts of anti Oxidizing agent tetra[methyl-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid] pentaerythritol ester, 0.2 parts of paraffin, 0.5 parts of heat stabilizer zinc stearate and 0.2 parts of chain extender Proportionally, put it into a high-speed mixer and mix for 3 minutes, then pump the mixed material into a 50°C drying oven for 4 hours, and finally put it into a twin-screw extruder for extrusion to obtain a co-mixed gold material.

[0021] Under the same process, the mechanical properties of P3HB4HB / PBS / PLA alloy and P3HB4HB / PLA alloy are compared in Table 1.

[0022] Table 1

[0023] Alloy material category

Example Embodiment

[0024] Example 2:

[0025] Mix 64 parts of PHBV (HV molar content is 5%, molecular weight is 1.6 million) with 24 parts of PLA (molecular weight is 250,000), 10.1 parts of PBS (molecular weight is 180,000), 0.8 parts of antioxidant 3,5-two Stearyl tert-butyl-4-hydroxyphenyl propionate, 0.5 parts of lubricant erucamide, and 0.6 parts of heat stabilizer calcium stearate are weighed and put into a high-speed mixer and mixed for 4 minutes. Then the mixed materials were pumped into a drying oven at 60°C for 3 hours, and finally put into a twin-screw extruder for extrusion.

[0026] Under the same process, the mechanical properties of PHBV / PBS / PLA alloy and PHBV / PLA alloy are compared in Table 2.

[0027] Table 2

[0028] Alloy material category

Example Embodiment

[0029] Example 3:

[0030] Combine 40 parts of P3HB4HB (4HB with a molar content of 15% and molecular weight of 1.2 million) with 20 parts of PLA (molecular weight of 250,000) and 11.8 parts of PBS (molecular weight of 180,000), 26 parts of starch, and 0.5 parts of antioxidant 2.6-Di-tert-butyl-4-methylphenol and 0.7 parts of antioxidant distearyl thiodipropionate, 0.3 parts of lubricant paraffin and 0.5 parts of lubricant erucamide, 0.2 parts of antistatic agent Tetraalkylammonium salt, weighed and put into a high-speed mixer for mixing for 5 minutes, then the mixed material is pumped into a 70℃ drying oven for 4 hours, and finally put into a twin-screw extruder for extrusion , To obtain a total mixed gold material.

[0031] Under the same process, the mechanical properties of P3HB4HB / PBS / PLA alloy and P3HB4HB / PLA alloy are compared in Table 3.

[0032] table 3

[0033]

[0034] 30% PHBH (3-hydroxyacetic acid HH mole content is 15%, weight average molecular weight is 1.2 million), ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-property polyhydroxyalkanoates (PHAs)/polybutylene succinate (PBS)/poly lactic acid (PLA) blend alloy, which comprises PHAs as a body, PBS as a wild phase, PLA as a compatibilization phase, and other components. The blend alloy provided by the invention has higher compatibility and higher mechanical properties, and can be widely applied to film blowing products, blow molding products, extrusion products, injection molding products, foaming products and spinning products.

Description

technical field [0001] The invention relates to the field of materials, in particular to a fully biodegradable blended alloy material. Background technique [0002] The traditional plastic industry consumes a lot of petroleum energy and the "white pollution" has attracted more and more attention. Since the 1960s and 1970s, people have begun to research and develop biodegradable plastics. At present, there are A variety of synthetic biodegradable materials (Biodegradable materials) have come out, including polyhydroxyalkanoates (PHAs), polylactic acid (PLA), polycarbonate (PPC), polybutylene succinate (PBS), polycaprolactone Esters (PCL), etc. They are used as plastic materials and after biodegradation, become water and carbon dioxide and do not cause harm to the environment. At present, more studies on biodegradable plastics are concentrated on polylactic acid (PLA), polyhydroxyalkanoates (PHAs), and polybutylene succinate (PBS). [0003] Polyhydroxyalkanoates (PHAs) are ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/04C08L67/02
Inventor 李敏张向南
Owner SHENZHEN ECOMANN BIOTECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap