Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Integrally casting technology of tire mold patterned ring basic model, silica gel, gypsum and aluminum ring

A tire mold and integral casting technology, which is applied in the field of tire mold pattern circle base mold, silica gel, gypsum, and aluminum ring integral casting technology, which can solve the problem of increased workload and labor intensity, inability to guarantee accuracy and concentricity, and production cost burden and other issues, to achieve the effect of improving work efficiency, saving electricity consumption, and reducing the cost of archetypes

Inactive Publication Date: 2012-02-15
淄博昂达机电设备销售有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the existing tire mold processing technology, the main feature is that the base mold, silica gel, primary gypsum and secondary gypsum are all processed into eight pieces on average, so there are the following defects: ① Since the base mold is processed into eight pieces, it is necessary to The processing and programming are programmed eight times, and the blank material of the base mold is wasteful, the processing volume is large, the corresponding workload is large, and the processing cycle is long; Not only is a large amount of silica gel wasted, but the processing accuracy cannot be guaranteed; ③The secondary gypsum processing is also divided into eight pieces, which also has the problem of heavy workload and waste of gypsum raw materials; Therefore, it is necessary to carry out two drying processes, one drying and two dryings. After drying, it is easy to deform. After the second drying, it is necessary to assemble the gypsum twice. The surface problem cannot guarantee the accuracy and concentricity after assembly, and increases the workload and labor intensity again
[0003] Therefore, the processing technology of this kind of tire mold is not ideal in the actual production process. The burden on it is poor in practicability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The overall casting process of the pattern ring base mold, silica gel, gypsum and aluminum ring of the tire mold mainly includes the following steps,

[0018] 11. First, the base mold is made of the base mold blank material, and the base mold blank is roughly turned out of the basic tire shape by a CNC lathe. After the tread reaches the specified size, the entire circular base mold blank is divided into eight equal parts, and processed by five-axis The center mills out the tire pattern surface on the outer surface of each formed base mold, and the base mold is completed; the base mold blank can be processed into a complete circle at one time, and the parts are turned into a whole, so that the whole circle of the base mold can be formed at one time. , effectively improve the concentricity of the tire mold circle, reduce the workload, and effectively guarantee the dimensional accuracy of subsequent tire processing;

[0019] 1.2. Use a professional silicone lining mold to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an integral casting technology of a tire mold patterned ring basic model, silica gel, gypsum and an aluminum ring, which belongs to the semi-steel tire mold field. The technology comprises the following steps: 1.1 a basic model base is prepared to a basic tire shape , a whole circle is divided into eight equal parts, the external surface of the basic model base is milled a patterned surface; 1.2 the basic model is placed in a silica gel liner mold, then the regulated silica gel is injected between an inner wall of the silica gel liner mold and a cylindrical surface ofthe basic model; 1.3 the silica gel liner mold is opened after the silica gel in the silica gel liner mold is solidified, the formed silica gel is dismounted from the surface of the basic model; 1.4 the formed silica gel is placed in the silica gel liner mold, then secondary gypsum is injected in the silica gel; 1.5 a gypsum model is placed in a secondary drying furnace for heating and drying. The silica gel and gypsum model of the present invention are capable of realizing one-step forming, optimizing the technology step of the tire mold, reducing the production manufacture cost and decreasing workload and labor intensity of operators.

Description

technical field [0001] The overall casting process of tire mold pattern ring base mold, silica gel, gypsum, and aluminum ring belongs to the field of semi-steel tire molds, and specifically designs an integral core injection process for tire mold gypsum cores. Background technique [0002] At present, the processing of general-purpose tire molds is divided into two types: flexible molds and two-half molds. In the existing tire mold processing technology, the main feature is that the base mold, silica gel, primary gypsum and secondary gypsum are all processed into eight pieces on average, so there are the following defects: ① Since the base mold is processed into eight pieces, it is necessary to The processing and programming are programmed eight times, and the blank material of the base mold is wasteful, the processing volume is large, the corresponding workload is large, and the processing cycle is long; Not only is a large amount of silica gel wasted, but the processing a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C33/38
Inventor 宋世忠
Owner 淄博昂达机电设备销售有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products