Blending technology

A kind of technology, the technology of hemp fiber, applied in the field of blending technology, can solve the problems that need to be further improved, and achieve the effect of preventing wrinkles, maintaining durability, and not easy to break

Inactive Publication Date: 2019-01-01
NANTONG SUZHONG TEXTILE
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, in order to improve other characteristics of cotton, hemp, and polyester blended yarns, manufacturers sometimes add other textile fiber materials to the yarns, or even change the yarn-making techniques and yarn structure, in order to obtain better quality blended yarn, but in the process of improvement, the elasticity and strength of cotton, linen and polyester blended yarns need to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] A kind of blending process, comprises the steps:

[0053] (1) Put the cotton fiber silk, hemp fiber silk and polyester fiber silk in the water tank, the water temperature is 60 ℃, cook for 80 minutes, then stand to cool to room temperature and then remove;

[0054] (2) placing the cotton fiber silk, hemp fiber silk and polyester fiber silk processed in step (1) in a natural state for presetting for 24 hours;

[0055] (3) respectively measure the stretchable maximum tensile value of cotton fiber silk, hemp fiber silk and polyester fiber silk;

[0056] (4) adopt water-jet loom to carry out three-way mixed spinning to cotton fiber silk, hemp fiber silk and polyester fiber silk with the lower value in three kinds of data that step (2) measures;

[0057] (5) drying the fabric obtained in step (4);

[0058](6) the fabric obtained in step (5) is cooled to room temperature;

[0059] (7) The dried fabric is sprayed with a sunscreen by a sprayer, and dried by a dryer. The comp...

Embodiment 2

[0062] A kind of blending process, comprises the steps:

[0063] (1) Put cotton fiber silk, hemp fiber silk and polyester fiber silk in a water tank at a water temperature of 70°C, cook for 100 minutes, then let it cool down to room temperature, and then remove it;

[0064] (2) placing the cotton fiber silk, hemp fiber silk and polyester fiber silk processed in step (1) in a natural state for presetting for 48 hours;

[0065] (3) respectively measure the stretchable maximum tensile value of cotton fiber silk, hemp fiber silk and polyester fiber silk;

[0066] (4) adopt water-jet loom to carry out three-way mixed spinning to cotton fiber silk, hemp fiber silk and polyester fiber silk with the lower value in three kinds of data that step (2) measures;

[0067] (5) drying the fabric obtained in step (4);

[0068] (6) the fabric obtained in step (5) is cooled to room temperature;

[0069] (7) The dried fabric is sprayed with a sunscreen by a sprayer, and dried by a dryer. The c...

Embodiment 3

[0072] A kind of blending process, comprises the steps:

[0073] (1) Put the cotton fiber silk, hemp fiber silk and polyester fiber silk in the water tank, the water temperature is 65 ℃, cook for 90 minutes, then let it stand and cool to room temperature, then remove it;

[0074] (2) placing the cotton fiber silk, hemp fiber silk and polyester fiber silk processed in step (1) in a natural state for presetting for 36 hours;

[0075] (3) respectively measure the stretchable maximum tensile value of cotton fiber silk, hemp fiber silk and polyester fiber silk;

[0076] (4) adopt water-jet loom to carry out three-way mixed spinning to cotton fiber silk, hemp fiber silk and polyester fiber silk with the lower value in three kinds of data that step (2) measures;

[0077] (5) drying the fabric obtained in step (4);

[0078] (6) the fabric obtained in step (5) is cooled to room temperature;

[0079] (7) The dried fabric is sprayed with a sunscreen by a sprayer, and dried by a dryer....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A blending technology comprises the following steps of (1) putting a cotton fiber filament, a hemp fiber filament and a polyester fiber filament in a water tank at the water temperature of 60 DEG C-70DEG C, cooking for 80-100 minutes, then standing, cooling to a room temperature and taking out; (2) putting the cotton fiber filament, the hemp fiber filament and the polyester fiber filament processed in the step (1) under a natural state and presetting for 24 to 48 hours; (3) measuring the maximum tension values of the cotton fiber filament, the hemp fiber filament and the polyester fiber filament; (4) using a water jet loom to carry out three-directional hybrid spinning on the cotton fiber filament, the hemp fiber filament and the polyester fiber filament with a lower value in the three kinds of data measured in the step (2); (5) drying a fabric obtained in the step (4); (6) cooling the fabric obtained in the step (5) to the room temperature; (7) using a spraying machine to spray a sun-screening agent on the dried fabric, and drying by a dryer; and (8) coloring the fabric dried in the step (5) to obtain a finished fabric.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a blending process. Background technique [0002] Cotton, linen, and polyester blends refer to textile products that are woven by blending cotton, linen, and polyester in a certain proportion. Cotton, linen, and polyester blends can be used to create a variety of garments. Compared with other fabrics, cotton, linen, and polyester blended fabrics have the advantage of being cheap. Cotton, linen, and polyester blended fabrics have the respective advantages of cotton, linen, and polyester, taking into account the advantages of environmental protection, breathability, comfort, good drape, and comfortable wearing. . Because the fabric has good elasticity and wear resistance under dry and wet conditions, stable size, and low shrinkage rate. It is consistent with the current international textile and clothing fashion trend. Linen-cotton blended fabrics are generally blended with 55...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D15/00D02G3/04D06B15/00D06M11/44D06M11/46D06M101/06D06M101/32D03D15/217D03D15/283
CPCD02G3/04D03D15/00D06B15/00D06M11/44D06M11/46D10B2331/04D10B2201/01D10B2201/02D06M2101/32D06M2101/06
Inventor 朱爱民
Owner NANTONG SUZHONG TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com