Direct spinning method for single-part four-end 2200dtex high-modulus low-shrinkage polyester industrial yarns

A high-modulus, low-shrinkage technology, applied in the field of spinning, can solve the problems of affecting single parts, low production efficiency, maximization of production capacity and reduction of production costs, and achieve the effect of reducing production costs and improving production capacity.

Active Publication Date: 2011-08-31
WUXI TAIJI IND
View PDF7 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the production of high-modulus low-shrinkage polyester industrial yarn is mostly one-step spinning with 3 heads / position and 4 heads / position, which can only be used to produce polyester yarns of 1100dtex~1670dtex, of which 2200dtex high-modulus low-shrinkage polyester Industrial yarn is generally realized by joint stock method, and the production efficiency is not high, which seriously affects the maximization of production capacity of a single part and the reduction of production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Example 1: A direct spinning method of 2200 dtex high modulus low shrinkage polyester industrial yarn with four ends in a single position, including the following process steps:

[0015] (1) Processing high-viscosity polyester chips: the raw material of polyester chips with a viscosity of 0.68dl / g is screened and then enters the high-speed rotating Su Lida crystallizer for pre-crystallization. The pre-crystallizer is heated by heat transfer oil, and the pre-crystallization temperature is 180 ℃ , The pre-crystallization time is 12min; then solid-phase polymerization is carried out to obtain high-viscosity polyester chips, the temperature of solid-phase polycondensation is 215℃, and the time is 24h; the viscosity of the high-viscosity polyester chips is 1.05dl / g, and the terminal carboxyl group is less than 15mol / t;

[0016] (2) Melt spinning: The high-viscosity polyester chips after solid-phase polymerization enter the screw extruder through the screw silo under the protection...

Embodiment 2

[0019] Example 2: A direct spinning method of 2200 dtex high modulus low shrinkage polyester industrial yarn with four ends in a single position, including the following process steps:

[0020] (1) Processing high-viscosity polyester chips: After sieving the raw material of polyester chips with a viscosity of 0.68dl / g, enter the high-speed rotating Suridar crystallizer for pre-crystallization. The pre-crystallizer is heated by heat transfer oil, and the pre-crystallization temperature is 185℃. , The pre-crystallization time is 8min; then solid-phase polymerization is carried out to obtain high-viscosity polyester chips, the temperature of solid-phase polycondensation is 230℃, and the time is 20h; the viscosity of the high-viscosity polyester chips is 1.15dl / g, and the terminal carboxyl group is less than 15mol / t;

[0021] (2) Melt spinning: the high-viscosity polyester chips after solid-phase polymerization enter the screw extruder through the screw silo under the protection of nitr...

Embodiment 3

[0024] Example 3: A direct spinning method of 2200 dtex high modulus low shrinkage polyester industrial yarn with four ends in a single position, including the following process steps:

[0025] (1) Processing high-viscosity polyester chips: the raw material of polyester chips with a viscosity of 0.68dl / g is screened and then enters the high-speed rotating Su Lida crystallizer for pre-crystallization. The pre-crystallizer is heated by heat transfer oil, and the pre-crystallization temperature is 180°C. , The pre-crystallization time is 10min; then solid-phase polymerization is carried out to obtain high-viscosity polyester chips, the temperature of solid-phase polycondensation is 220℃, and the time is 23h; the viscosity of the high-viscosity polyester chips is 1.1dl / g, and the terminal carboxyl group is less than 15mol / t;

[0026] (2) Melt spinning: the high-viscosity polyester chips after solid-phase polymerization enter the screw extruder through the screw silo under the protection...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Heightaaaaaaaaaa
Heightaaaaaaaaaa
Login to View More

Abstract

The invention relates to a direct spinning method for single-part four-end 2200dtex high-modulus low-shrinkage polyester industrial yarns, which comprises the following process steps of: pre-crystallizing raw materials, such as polyester slices, and obtaining polyester slices by solid phase polymerization; heating the polyester slices in a screw extruder to obtain polyester melts, distributing the polyester melts to melt branch pipes through a main melt pipe, then metering via a metering pump, feeding the melts to a spinning assembly and extruding the melts from a spinneret to form tows, and subjecting the tows to cooling shaping in a circular blowing device; oiling the surface of the tows, drawing, shaping and relaxing the tows by using six pairs of rollers, forming first-stage drawing between the first pair of rollers and the second pair of rollers, forming second-stage drawing between the second pair of rollers and the third pair of rollers, performing constant velocity shaping between the third pairs of rollers and the fourth pair of rollers as well as between the fourth pair of rollers and the fifth pair of rollers, and forming retraction shaping between the fifth pair of rollers and the sixth pair of rollers; and coiling to obtain the polyester industrial yarns. The polyester yarns produced according to the method disclosed by the invention have high breaking strength, effectively-improved the yield of single part and lowered production cost.

Description

Technical field [0001] The invention relates to a spinning method, in particular to a direct spinning method of a single-position four-end 2200 dtex high modulus low shrinkage polyester industrial yarn, which belongs to the field of polyester industrial yarn manufacturing. Background technique [0002] At present, the production of high-modulus and low-shrinkage polyester industrial yarns is mostly one-step 3-end / position and 4-end / position spinning, which can only be used to produce 1100dtex~1670dtex polyester yarn, of which 2200dtex high modulus low shrinkage polyester Industrial yarns are generally realized by the method of jointing, and the production efficiency is not high, which seriously affects the maximum production capacity of a single part and the reduction of production costs. Summary of the invention [0003] The purpose of the present invention is to overcome the deficiencies in the prior art and provide a direct spinning method of 2200dtex high modulus and low shrin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01D5/084D01D5/088D01D5/096D01D5/16D01D1/00D01D1/04
Inventor 许其军姚峻季永忠
Owner WUXI TAIJI IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com