Manufacturing method of cured film, photosensitive resin composition, cured film, organic EL display device and liquid crystal display device

A technology of photosensitive resin and manufacturing method, applied in the field of photosensitive resin composition and manufacturing method of cured film, can solve problems such as insufficient sensitivity, and achieve the effect of excellent heat resistance and transparency

Active Publication Date: 2014-09-17
FUJIFILM CORP
View PDF26 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the case of this composition, the sensitivity is insufficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of cured film, photosensitive resin composition, cured film, organic EL display device and liquid crystal display device
  • Manufacturing method of cured film, photosensitive resin composition, cured film, organic EL display device and liquid crystal display device
  • Manufacturing method of cured film, photosensitive resin composition, cured film, organic EL display device and liquid crystal display device

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0338] (Method for preparing photosensitive resin composition)

[0339] The essential components of Component A to Component C and optional components added as needed are mixed in a predetermined ratio by any method, stirred and dissolved, and a photosensitive resin composition is prepared. For example, after dissolving component A or component B in a solvent in advance to prepare a solution, respectively, these may be mixed at a predetermined ratio to prepare a photosensitive resin composition. The photosensitive resin composition prepared above can also be used after filtering using the filter etc. which have a pore diameter of 0.2 micrometers.

[0340] II. Manufacturing method of cured film

[0341] The method for producing a cured film of the present invention is characterized in that it includes the following steps in the following order: (1) a low-temperature treatment step of bringing the temperature of the photosensitive resin composition to 10° C. or lower; (2) combini...

Embodiment 1～44、 comparative example 1～7、 Embodiment 101～139

[0407] (Examples 1-44, Comparative Examples 1-7, Examples 101-139, Examples 201-239 and Examples 301-308)

[0408] Mix the ingredients shown in Table 2 to Table 5, and then add a 1:1 mixed solvent of C1: propylene glycol monomethyl ether acetate and C2: diethylene glycol ethyl methyl ether to make the viscosity 3.0 mPa·s , and filtered through a 0.2 μm polytetrafluoroethylene filter to prepare a positive-type photosensitive resin composition.

[0409] Table 2

[0410]

[0411] table 3

[0412]

[0413] Table 4

[0414]

[0415] table 5

[0416]

[0417] In addition, the abbreviations in Table 2 to Table 5 are as follows.

[0418]

[0419] B5: α-(4-tosyloxyimino)benzonitrile (synthesized according to the method described in paragraph 0108 of JP 2002-528451 A.)

[0420] B6: α-[(4-tosyloxyimino)-4-methoxyphenyl]acetonitrile (PAI-101, manufactured by Midori Chemical Co., Ltd.)

[0421] D1: NBCA (10-butyl-2-chloroacridone, manufactured by Kurokane Kasei Co., Ltd....

Embodiment 1

[0456] The following evaluation was performed using the photosensitive resin composition of Example 1.

[0457]

[0458] The prepared photosensitive resin composition was temporarily treated at low temperature under the conditions shown in Table 6, and then returned to room temperature (23° C.). After slit-coating the photosensitive resin composition on a glass substrate of 2160×2460 mm, the solvent was removed by prebaking on a hot plate at 90° C. for 90 seconds, and a coating film having a film thickness of 3 μm was formed. Next, exposure was performed through a predetermined mask using FX-85S (i-line method, manufactured by Nikon Corporation). After exposure, at the temperature shown in Table 6, after only passing the time shown in Table 6, use 0.4% by weight of tetramethylammonium hydroxide aqueous solution at 25 ° C for 35 seconds after spray development, then shower with ultrapure water Wash for 1 minute. Through these operations, the optimum exposure amount (E opt ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
wavelengthaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The present invention provides a method for producing a cured film having excellent patterning performance, ITO sputtering resistance, and heat-resistant transparency, which can be produced with high and stable sensitivity, and which can form contact holes by slit coating. The manufacturing method of this cured film comprises the following steps: the step of making the temperature of the photosensitive resin composition 10° C. or lower, the step of applying the photosensitive resin composition to the substrate by slit, The process of removing the solvent from the composition, the process of exposing the photosensitive resin composition from which the solvent has been removed to active light, the process of 45 seconds or more at room temperature, the process of developing with an aqueous developer, and the process of thermal curing The photosensitive resin composition contains the following components: (ingredient A) a structural unit containing a residue with an acid group protected by an acid decomposable group, a structural unit with a crosslinking group, a carboxyl group and / or a phenolic A copolymer of a structural unit of a hydroxyl group, (component B) a photoacid generator, and (component C) a solvent.

Description

technical field [0001] The present invention relates to a method for producing a cured film, a photosensitive resin composition, a cured film, an organic EL (organic electro) display device, and a liquid crystal display device. Background technique [0002] In the past, in electronic components such as liquid crystal display elements, integrated circuit elements, solid-state imaging elements, and organic EL, it is generally used to form a planarizing film for imparting flatness to the surface of the electronic component, and to protect the electronic component from deterioration or damage. The photosensitive resin composition is used for a film or an interlayer insulating film that maintains insulation. In recent years, along with the increase in size of display devices, there is a demand for slit coater suitability for coating and manufacturing with a slit coater. In addition, with this increase in size, exposure becomes time-consuming, and high sensitivity is required in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G03F7/00G03F7/039G03F7/004G02F1/1333H01L27/32
CPCG02F1/13G02F1/1303G03F7/00G03F7/004G03F7/0045H10K71/00H10K99/00
Inventor 安藤豪杉原幸一
Owner FUJIFILM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap