Composite structure plate of recombination bamboo wood and medium-density fiberboard and manufacture method thereof

A technology for recombining bamboo and composite structures, which is applied in the direction of manufacturing tools, joining of wooden veneers, wood processing appliances, etc., can solve the problem of low raw material utilization rate and poor quality controllability of wood rotary cut veneer and bamboo curtain and bamboo mat High, complex processing technology and other issues, to achieve excellent anti-ultraviolet performance, expand the scope and field of use, and achieve the effect of uniform material

Inactive Publication Date: 2012-11-14
INT CENT FOR BAMBOO & RATTAN
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the raw material utilization rate of wood rotary-cut veneer and bamboo curtain and bamboo mat is very low. The yield of wood rotary-cut veneer is only about 60%, and the yield of bamboo curtain and bamboo mat plywood is even lower than 50%.
Regardless of whether it is unit processing or plate making, the processing technology is relatively complicated, labor-intensive, and the quality controllability is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite structure plate of recombination bamboo wood and medium-density fiberboard and manufacture method thereof
  • Composite structure plate of recombination bamboo wood and medium-density fiberboard and manufacture method thereof
  • Composite structure plate of recombination bamboo wood and medium-density fiberboard and manufacture method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The present embodiment provides a kind of recombined bamboo and medium-density fiberboard composite structure board, and it can be used for making doors and windows (such as double-layer structure doors and windows) etc., structure such as figure 1 shown. The boards used in the composite structure board are medium density fiberboard 1 produced from wood fiber (single tree species or mixed tree species with similar properties) and recombined bamboo material 2 obtained by dipping and molding bamboo tow (Moso bamboo or Ci bamboo).

[0040] The structure of the composite structural board provided in this embodiment is based on recombined bamboo 2, and the upper layer is glued with a medium density fiberboard 1 coated with isocyanate glue on one side, which is manufactured according to the following steps:

[0041] Material selection: use 20mm, 25mm thick medium density fiberboard with a density of 0.75g / cm 3 , the water content is 8%; the selected density is 1.05g / cm 3 , ...

Embodiment 2

[0054] This embodiment provides a composite structure board of recombined bamboo and medium density fiberboard, which can be used to manufacture floors, with a structure such as figure 2 shown. The boards used in the composite structure board are medium density fiberboard 1 produced from wood fiber (single tree species or mixed tree species with similar properties) and recombined bamboo material 2 obtained by dipping and molding bamboo tow (Moso bamboo or Ci bamboo).

[0055] The structure of the composite structure board provided by this embodiment is a medium density fiberboard 1 coated with isocyanate glue on both sides as the core layer, and a layer of recombined bamboo 2 coated with isocyanate glue on one side is glued to the top and bottom of it. It is manufactured according to the following steps of:

[0056] Material selection: use 9mm thick medium density fiberboard with a density of 0.75g / cm 3 , the water content is 8%; the selected density is 1.05g / cm 3 , Recomb...

Embodiment 3

[0066] This embodiment provides a composite structural board of recombined bamboo and medium density fiberboard, which can be used to manufacture building templates, with a structure such as figure 2 shown. The boards used in the composite structure board are medium density fiberboard 1 produced from wood fiber (single tree species or mixed tree species with similar properties) and recombined bamboo material 2 obtained by dipping and molding bamboo tow (Moso bamboo or Ci bamboo).

[0067] The structure of the composite structure board provided by this embodiment is a medium density fiberboard 1 coated with isocyanate glue on both sides as the core layer, and a layer of recombined bamboo 2 coated with isocyanate glue on one side is glued to the top and bottom of it. It is manufactured according to the following steps of:

[0068] Material selection: use 10mm thick medium density fiberboard with a density of 0.75g / cm 3 , the water content is 8%; the selected density is 1.05g / ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a composite structure plate of recombination bamboo wood and a medium-density fiberboard and a manufacture method thereof. The composite structure plate is composed of at least one layer of recombination bamboo wood and at least one layer of medium density fiberboard, and the thickness of the composite structure plate is 7-90 mm. The manufacture method includes the following steps: coating weather resistance glue on the recombination bamboo wood and the medium-density fiberboard, and coating the weather resistant glue on a contact face or coating the weather resistance glue on one lateral surface of the contact face; assembling the recombination bamboo wood and the medium-density fiberboard with the weather resistance glue to obtain a plate blank; and cold pressing, maintaining pressure, relieving pressure and preserving the plate blank to obtain the composite structure plate of the recombination bamboo wood and the medium-density fiberboard. The composite structure plate has good structure performance and is capable of conducting continuous production, simple in process, high in production efficiency, stable and reliable in product performance, remarkable in cost advantage, energy-saving, environment-friendly and suitable for various use purposes.

Description

technical field [0001] The invention relates to a novel composite structural panel for structure and a manufacturing method thereof, in particular to a composite structural panel of recombined bamboo and medium-density fiberboard and a manufacturing method thereof, belonging to the technical field of wood-based panel manufacturing in the wood / bamboo industry. Background technique [0002] As a characteristic and advantageous resource in my country, bamboo has the characteristics of high strength and good toughness. It has always been considered as an ideal structural material and has been widely used, such as bamboo plywood for car floor and building formwork. However, due to the lack of dedicated automatic mechanical processing equipment, most of the processes (such as breaking bamboo strips, weaving curtains and mats, etc.) still remain in the manual production stage for a long time, and cannot form large-scale continuous production. The development of recombined bamboo pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27D1/04B27G11/00B27D1/08
Inventor 费本华王晓欢杨峰宋莎莎陶仁中
Owner INT CENT FOR BAMBOO & RATTAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap