Method for utilizing caustic calcined dolomite
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A light-burned dolomite powder and cement technology, which is applied in the field of light-burned dolomite powder utilization, can solve the problems of low MgO content, high production cost, waste of resources, etc., and achieve the effects of high production efficiency, short process and low production cost
Active Publication Date: 2012-12-19
SHANXI TAIGANG STAINLESS STEEL CO LTD
View PDF0 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, in the roasting production process, about 10% of the lightly burned dolomite powder with a particle size of less than 10mm is produced every year. These powders cannot be directly added to the converter or electric furnace because the particle size is too small. serious pollution to the environment
Many enterprises use lightly burned dolomite powder to make magnesium metal, but the disadvantage is that the effective MgO content is too low and the production cost is high
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0035] The utilization method embodiment of this lightly burned dolomite powder is the following steps in sequence:
[0036] 1. Ingredients
[0037] Finely grind the lightly burned dolomite, fine grinding requirements: the maximum particle size is 1mm, and 92% of the particles are less than 0.5mm;
[0038] Lightly burned dolomite powder, 20% MgCl 2 The solution is mixed with 325# cement according to the following quality:
[0041] Lightly burnt dolomite powder, cement and MgCl with a forklift 2 The solution is mixed evenly to form a mixture, and the MgCl in the mixture 2 It is 4kg. Until no white cement can be seen.
[0042] 2. Add organic binder
[0043] Spray 37.5kg of polyvinyl alcohol organic binder with a prepared concentration of 4% onto the mixture, and mix evenly (the quality of polyvinyl alcohol in the organic binder is 1.5kg). Then the material is transported to the doubl...
Embodiment 2
[0049] The difference between this example and Example 1 is that in step 1, during the batching, MgCl is added to the lightly burned dolomite powder 2 After the solution, mix well first, then add cement and then mix well.
[0050] The cement of above-mentioned two embodiments also can replace with 425#, 525#. What two embodiment used is the II type pair of roller briquetting machine that Luoyang Guoao Machinery Co., Ltd. produces.
[0051] The mixing described in the above two embodiments in step 1, batching and step 2, adding organic binder can be mixed with a forklift, or can be stirred and mixed evenly with a mixer.
[0052] The concentrations described in the present application documents are mass percent concentrations.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
particle size
aaaaa
aaaaa
strength
aaaaa
aaaaa
strength
aaaaa
aaaaa
Login to View More
Abstract
The invention relates to a method for utilizing caustic calcined dolomite. The method sequentially comprises the following steps of: 1, blending: performing fine grinding on caustic calcined dolomite and uniformly mixing 1 part of ground caustic calcined dolomite, 0.03-0.05 part of MgCl2 solution with the concentration of 15-25 percent and 0.02-0.05 part of cement; 2, adding an organic adhesive: spraying a polyvinyl alcohol organic adhesive with the concentration of 3-5 percent onto the mixture and uniformly mixing, wherein the mass of polyvinyl alcohol in the organic adhesive accounts for 0.01-0.02 percent of the mass of dolomite dust; 3, extruding and forming: conveying the mixture, into which the organic adhesive is added, onto a ball press for pressing into balls; and 4, curing the balls by natural drying, wherein the measured intensity is between 1,300N / ball and 1,800N / ball. The method for utilizing the caustic calcined dolomite has a low production cost, and environmental pollution caused by dolomite dust is avoided.
Description
technical field [0001] The invention relates to a utilization method of lightly burned dolomite powder. Background technique [0002] After the dolomite raw ore is mined, in order to make better use of it in the steelmaking process, the raw ore needs to be roasted to make the CaCO 3 Decompose to generate CaO, MgCO 3 Decompose to generate MgO. However, in the roasting production process, about 10% of the lightly burned dolomite powder with a particle size of less than 10mm is produced every year. These powders cannot be directly added to the converter or electric furnace because the particle size is too small. Serious pollution to the environment. Many enterprises use light-burned dolomite powder to make magnesium metal, but the disadvantage is that its effective MgO content is too low and the production cost is high. In order to effectively utilize light-burned dolomite powder and solve the backlog problem of light-burned dolomite powder, it has become an imminent subjec...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More