Light sky blue glass-metal screen printing paint

A technology of glass metal and Tianlan, applied in ink, household utensils, applications, etc., can solve the problems of high production cost, short life, non-environmental protection, etc., and achieve the effect of high product quality, low production cost and less pollution

Inactive Publication Date: 2012-05-16
NANTONG KST GLASS
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, whether the color tone of the ink is different before and after drying during printing is a problem that is easily overlooked
Generally speaking, for screen printing inks that are dried by heat-setting and light-setting, the color changes in shades, and the colorants and binders of organic inks are all organic matter. This kind of ink has a good effect on decorating flat glass, but the ink is attached The strength is poor, the chemical stability is not good, it is a short-lived decoration method, at the same time, the pollution is serious, it is not environmentally friendly, it is harmful to the human body, and the production cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Select blue ink, white ink, red ink, GFN emerald blue, BD blue, varnish, flux, linking agent, the weight ratio of each component is 34g for blue ink, 33g for white ink, 13g for red ink, 10g for GFN emerald blue, and BD blue 5g, varnish 2g, fluxing agent 3g, linking agent 1g, pay attention to the brightness of the ink color when mixing the ink, if the brightness is high, try to use the original color to mix, otherwise it is easy to make the ink "grey" and reduce the original color. For certain color brightness, choose 270-mesh synthetic fiber screen, and use a pneumatic stretcher. The binder agent is made of ethyl cellulose, terpineol, turpentine, and alkyd resin, which are stirred and ground, sintered and consolidated by glass at a high temperature, and the sintering temperature is 480°C to obtain a finished product.

Embodiment 2

[0017] Select blue ink, white ink, red ink, GFN emerald blue, BD blue, varnish, flux, linking agent, the weight of each component is 36g for blue ink, 35g for white ink, 15g for red ink, 12g for GFN emerald blue, and BD blue 7g, varnish 4g, fluxing agent 5g, linking agent 3g, pay attention to the brightness of the ink color when adjusting the ink, if the brightness is required to be mixed with the original color as much as possible, otherwise it will easily make the ink "grey" and reduce the original color. For certain color brightness, choose 300-mesh synthetic fiber screen and use pneumatic stretcher. The binder agent is made of ethyl cellulose, terpineol, turpentine, and alkyd resin, which are stirred and ground, and sintered and consolidated by glass at a high temperature at a sintering temperature of 520°C to obtain a finished product.

Embodiment 3

[0019] Select blue ink, white ink, red ink, GFN emerald blue, BD blue, varnish, flux, linking agent, the weight ratio of each component is 35g for blue ink, 34g for white ink, 14g for red ink, 11g for GFN emerald blue, and BD blue 6g, 3g of varnish, 4g of flux, and 2g of linking agent. Pay attention to the brightness of the ink color when mixing the ink. If the brightness is high, try to use the original color to mix it, otherwise it will easily make the ink "grey" and reduce the original color. For certain color brightness, choose 285-mesh synthetic fiber screen, and use a pneumatic stretching machine. The binder agent is made of ethyl cellulose, terpineol, turpentine, and alkyd resin. After stirring and grinding, the glass is sintered and consolidated at a high temperature at a sintering temperature of 500°C to obtain a finished product.

[0020] In summary, the glass metal screen printing oil of the present invention has less pollution, high product quality, low production ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to light sky blue glass-metal screen printing paint. The paint comprises the following components in parts by weight: 34-36 parts of blue ink, 33-35 parts of white ink, 13-15 parts of red ink, 10-12 parts of GFN turquoise blue, 5-7 parts of BD blue, 2-4 parts of varnish, 3-5 parts of flux and 1-3 parts of coupling agent. The paint has the advantages of less pollution, high product quality, lower production cost, economy and practicability.

Description

[0001] technical field [0002] The invention relates to a glass metal screen printing paint, in particular to a light sky blue glass metal screen printing paint and a production process thereof. [0003] Background technique [0004] At present, the graphic printing on the glass surface mainly adopts screen printing method, cleans the glass to be screen printed, prints the ink on the surface of the glass, and then adopts the curing measures of the ink to make the pattern firm and durable. The printing ink is dried To dry, the light color is lighter than the undried one after drying, and the dark color is darker after drying. In addition, whether the color tone of the ink is different before and after drying during printing is a problem that is easily overlooked. Generally speaking, for screen printing inks that are dried by heat-setting and light-setting, the color changes in shades, and the colorants and binders of organic inks are all organic matter. This kind of ink ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/14C09D11/06C09D11/10C09D11/02C03C17/00C09D11/105
Inventor 张玉平
Owner NANTONG KST GLASS