Deep blue glass-metal screen printing paint

A technology of dark blue glass and metal wire, applied in ink, household utensils, applications, etc., can solve the problems of high production cost, non-environmental protection, serious pollution, etc., and achieve the effect of low production cost, less pollution and high product quality

Inactive Publication Date: 2012-05-16
NANTONG KST GLASS
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, whether the color tone of the ink is different before and after drying during printing is a problem that is easily overlooked
Generally speaking, for screen printing inks that are dried by heat-setting and light-setting, the color changes in shades, and the colorants and binders of organic inks are all organic matter. This kind of ink has a good effect on decorating flat glass, but the ink is attached The strength is poor, the chemical stability is not good, it is a short-lived decoration method, at the same time, the pollution is serious, it is not environmentally friendly, it is harmful to the human body, and the production cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Choose white ink, yellow ink, black ink, AEL zhangqing, varnish, flux, linking agent, the weight ratio of each component is 43g for white ink, 25g for yellow ink, 6g for black ink, 17g for AEL zhangqing, 2g for varnish, 2g for auxiliary Solvent 3g, linking agent 1g, pay attention to the brightness of the ink color when mixing the ink, if the brightness is high, use the original color as much as possible to mix, otherwise it will easily make the ink "grey" and reduce the original color brightness, choose 270 Purpose Synthetic fiber screen, using pneumatic stretching machine, the requirement of stretching is uniform tension, 45 degrees between screens, choose chromium oxide coloring agent, borosilicate glass flux, linking agent made of ethyl fiber Sodium, terpineol, turpentine, and alkyd resin are stirred and ground, and the glass is sintered and consolidated at high temperature at a sintering temperature of 480°C to obtain a finished product.

Embodiment 2

[0017] Select white ink, yellow ink, black ink, AEL zhangqing, varnish, flux, and linking agent. The weight ratio of each component is 45g for white ink, 27g for yellow ink, 8g for black ink, 19g for AEL zhangqing, 4g for varnish, and 4g for auxiliary. Flux 5g, linking agent 2g, pay attention to the brightness of the ink color when adjusting the ink, if the brightness is high, use the original color as much as possible to mix, otherwise it will easily make the ink "grey" and reduce the original color brightness, choose 300 Purpose Synthetic fiber screen, using pneumatic stretching machine, the requirement for stretching is uniform tension, 90 degrees between screens, choose chromium oxide colorant, borosilicate glass flux, linking agent made of ethyl fiber Sodium, terpineol, turpentine, and alkyd resin are stirred and ground, and the glass is sintered and consolidated at high temperature at a sintering temperature of 520°C to obtain a finished product.

Embodiment 3

[0019] Choose white ink, yellow ink, black ink, AEL zhangqing, varnish, flux, linking agent, the weight ratio of each component is 44g for white ink, 26g for yellow ink, 7g for black ink, 18g for AEL zhangqing, 3g for varnish, 3g for auxiliary Flux 4g, linking agent 1.5g, pay attention to the brightness of the ink color when mixing the ink, if the brightness is high, try to use the original color to mix, otherwise it is easy to make the ink "grey" and reduce the original color brightness, choose 285-mesh synthetic fiber screen, using a pneumatic stretching machine, the requirement for stretching the screen is uniform tension, the angle between the screens is 22.5 degrees, choose chromium oxide colorant, borosilicate glass flux, and the linking agent is made of ethyl Cellulose, terpineol, turpentine, and alkyd resin are stirred and ground, and the glass is sintered and consolidated at a high temperature at a sintering temperature of 500°C to obtain a finished product.

[0020] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to deep blue glass-metal screen printing paint. The paint comprises the following components in parts by weight: 43-45 parts of white ink, 25-27 parts of yellow ink, 6-8 parts of black ink, 17-19 parts of AEL navy, 2-4 parts of varnish, 3-5 parts of flux and 1-2 parts of coupling agent. The paint has the advantages of less pollution, high product quality, lower production cost, economy and practicability.

Description

[0001] technical field [0002] The invention relates to a glass metal screen printing paint, in particular to a dark blue glass metal screen printing paint and a production process thereof. [0003] Background technique [0004] At present, the graphic printing on the glass surface mainly adopts screen printing method, cleans the glass to be screen printed, prints the ink on the surface of the glass, and then adopts the curing measures of the ink to make the pattern firm and durable. The printing ink is dried To dry, the light color is lighter than the undried one after drying, and the dark color is darker after drying. In addition, whether the color tone of the ink is different before and after drying during printing is a problem that is easily overlooked. Generally speaking, for screen printing inks that are dried by heat-setting and light-setting, the color changes in shades, and the colorants and binders of organic inks are all organic matter. This kind of ink has a g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/14C09D11/06C09D11/10C09D11/02C03C17/00C09D11/105
Inventor 张玉平
Owner NANTONG KST GLASS