Artificial hemp weaving process

A man-made and handcrafted technology, applied in the field of weaving technology, can solve the problems of poor quality of the final weaving products and achieve the effect of improving quality

Inactive Publication Date: 2012-03-07
SUZHOU DONGMAO TEXTILE IND
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide an artificial hemp weaving process, which can solve the final problem caused by the different characteristics of artificial silk and polyester filament when using artificial silk and polyester filament for mixed weaving. Disadvantages of poor quality weaving products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] In order to further disclose the technical solutions of the present invention, the implementation manners of the present invention are described in detail.

[0013] In the rayon weaving process disclosed by the present invention, the different characteristics of rayon and polyester filament are taken into account, that is, rayon has poor water resistance, is easy to break when exposed to water, and has weak tensile strength and is easy to break under force; while polyester is long The wire has high twist and strong tensile strength. Therefore, before the mixed spinning of rayon and polyester filaments, the polyester filaments are pretreated first, so that the characteristics of the pretreated rayon and polyester filaments are more consistent, thereby ensuring that the final weaving products the quality of. Based on above-mentioned design, the present invention has adopted following steps:

[0014] Put polyester filaments in a water steamer at a water temperature of 75...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an artificial hemp weaving process. In the artificial hemp weaving process, when artificial silk and dacron filaments are blended and woven into fabrics, i.e. artificial hemp, firstly, the artificial silk is placed into a water steaming box to be steamed for 80 minutes at the water temperature being 75 to 80 DEG C, the pre-forming is carried out for 12 to 20 hours after the artificial silk is taken out, and then, the artificial silk and the dacron filaments are fed into a knitting machine to be blended and woven into fabrics, i.e. the artificial hemp. When the process is adopted, different characteristics of the artificial silk and the dacron filaments are considered, and the artificial silks are pretreated, so the characteristics of the artificial silk more conform to the characteristics of the dacron filaments, the proceeding of the subsequent process is more favorably realized, and the quality of the finally woven products is improved.

Description

technical field [0001] The invention relates to a weaving process, in particular to a weaving process using different raw material silks for mixed weaving. Background technique [0002] When using different raw material yarns for mixed spinning, the tension of various raw material yarns and suitable processing temperature are important parameters that affect the quality of the final product. Therefore, it is necessary to take into account the characteristics of different raw material yarns when designing the textile process. For example, when we use rayon and polyester filament to weave into a fabric, that is, artificial hemp, because the characteristics of rayon and polyester filament are quite different, we need to use a specific process for weaving. Specifically, rayon has poor water resistance, is easy to break when exposed to water, and has weak tensile strength and is easy to break under force; while polyester filament has high twist and strong tensile strength. In or...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06B1/00
Inventor 黄锡坚钟钊伟
Owner SUZHOU DONGMAO TEXTILE IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products