Preparation method of porous nickel oxide/tin dioxide micro/nano spheres

A technology of tin dioxide and micro-nano spheres, which is applied in the direction of material resistance, etc., can solve the problems of inability to realize the regulation of the morphology and microstructure of tin dioxide nanocrystals, restrict gas-sensing characteristics, and the response sensitivity is not high enough to achieve porous The effect of uniform pore size distribution, stable sensitive performance and high sensitive response

Inactive Publication Date: 2012-09-19
ANHUI NORMAL UNIV
View PDF2 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The tin dioxide rod-shaped nanocrystals prepared by this method have a certain sensitive response to ethanol gas, but the response sensitivity is not high, mainly because the sensitive film formed by the extremely small tin dioxide nanorods will cause a large number of closed pores, It blocks the outside gas from reaching the inside of the sensitive film, thus restricting the further improvement of its gas-sensing properties, especially the improvement of sensitivity; regulation of structure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of porous nickel oxide/tin dioxide micro/nano spheres
  • Preparation method of porous nickel oxide/tin dioxide micro/nano spheres
  • Preparation method of porous nickel oxide/tin dioxide micro/nano spheres

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Dissolve the raw material of sodium stannate in water, adjust the pH value of the solution to 12.60 with 5.0M sodium hydroxide, prepare 30 ml of 0.5M sodium stannate solution, then add 3 ml of concentrated ammonia water (mass percentage concentration is 25.0-28.0% ), under magnetic stirring at a speed of 60 rpm, add 15 ml of 1.0M nickel sulfate solution to obtain a mixed solution;

[0041] Standing and aging for 6 hours at a temperature of 80°C, a light green precipitate was obtained; the light green precipitate was filtered, washed, and dried to obtain a micronano-spherical nickel hydroxystannate precursor. The product characterization results are shown in the appendix figure 1 And attached figure 2 shown;

[0042] Micronano spherical nickel hydroxystannate precursor at 700 o C roasting for 2h, after natural cooling, light yellow porous micro-nano spherical NiO / SnO 2 Mixture powder, product characterization results are attached image 3 And attached Figure 4 sho...

Embodiment 2

[0044] Dissolve the tin tetrachloride pentahydrate raw material in water, adjust the pH value of the solution to 13.50 with 5.0M sodium hydroxide, prepare 30 milliliters of 0.5M sodium stannate solution, then add 4 milliliters of concentrated ammonia water (mass percentage concentration is 25.0 -28.0%), under magnetic stirring at a speed of 50 rpm, add 15 ml of 1.0M nickel sulfate solution to obtain a mixed solution;

[0045] Standing and aging at a temperature of 60°C for 6 hours, a light green precipitate was obtained; the light green precipitate was filtered, washed, and dried to obtain a micronano-spherical nickel hydroxystannate precursor;

[0046] The micro-nano spherical nickel hydroxystannate precursor was heated at 720 o C roasting for 2h, after natural cooling, light yellow porous micro-nano spherical NiO / SnO 2 Hybrid powder.

Embodiment 3

[0048] Dissolve the tin tetrachloride pentahydrate raw material in water, adjust the pH value of the solution to 11.80 with 5.0M sodium hydroxide, prepare 30 milliliters of 0.5M sodium stannate solution, then add 6 milliliters of concentrated ammonia water (mass percentage concentration is 25.0 -28.0%), under magnetic stirring with a rotating speed of 80 rpm, add 15 ml of 1.0M nickel sulfate solution to obtain a mixed solution;

[0049] Standing and aging at 60° C. for 8 hours, a light green precipitate was obtained. The light green precipitate is filtered, washed, and dried to obtain a micro-nano spherical nickel hydroxystannate precursor;

[0050] Micro-nano spherical nickel hydroxystannate precursor at 800 o C roasting for 2h, after natural cooling, light yellow porous micro-nano spherical NiO / SnO 2 Hybrid powder.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
pore size distributionaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of porous nickel oxide / tin dioxide micro / nano spheres, which comprises the following steps: stirring tin tetrachloride pentahydrate, nickel sulfate hexahydrate, sodium hydroxide and ammonia water which are used as raw materials, heating, separating, washing, drying and the like to obtain micro / nano spherical hydroxy nickel stannate; and roasting a micro / nano spherical NiSn(OH)6 precursor at high temperature, and cooling to respectively obtain porous micro / nano spherical NiO / SnO2 powder. The micro / nano spherical NiO / SnO2 product prepared by the method disclosed by the invention is light green powder, and has the advantages of large specific area and good product quality. The impedance gas sensing element prepared from the micro / nano spherical NiO / SnO2 powder has high sensitivity, and the sensitivity S value for 100ppm methylbenzene and formaldehyde gases is respectively up to 19.8 and 27.6.

Description

technical field [0001] The invention belongs to the technical field of preparation methods of micro-nano tin-based compounds, and in particular relates to a preparation method of micro-nano spherical nickel hydroxystannate and porous oxygen nickel / tin dioxide powder. Background technique [0002] Gas sensor is a type of sensor widely used in sensor systems in my country, and has been widely used in the fields of environmental protection, medical, automobile, metallurgy and chemical industry. In recent years, gas sensors have been used more and more widely, the most important of which are to prevent accidents, improve the quality of the living environment, ensure the consistency of production process conditions, and protect the environment. Semiconductor gas sensors have a series of advantages such as high sensitivity, simple structure, convenient use, and low price. Therefore, semiconductor gas sensors have always been the main gas sensors at home and abroad. [0003] Tin d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G01N27/12
Inventor 黄家锐王影影谷翠萍
Owner ANHUI NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap