Steel for freight train connecting piece and preparation method thereof

A technology for connecting parts and trains, which is applied in the field of alloy structural steel, and can solve the problems that the comprehensive mechanical properties and low temperature impact properties cannot be well satisfied.

Active Publication Date: 2012-07-04
LAIWU IRON & STEEL GRP
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is mainly aimed at the fact that the comprehensive mechanical properties and low-temperature impact performance of the current freight train connectors cannot well meet the requirements of high-speed and heavy-duty railway vehicles. For this, the present invention provides a steel for freight train

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel for freight train connecting piece and preparation method thereof
  • Steel for freight train connecting piece and preparation method thereof
  • Steel for freight train connecting piece and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0035] Preparation of steel for freight train connectors. The steel products are produced by UHP ultra-power electric furnace, LF refining outside the furnace, VD vacuum degassing treatment, continuous casting casting slabs, and rolling into lumber. Each embodiment produces steel products with a specification of Φ150mm. The specific production process is as follows:

[0036] (1) Smelting: use electric furnace smelting, control the end point of molten steel [C]=0.10%-0.15%, [P]≤0.015%, the content of residual elements meets the design requirements, and the tapping temperature of molten steel is 1660°C-1670°C; LF The smelting time of refining is 35 minutes; vacuum treatment after refining, the vacuum degree of VD furnace is controlled to be less than 67Pa, and the holding time is 15 minutes.

[0037] (2) Pouring: continuous casting full protection pouring, control the liquid level fluctuation of the crystallizer to 700±2mm, the liquid level fluctuation of the tundish to 800±25...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides steel for a freight train connecting piece and a preparation method thereof. The steel for the freight train connecting piece comprises the following chemical ingredients in percentage by mass: 0.24-0.28 percent of C, 0.20-0.40 percent of Si, 1.20-1.50 percent of Mn, 0.50-0.65 percent of Cr, 0.45-0.65 percent of Ni, 0.20-0.30 percent of Mo, 0.03-0.05 percent of Ti, 0.025-0.040 percent of Al, less than or equal to 0.020 percent of S, less than or equal to 0.020 percent of P, less than or equal to 0.15 percent of Cu, less than or equal to 15 ppm of O, less than or equal to 1.5 ppm of H and the balance of Fe and inevitable impurities. According to the invention, as the steel for the freight train is adopted, the mechanical properties of strength, low-temperature impact performance, fatigue life and the like of the connecting piece can be improved, so that the development of railway vehicles towards the high-speed heavy-load direction can be improved, and railway accidents caused by the connecting piece are reduced or avoided.

Description

technical field [0001] The invention belongs to the technical field of alloy structural steels, in particular, the invention relates to a steel for freight train connectors and a preparation method thereof. Background technique [0002] The freight train connector is an important part of the railway vehicle installation, and it directly completes the transmission of the longitudinal force between the vehicles when the vehicles are towed, connected and buffered. The connecting parts of trains are used in harsh conditions and are subject to strong impact, especially in winter, they are prone to breakage. Judging from the inspection and maintenance of freight cars currently in operation, about 70% of the problems occur on the connecting parts of freight cars. The comprehensive mechanical properties, low-temperature impact properties and fatigue life of steel used in freight trains are more demanding. [0003] At present, some manufacturers have carried out trial production res...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/50C21C7/10B22D11/18C21D8/06
Inventor 徐锡坤裴建华翟正龙张伟范黎明李法兴杜国强戈文英刘永昌卢乃双
Owner LAIWU IRON & STEEL GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap