Novel blending spinning process

A process and a new type of technology, applied in textiles, textiles, papermaking, fabrics, etc., can solve the problems of multiple dams and unsatisfactory effects, and achieve the effect of not being easy to break and reducing the number of dams

Inactive Publication Date: 2017-11-17
NANTONG XIANGJIA TEXTILE SCI & TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the effect of the above-mentioned traction and pretreatment process is still unsatisfactory, and there will still be more baffles in the final woven product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The novel hybrid textile process of present embodiment, this hybrid textile process comprises the steps:

[0025] (1) Measure the maximum stretchable limit of nylon fiber, that is, the maximum pressure value that can be applied to it;

[0026] (2) Put the cotton fiber and polyester fiber in a water steamer, steam for 60 minutes at a water temperature of 90°C;

[0027] (3) Place the cotton and polyester fibers treated in step (2) in a natural state for pre-setting for 16 hours;

[0028] (4) Use a water jet loom to weave cotton fiber, polyester fiber and nylon fiber in a ratio of 2:3:1 for the maximum pressure value in step (1); Use nozzles with a specification of 75-40 for traction, nozzles with a specification of 75-40 for drawing polyester fiber filaments, and nozzles with a specification of 45-20 for nylon fiber filaments.

Embodiment 2

[0030] The novel hybrid textile process of present embodiment, this hybrid textile process comprises the steps:

[0031] (1) Measure the maximum stretchable limit of nylon fiber, that is, the maximum pressure value that can be applied to it;

[0032] (2) Put the cotton fiber and polyester fiber in a water steamer at a water temperature of 80°C for 70 minutes;

[0033] (3) Place the cotton and polyester fibers treated in step (2) in a natural state for pre-setting for 12 hours;

[0034] (4) Use a water jet loom to weave cotton fiber, polyester fiber and nylon fiber in a ratio of 2:3:1 for the maximum pressure value in step (1); Use nozzles with a specification of 75-40 for traction, nozzles with a specification of 75-40 for drawing polyester fiber filaments, and nozzles with a specification of 45-20 for nylon fiber filaments.

Embodiment 3

[0036] The novel hybrid textile process of present embodiment, this hybrid textile process comprises the steps:

[0037] (1) Measure the maximum stretchable limit of nylon fiber, that is, the maximum pressure value that can be applied to it;

[0038] (2) Put the cotton fiber and polyester fiber in a water steamer at a water temperature of 85°C for 65 minutes;

[0039] (3) Place the cotton and polyester fibers treated in step (2) in a natural state for pre-setting for 14 hours;

[0040] (4) Use a water jet loom to weave cotton fiber, polyester fiber and nylon fiber in a ratio of 2:3:1 for the maximum pressure value in step (1); Use nozzles with a specification of 75-40 for traction, nozzles with a specification of 75-40 for drawing polyester fiber filaments, and nozzles with a specification of 45-20 for nylon fiber filaments.

[0041] In summary, as described in Examples 1-3, compared with the existing mixed textile process of the enterprise, the improved process of the prese...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a novel blending spinning process. The method comprises the following steps of 1, measuring a maximum stretchable limit of nylon fiber filaments, namely a maximum exerted pressure value; 2, placing cotton fiber filaments and polyester fiber filaments into a water steaming tank to be steamed for 60-70 minutes, wherein the water temperature is 80-90 DEG C; 3, placing the cotton fiber filaments and the polyester fiber filaments which are processed in the step 2 in a natural state to be preshaped for 12-16 hours; 4, adopting a water-jet loom to conduct blending spinning on the cotton fiber filaments, the polyester fiber filaments and the nylon fiber filaments with the maximum pressure value in the step 1, wherein when traction is conducted on the cotton fiber filaments by the water-jet loom, a nozzle with the specification of 75-40 is adopted, when traction is conducted on the polyester fiber filaments by the water-jet loom, a nozzle with the specification of 75-40 is adopted, and when traction is conducted on the nylon fiber filaments, a nozzle with the specification of 45-20 is adopted. The novel blending spinning process has the advantages that the defect can be overcome that when the polyester fiber filaments and the nylon fiber filaments are adopted to be subjected to blending spinning, the quality of final spun products is less than satisfactory because the characteristics of the polyester fiber filaments and the nylon fiber filaments are different.

Description

technical field [0001] The invention relates to a weaving process, in particular to a weaving process using different raw material silks for mixed weaving. Background technique [0002] When using different raw material yarns for mixed spinning, the tension of various raw material yarns and suitable processing temperature are important parameters that affect the quality of the final product. Therefore, it is necessary to take into account the characteristics of different raw material yarns when designing the textile process. For example, when we use polyester fiber and nylon fiber to weave into fabrics, since the characteristics of polyester fiber and nylon fiber are quite different, we need to use a specific process for weaving. Specifically, nylon fiber has poor shape retention, is easily deformed, and has poor heat resistance; while polyester fiber has good hot water resistance and good elastic recovery ability. In order to take care of the characteristics of different r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D15/00
CPCD10B2201/02D10B2331/02D10B2331/04D03D15/47
Inventor 仲伟德
Owner NANTONG XIANGJIA TEXTILE SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products