Cement based capillary crystalline high-performance waterproofing powder and application thereof

A osmotic crystalline, cement-based technology, applied in the field of cement-based osmotic crystalline waterproof materials, can solve the problems of low manufacturing cost and production efficiency, poor waterproof effect, difficult factory production, etc., to improve construction, reduce shrinkage, Reduce the effect of flocculation

Active Publication Date: 2013-07-24
ANHUI LENCAQI BUILDING MATERIAL
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Chinese patents CN1587173 and CN1472258 mix the cement-based waterproof material with water and apply it on the surface of the base surface or sprinkle the dry powder on the newly poured concrete surface, and the waterproof effect is relatively poor; Chinese patent CN101074355 is an emulsion type waterproof material, which is suitable for construction site production , it is difficult to produce in a factory, so the manufacturing cost and production efficiency are low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cement based capillary crystalline high-performance waterproofing powder and application thereof
  • Cement based capillary crystalline high-performance waterproofing powder and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] In specific implementation, the raw material composition of cement-based permeable crystalline high-performance waterproof material according to parts by mass is listed in Table 1:

[0030] Table 1 Proportion of cement-based permeable crystalline high-performance waterproof materials

[0031]

[0032] The active masterbatch contains calcium carbonate and calcium chloride. The mass ratio of calcium carbonate and calcium chloride is 1:1. The total mass percentage of calcium carbonate and calcium chloride is not less than 97% of the active masterbatch for permeating crystallization. %; Cellulose is non-ionic cellulose hydroxypropyl methyl ether; rubber powder is a rubber powder copolymerized with vinyl tertiary carbonate and vinyl ester at a ratio of 1:2.27 by mass; water reducing agent is Powdered naphthalene water reducer, commonly used naphthalenesulfonate formaldehyde condensate; Portland cement particle size is 0.025-0.04mm; quartz sand particle size is 0.08-0.2mm; calcium...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a cement based capillary crystalline high-performance waterproofing powder and an application thereof. The cement based capillary crystalline high-performance waterproofing powder is characterized in that inorganic materials of Portland cement, quartz sand and the like serve as a base, active compound capillary crystalline master batch, polymers and other various auxiliarymaterials are added and mixed to prepare powder waterproofing materials; and the cement based capillary crystalline high-performance waterproofing powder includes, by weight, 35-50 parts of the Portland cement, 25-32 parts of the quartz sand, 2-6 parts of the capillary crystalline active master batch, 0-10 parts of calcium carbonate, 5-13 parts of talcum powders, 0.1-0.2 part of cellulose, 6-12 parts of rubber powders, 0.55-1.2 parts of water reducers, 0.1-0.4 part of power organic silicon defoamer and 4.1-5.8 parts of complexing agents. Various raw materials are uniformly stirred in a mixer to obtain the cement based capillary crystalline high-performance waterproofing powder, and the cement based capillary crystalline high-performance waterproofing powder is mixed with a certain amount of clear water to prepare the waterproofing materials. The cement based capillary crystalline high-performance waterproofing powder is simple in preparing, convenient to use and good in water resistance and anti-permeability.

Description

Technical field [0001] The invention belongs to a cement-based permeable crystalline waterproof material and its application, and specifically relates to a cement, mortar, concrete waterproof and anti-leakage material used in dams, canals, river beds, bridges, tunnels, underground, construction and other projects High-performance cement-based permeable crystalline waterproof material. Background technique [0002] At present, there are many waterproof materials and structures developed and used. Generally speaking, it can be divided into two categories: flexible waterproof and rigid waterproof. Years of practice have proved that although traditional flexible waterproof materials such as polymer coils and coatings have the advantages of flexibility and convenient construction, they have weak adhesion to the base concrete, especially when the base is wet or has water seepage. It cannot be used, and it is not suitable for waterproofing the back surface and wet base surface. On the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B111/27
Inventor 朱厚信乔启信吴涛
Owner ANHUI LENCAQI BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products