Heat-conducting flame-retardant polyethylene terephthalate composite and preparation method thereof

A technology of ethylene glycol phthalate and composite materials, which is applied in the field of thermally conductive and flame-retardant polyethylene terephthalate composite materials and its preparation, and can solve application restrictions, limited applications, and unimproved flame retardant properties, etc. problems, achieve good flame retardant properties, excellent thermal conductivity, and good mechanical properties

Active Publication Date: 2012-05-30
HEFEI GENIUS NEW MATERIALS
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent CN 101805496 A discloses a new type of halogen-free flame-retardant reinforced polyester alloy (ETP), whose flame-retardant performance reaches the U.S. UL94 0.8mm V-0 level, with excellent mechanical properties, and can replace higher-priced halogen-free flame-retardant PBT, PC, PA and other materials have good molding effect and do not affect color matching, but their further application is limited due to the lack

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-conducting flame-retardant polyethylene terephthalate composite and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Embodiment 1 (by weight, the same below)

[0030] 50 parts of polyethylene terephthalate, 20 parts of thermal conductivity silicon carbide whiskers, 12 parts of flame retardant polydibromostyrene, 6 parts of flame retardant synergist antimony trioxide, 10 parts of toughening agent GMA, 0.5 part of silane coupling agent, 0.5 part of antioxidant ST-3610, 1 part of processing aid calcium stearate.

Embodiment 2

[0032] 40 parts of polyethylene terephthalate, 30 parts of silicon carbide whiskers as a thermal conductivity agent, 12 parts of polydibromostyrene as a flame retardant, 6 parts of antimony trioxide as a flame retardant synergist, and 10 parts of toughening agent GMA , 0.5 parts of silane coupling agent, 0.5 parts of antioxidant ST-3610, 1 part of processing aid calcium stearate.

Embodiment 3

[0034] 30 parts of polyethylene terephthalate, 40 parts of aluminum nitride whisker as heat conduction agent, 12 parts of flame retardant isophenyl propyl phosphate, 6 parts of antimony trioxide as flame retardant synergist, toughening agent GMA 10 parts, 0.5 part of silane coupling agent, 0.5 part of antioxidant P262, 1 part of processing aid calcium stearate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a heat-conducting flame-retardant polyethylene terephthalate composite, which comprises, by weight, 30-50 parts of polyethylene terephthalate, 20-40 parts of heat-conducting agent, 12-15 parts of flame retardant, 6-8 parts of flame retardant synergist, 5-10 parts of flexibilizer, 0.5-2 parts of coupling agent, 0.3-0.5 part of antioxidant and 0.5-1 part of processing aid. The composite made by the preparation method has excellent heat conductivity and flame retardancy and further has fine mechanical property, and is widely applicable to electronic and electrical components having high requirement for heat dissipation, and applicable range of PET (polyethylene terephthalate) in fields of electronics, electrical appliances, automobiles, home appliances and the like is widened.

Description

technical field [0001] The invention relates to a PET composite material, in particular to a thermally conductive and flame-retardant polyethylene terephthalate composite material and a preparation method thereof. Background technique [0002] Polyethylene terephthalate (PET) is the lowest price among engineering plastics and has high cost performance. PET is a milky white or light yellow, highly crystalline polymer with a smooth and shiny surface. It has excellent physical and mechanical properties in a wide temperature range. The long-term use temperature can reach 120°C. Under the same conditions, its electrical properties are still good, but its corona resistance is poor, and its creep resistance, fatigue resistance, friction resistance, and dimensional stability are all good. There are ester bonds in the PET molecular chain, which will decompose under the action of strong acid, strong alkali and water vapor. It is resistant to organic solvents and weather resistance. I...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/02C08L23/08C08L33/08C08L33/14C08K13/04C08K7/10C08K7/04C08K7/08B29B9/06
Inventor 章园红
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap