Method for deducing stress intensity factor of butt joint containing I-type center bursts and application

A stress intensity factor, butt joint technology, applied in special data processing applications, instruments, electrical digital data processing, etc., can solve problems such as the inability to guide the structural design of butt joints, and the lack of a stress intensity factor formula.

Inactive Publication Date: 2011-09-07
HARBIN INST OF TECH
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0015] The purpose of the present invention is to provide a derivation method and application of the stress intensity factor of a butt joint containing a type I central crack, so as to solve the problem that the joint with a reinforcement is not provided in the prior art and the butt joint contains a type I central crack and is subjected to tension The stress intensity factor formula under load cannot guide the structural design of butt joints with I-type central penetrating cracks and a certain reinforcement
[0016] The present invention also solves the problem of how to solve the stress intensity factor of a butt joint containing a type I central crack through the working load, crack size and joint shape, and how to use the formula to solve the critical crack size and critical stress of a butt joint containing a type I central crack and the remaining life of the connector

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for deducing stress intensity factor of butt joint containing I-type center bursts and application
  • Method for deducing stress intensity factor of butt joint containing I-type center bursts and application
  • Method for deducing stress intensity factor of butt joint containing I-type center bursts and application

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0101] Specific implementation mode one: as Figure 1~3 As shown, the specific process of the derivation method of the stress intensity factor of the butt joint with type I central crack described in this embodiment is:

[0102] Step 1. Analytical calculation The stress intensity factor formula when only the weld reinforcement h is considered:

[0103] Based on the situation that the joint with reinforcement contains a central crack (such as the attached figure 2 shown), it can be seen from any fracture mechanics textbook that for an infinite plate with a central penetrating crack subjected to uniform tensile stress, the Westcrgacrd stress function of the problem is:

[0104] Z I ( z ) = σz z 2 - a 2 - - - ( 5 ...

specific Embodiment approach 2

[0137] Specific implementation mode two: as Figure 1~3 As shown, in this embodiment, the stress intensity factor formula of a butt joint with a type I central crack is used to determine the critical crack size a of a butt joint with a type I central penetrating crack with a certain reinforcement c ;

[0138] Specific steps are as follows:

[0139] Step 1. Measure the fracture toughness K of the weld material IC ;

[0140] Step 2. Substituting the shape parameters of the joint: half-width w of the capping weld bead, weld reinforcement h, arc transition radius r of the weld toe and half t of the plate thickness into formula (13) to obtain f;

[0141] Step 3: Establish and calculate the critical crack size a of the butt joint with a type I central penetration crack with a certain reinforcement height c The formula for:

[0142] a c = ( πt ...

specific Embodiment approach 3

[0145] Specific implementation mode three: as Figure 1~3 As shown, in this embodiment, the critical load σ of the butt joint with a type I central penetrating crack and a certain reinforcement is determined by using the stress intensity factor formula of the butt joint with a type I central penetrating crack and a certain reinforcement c ;

[0146] Specific steps are as follows:

[0147] Step 1. Establish and calculate the critical load σ of the butt joint with a certain reinforcement height of the type I central penetrating crack c The formula for:

[0148] σ c = K IC { 1 + ( 0.85038 + 0.84549 h h + t ) exp ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for deducing a stress intensity factor of a butt joint containing I-type center bursts and application, belonging to the technical field of welding and solving the problems on a solution to the stress intensity factor of the butt joint containing the I-type center bursts by means of work loads, burst dimensions and joint shapes as well as on solutions to criticalburst dimensions, critical stress and residual service life of the butt joint containing the I-type center bursts by using a formula in the specifications. The method comprises the following steps of: firstly, solving a stress intensity factor formula for the butt joint containing the I-type center bursts by using an analysis method when the surplus height of the joint is only considered, then solving a stress intensity factor formula by means of a finite element calculation method and a result regression analysis method when the width of a capping bead and the transition arc radius of a weldtoe are considered, and further determining the stress intensity factor formula of the butt joint containing the I-type center bursts. By applying the formula, the critical burst dimensions, the critical stress and the residual service life of the butt joint containing the I-type center bursts can be further solved. The method is suitable for conditions of any materials of the butt joint containing the I-type center bursts.

Description

technical field [0001] The invention relates to a derivation method and application of a stress intensity factor, in particular to a derivation method and application of a stress intensity factor of a butt joint with an I-type central penetrating crack with a certain reinforcement, and belongs to the field of welding technology. Background technique [0002] Welding is widely used in structural design as a connection method, and the equal matching principle (the strength of the filler material is equal to that of the base metal) is generally adopted for the selection of welding filler materials. Due to its local rapid heating and cooling process, large residual tensile stress is generated in the weld area. In addition, defects such as pores and cracks are prone to occur in the weld, and grains in some areas are coarse. These all make the load-bearing capacity of the weld area It is lower than the bearing capacity of the base metal, and the welded structure is prone to stress...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G06F17/50
Inventor 杨建国王涛方洪渊刘雪松董志波张勇张敬强王佳杰
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap