Optically-transparent dual-curing adhesive

An optically transparent, adhesive technology, applied in the direction of adhesive types, non-polymer organic compound adhesives, ester copolymer adhesives, etc., can solve the corrosion of unbonded parts, and the adhesive cannot be fully cured , peeling, etc.

Inactive Publication Date: 2013-02-13
HENKEL KGAA +1
View PDF13 Cites 34 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0016] However, the various dual-curing adhesives described above cannot be used to solve the problem to be solved in the present invention, that is, when there is a shadow, that is, a part where light cannot pass through, between the touch screen of ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Optically-transparent dual-curing adhesive
  • Optically-transparent dual-curing adhesive
  • Optically-transparent dual-curing adhesive

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0102]

[0103] The adhesive composition of the present invention can be prepared by adding and mixing the components of the adhesive composition described above in set proportions in a substantially light-proof mixing vessel with conventional stirring means. Mixing is usually carried out at ambient temperature, but may also be carried out at a temperature slightly higher or lower than ambient temperature. The mixing should be carried out for a period of time long enough to obtain a homogeneous combination of the components, thereby obtaining the adhesive composition. The thus obtained adhesive composition is stored away from light; it is used for subsequent bonding between the touch screen of the optoelectronic product and the substrate.

[0104] The volume of the mixing container is not specifically limited, and it may be, for example, about 1-100 L, or 5-50 L, or 10-30 L, etc. according to specific preparation requirements. The mixing vessel can be a commercially availab...

Embodiment 1

[0138] Embodiment 1 (according to the present invention)

[0139] Adhesive composition 1 was prepared according to the composition and preparation method of the following table 1:

[0140] Table 1

[0141] components

Content

Urethane oligomers 1-1 containing (meth)acryloyloxy groups

70 parts by weight

(Meth)acrylate 4-1

10 parts by weight

(meth)acrylate 4-2

7 parts by weight

(meth)acrylate 4-3

7 parts by weight

UV photoinitiator 5-1

2 parts by weight

UV photoinitiator 5-2

1 part by weight

Thermal Initiator 6-1

2 parts by weight

Thermal Initiator 6-2

1 part by weight

[0142] The preparation method of adhesive composition is as follows:

[0143] Under the condition of avoiding light, the above-mentioned components (total 100g) were added successively in the plastic barrel with a capacity of 150g, and put into the SpeedMixer produced by FlackTech Inc. TM In the mixer, at...

Embodiment 2

[0144] Embodiment 2 (according to the present invention)

[0145] Adhesive composition 2 is prepared according to the composition of the following table 2 and the preparation method as in Example 1:

[0146] Table 2

[0147] components

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an optically-transparent dual-curing adhesive, and a preparation method and a use thereof, and concretely relates to an optically-transparent, ultraviolet-curable and heat-curable adhesive, for example, the adhesive can be used for bonding the touch screen and the substrate of an electronic product.

Description

technical field [0001] The present invention relates to an optically transparent dual-cure adhesive, as well as a preparation method and use of the dual-cure adhesive. More specifically, the present invention relates to an optically clear adhesive capable of both UV curing and heat curing, which can be used, for example, for bonding touch screens and substrates of electronic products. Background technique [0002] Since the UV-curable (hereinafter referred to as: UV-curable) adhesive was reported in the 1960s, a lot of research has been done on it and remarkable achievements have been made. The UV light-curing adhesive refers to an adhesive that can be cured rapidly under ultraviolet light irradiation. Today, UV light-curing adhesives have been successfully applied in many industrial assembly fields, especially those that require rapid assembly, such as liquid crystal display (LCD) manufacturing, optical product manufacturing such as cameras, optical disc manufacturing, wat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J4/02C09J4/06G02F1/133
CPCC09J133/08C08F283/008C09J4/06C09J109/00C09J175/04C09J175/14C08F222/1065C08F220/1811C08F220/20C08F220/281C09J133/06C09J133/14C09J175/16
Inventor 张瑞吕道强
Owner HENKEL KGAA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap