Resin composition, phase-ontrast film, method for manufacturing phase-contrast film, and long circularly-polarizing plate

A technology of resin composition and retardation film, applied in polarizing elements, instruments, optics, etc., can solve the problems of difficulty in large area, low manufacturing efficiency, waste, etc., and achieve easy manufacturing, excellent heat resistance and transparency Effect

Inactive Publication Date: 2013-09-04
ZEON CORP
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, when it is desired to cut out a rectangular product from a long stretch film, only a rectangular film that is obliquely inclined relative to the long direction can be cut out, resulting in more waste.
Therefore, the manufacturing efficiency becomes low, and it is difficult to enlarge the area

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resin composition, phase-ontrast film, method for manufacturing phase-contrast film, and long circularly-polarizing plate
  • Resin composition, phase-ontrast film, method for manufacturing phase-contrast film, and long circularly-polarizing plate
  • Resin composition, phase-ontrast film, method for manufacturing phase-contrast film, and long circularly-polarizing plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0129] Hereinafter, the present invention will be specifically described by showing examples, but the present invention is not limited to the following examples, and can be implemented with any changes within the scope not departing from the claims of the present invention and their equivalents.

[0130] [explanation of evaluation method]

[0131] (Measuring method of glass transition temperature)

[0132] The glass transition temperature of the resin composition was measured by heating up at 20°C / min using a differential scanning calorimeter (EXSTAR6220 manufactured by Seiko Instruments).

[0133] (Measurement method of haze)

[0134] According to JIS K7361-1997, haze was measured at 5 places using the "nephelometer NDH-300A" by Nippon Denshoku Industries Co., Ltd., and it calculated|required from the average value.

[0135] (Re 450 、Re 550 and Re 650 , Nz450, Nz550 and Nz650 determination method)

[0136] Using AxoScan manufactured by AXOMETRICS, the in-plane direction...

manufacture example 1

[0142] [Manufacture Example 1: Manufacture of Styrene-Maleic Anhydride Copolymer B1]

[0143] A complete mixing reactor with a stirrer, a tower plug flow reactor, and a devolatilization tank with a preheater are connected in series to form a manufacturing device. 85 parts by mass of styrene, 15 parts by mass of maleic anhydride, 0.02 parts by mass of 1,1-bis(t-butylperoxy)-cyclohexane, and 0.2 parts by mass of n-dodecylmercaptan were mixed to prepare a raw material solution. This raw material solution was introduced into a complete mixing type reactor controlled at a temperature of 130° C., and stirred at 180 rpm. Next, the reaction liquid is continuously withdrawn from the fully mixed reactor and introduced into a tower-type plug-flow reactor, which is adjusted to have a temperature of 130°C to 160°C along the liquid flow direction. temperature gradient. This reaction solution was introduced into a devolatilizer controlled at a temperature of 235° C. and a pressure of 1.0 k...

manufacture example 2

[0144] [Manufacture example 2: Manufacture of styrene-maleic anhydride copolymer B2]

[0145]Except having adjusted the quantity of styrene to 90 mass parts, and the quantity of maleic anhydride to 10 mass parts, it carried out similarly to manufacture example 1, and manufactured the styrene-maleic anhydride copolymer B2. The obtained styrene-maleic anhydride copolymer B2 contained 92% by weight of styrene units and 8% by weight of maleic anhydride units. In addition, the glass transition temperature of the styrene-maleic anhydride copolymer B2 was 102°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Glass transition temperatureaaaaaaaaaa
Glass transition temperatureaaaaaaaaaa
Glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

A resin composition comprising polyphenylene ether (A) and a copolymer (B) containing repeating units derived from styrene and repeating units derived from maleic anhydride, the amount of the repeating units derived from maleic anhydride in copolymer (B) being set to 5-20 wt%, and the polyphenylene ether (A) being set to 25-35 parts by weight per 100 parts by weight of the repeating unit derived from styrene.

Description

technical field [0001] The present invention relates to a resin composition, a retardation film using the resin composition, a method for producing the retardation film, and a long circular polarizing plate using the retardation film. Background technique [0002] In a display device such as a liquid crystal display device, a retardation film may be used, for example, to correct retardation (retardation) or the like. As the retardation film, one obtained by stretching a long unstretched film formed of a resin in the MD direction (machine direction) or the TD direction (traverse direction) and orienting the molecules contained in the film is known. A stretched film is preferable because it can be easily produced. Here, the MD direction is the conveyance direction of the film in a production line. The MD direction generally coincides with the long direction of the elongated film, also referred to as the machine direction. Furthermore, the TD direction is a direction perpend...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L25/08B29C55/04C08J5/18C08L35/06G02B5/30
CPCB29K2025/06B29K2071/12B29K2995/0034C08J5/18C08J2325/08C08J2471/12B29C55/04G02B5/3083B29C55/12C08L71/12C08L25/08C08L35/06G02B5/30B29C55/02G02B1/08
Inventor 波多野拓
Owner ZEON CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products