Method for preparing Portland cement clinker

A technology for Portland cement and clinker is applied in the field of preparation of Portland cement clinker, which can solve the problems of high reaction temperature and decrease, and achieve the effects of simple preparation process, good chemical uniformity and small product particle size.

Inactive Publication Date: 2011-08-17
TONGJI UNIV
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when using the traditional high-temperature sintering reaction method to synthesize cement clinker minerals, not only the required reaction temperature is high, but also because mineralizers are usually used to reduce the sintering temperature or make certain crystal forms of single mineral crystals stable at room temperature. Exist, will introduce other components in cement clinker minerals

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of preparation method of portland cement clinker, according to the formula preparation sol of table 1, concrete preparation method comprises the following steps:

[0021] Tetraethyl orthosilicate ((C 2 h 5 O) 4 Si) 54.74 parts, calcium nitrate hydrate (Ca(NO 3 ) 2 4H 2 O) 186.32 parts, ethanol (C 2 h 5 OH) 1239.65 parts, nitric acid (HNO 3 ) 17.57 parts mixed, according to the weight ratio ethyl orthosilicate ((C 2 h 5 O) 4 Si) 24.18 parts, calcium nitrate hydrate (Ca(NO 3 ) 2 4H 2 O) 54.88 parts, ethanol (C 2 h 5 OH) 433.65 parts, nitric acid (HNO 3 ) 6.15 parts mixed, according to the weight ratio of aluminum nitrate hydrate (Al(NO 3 ) 3 9H 2 O) 19.44 parts, calcium nitrate hydrate (Ca(NO 3 ) 2 4H 2 O) 18.36 parts, hexamethylenetetramine ((CH 2 ) 6 N 4 )8.50 parts, acetylacetone ((CH 3 CO) 2 CH(AcAcH)) 2.38 parts, deionized water 107.00 parts mixed, aluminum nitrate hydrate (Al(NO 3 ) 3 9H 2 O) 20.06 parts, calcium nitrate hydrate (...

Embodiment 2

[0023] A kind of preparation method of portland cement clinker, according to the formula preparation sol of table 1, concrete preparation method comprises the following steps:

[0024] Tetraethyl orthosilicate ((C 2 h 5 O) 4 Si) 50.18 parts, calcium nitrate hydrate (Ca(NO 3 )2 4H 2 O) 170.79 parts, ethanol (C 2 h 5 OH) 1136.35 parts, nitric acid (HNO 3 ) 16.11 parts mixed, according to the weight ratio of ethyl orthosilicate ((C 2 h 5 O) 4 Si) 30.23 parts, calcium nitrate hydrate (Ca(NO 3 ) 2 4H 2 O) 68.60 parts, ethanol (C 2 h 5 OH)542.07 parts, nitric acid (HNO 3 ) 7.68 parts are mixed, according to the weight ratio of aluminum nitrate hydrate (Al(NO 3 ) 3 9H 2 O) 13.89 parts, calcium nitrate hydrate (Ca(NO 3 ) 2 4H 2 O) 13.11 parts, hexamethylenetetramine ((CH 2 ) 6 N 4 )6.07 parts, acetylacetone ((CH 3 CO) 2 CH(AcAcH)) 1.70 parts, deionized water 80.00 parts mixed, aluminum nitrate hydrate (Al(NO 3 ) 3 9H 2 O) 23.15 parts, calcium nitrate hydrat...

Embodiment 3

[0026] A kind of preparation method of portland cement clinker, according to the formula preparation sol of table 1, concrete preparation method comprises the following steps:

[0027] Tetraethyl orthosilicate ((C 2 h 5 O) 4 Si) 45.61 parts, calcium nitrate hydrate (Ca(NO 3 ) 2 4H 2 O) 155.26 parts, ethanol (C 2 h 5 OH) 1033.04 parts, nitric acid (HNO 3 ) 14.65 parts mixed, according to the weight ratio of ethyl orthosilicate ((C 2 h 5 O) 4 Si) 36.28 parts, calcium nitrate hydrate (Ca(NO 3 ) 2 4H 2 O) 82.33 parts, ethanol (C 2 h 5 OH) 650.48 parts, nitric acid (HNO 3 ) 9.22 parts are mixed, according to the weight ratio of aluminum nitrate hydrate (Al(NO 3 ) 3 9H 2 O) 11.11 parts, calcium nitrate hydrate (Ca(NO 3 ) 2 4H 2 O) 10.49 parts, hexamethylenetetramine ((CH 2 ) 6 N 4 )4.86 parts, acetylacetone ((CH 3 CO) 2 CH(AcAcH)) 1.36 parts, deionized water 65.00 parts mixed, aluminum nitrate hydrate (Al(NO 3 ) 3 9H 2 O) 24.69 parts, calcium nitrate hyd...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for preparing Portland cement clinker. The method comprises the following steps: proportionally mixing tetraethoxysilane, a calcium nitrate hydrate, an aluminium nitrate hydrate, a ferric nitrate hydrate, ethanol, nitric acid, hexamethylenetetramine, acetylacetone, deionized water and the like uniformly to obtain four kinds of mixed liquid, fully stirring the four kinds of mixed liquid respectively at the temperature of 50-70 DEG C until proper viscosity to obtain monomineral sols of the Portland cement clinker, then mixing the four monomineral sols in a massratio of (36-55):(24-40):(11-19):(20-31), ageing the mixture to form gel, carrying out heat treatment on the gel at the temperature of 1150-1200 DEG C for 4-6 hours and cooling the gel to the room temperature, thus obtaining the Portland cement clinker. Compared with the prior art, the method has the following advantages: the preparation process is simple; the reaction process is easy to control;and the product has high uniformity and purity and can be fired at the temperature lower than the temperature in the traditional methods.

Description

technical field [0001] The invention relates to a preparation method of inorganic materials, in particular to a preparation method of Portland cement clinker. Background technique [0002] When studying cement hydration, in order to minimize unknowable factors, laboratory-synthesized cement and clinker single minerals are usually used as research objects. However, when using the traditional high-temperature sintering reaction method to synthesize cement clinker minerals, not only the required reaction temperature is high, but also because mineralizers are usually used to reduce the sintering temperature or make certain crystal forms of single mineral crystals stable at room temperature. Existence, will introduce other components in cement clinker minerals. [0003] In recent years, with the emergence of various chemical methods, it has brought about a revolution in the synthesis of cement clinker minerals. They all try to overcome the shortcomings of the traditional solid-s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/02
Inventor 刘贤萍王培铭陈红霞
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap