Novel protective agent for immersion type protection of stone material and preparation method thereof

A preparation method and technology of protective agent, which is applied in the field of protective agent and preparation of new stone immersion protection, can solve the problems of impossibility, saturation of stone protective agent, affecting the protective effect and service life, etc., so as to improve the protective effect and prolong The effect of service life, high economy and practicality

Inactive Publication Date: 2012-10-17
SHENZHEN UNION STONE DECORATION TECH
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the process of protecting stone is to use a brush to apply the protective agent on the surface of the stone, but this process has many disadvantages: this method of applying the protective agent often has missing areas, such as the bottom surface where the stone board is placed, and secondly , manual operation can never be perfect, there will be parts that are missed, and this method of applying protective agent cannot saturate the stone protective agent, which will obviously affect the protective effect and service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0024] Example: Take 200ml of butyltriethoxysilane and propenyltriethoxysilane of the same volume, pour them into a container and mix them, and keep them at a temperature of 60 degrees Celsius for 20 minutes to obtain solution A; then take hexachloro Put 5ml of platinum acid, 10ml of dibutyltin dilaurate and 35ml of p-toluenesulfonic acid into another vessel, and keep it at 50 degrees Celsius for 40 minutes to obtain solution B; then mix the obtained solution A and solution B Mix and dissolve in 300ml of absolute ethanol, stir well, and then keep it at 50 degrees Celsius for 30 minutes; obtain solution C, then put 250ml of water into the obtained solution C, and stir well to obtain the protective agent.

[0025] During the preparation process, the ratio of the protective agent is as follows:

[0026] water 25%,

[0027] Absolute ethanol 30%,

[0028] Butyltriethoxysilane 20%,

[0029] Acryltriethoxysilane 20%,

[0030] p-toluenesulfonic acid 3.5%,

[0031] Dibutyltin Dila...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method for immersion type protection of a stone material. The preparation method comprises the following steps: mixing butyl-triethoxysilane and allyl-triethoxysilane according to a volume ratio of 1: 1 and maintaining an obtained mixture at a temperature of 60 DEG C for 20 min so as to obtain a solution A (with a volume accounting for 40% of a total solution); mixing hexachloroplatinic acid, dibutyltin dilaurate and p-toluenesulfonic acid according to a volume ratio of 0.5: 1: 3.5 and maintaining an obtained mixture at a temperature of 50 DEG C for 40 min so as to obtain a solution B (with a volume accounting for 5% of the total solution); dissolving the solution A and the solution B in absolute alcohol (with a volume accounting for 30% of the total solution), carrying out full stirring and maintaining an obtained mixture at a temperature of 50 DEG C for 30 min; and adding a proper amount of water (with a volume accounting for 25% of the total solution) into a finally-obtained solution. The protective agent provided in the invention enables comprehensive and saturated protection to be realized, protection effects to be improved and a service life to be prolonged and has high economical efficiency and practicality.

Description

technical field [0001] The invention relates to a protective agent and a preparation method for a novel stone immersion protection. Background technique [0002] At present, the raw materials used for decorative stone are mainly marble and granite. Natural stones have a large number of voids of various sizes. Through capillary phenomena, pollutants on the surface or bottom of the stone can penetrate into the interior of the stone through these voids, forming a difficult Remove water spots, white blooms, rust and stains. In order to deal with this problem, stone protective agents have been used in the stone processing industry in recent years. [0003] The current stone protective agents are mainly organosilanes, which are penetrating protective agents. The principle of penetrating protective agents is to penetrate organic matter into the surface and deep layers of stone through solvents, but do not block the capillary pores of stone. Most of these protective agents use Most...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/50C04B41/66
Inventor 罗凌利罗斯特陈幼杰屈花艳谢细球陈伟华
Owner SHENZHEN UNION STONE DECORATION TECH