Preparation method of porous spherical compound humidifying agent
A technology of humidity-conditioning agent and porous spherical type, which is applied in the field of preparation of porous spherical composite humidity-conditioning agent, which can solve the problems of insufficient number of pores, moisture capacity and moisture absorption and desorption performance to be further improved, so as to increase the specific surface area, Fast response to moisture absorption and desorption, and convenient reuse
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] Embodiment 1: a kind of preparation method of porous spherical composite humidity-conditioning agent is characterized in that the steps are as follows:
[0017] a. activating the zeolite at 450° C. for 2 hours to obtain the activated zeolite;
[0018] b. Take 30 parts of polyacrylic acid in parts by mass, add to 115 parts of sodium hydroxide solution (dissolve 15 parts of sodium hydroxide in 100 parts of distilled water) for neutralization; then add 0.9 parts of sodium carboxymethyl cellulose, 3 parts Add the activated zeolite and 0.3 parts of potassium persulfate into the reactor filled with the above solution (the solution obtained after the neutralization of polyacrylic acid and sodium hydroxide solution), and stir the reaction at a temperature of 70 ° C. After about 30 minutes of reaction 1. Dissolve 0.3 parts of aluminum chloride in 10 parts of distilled water to make a solution and add it to the above reactor, then add 0.3 parts of N,N-methylenebisacrylamide, cont...
Embodiment 2
[0022] Embodiment 2: a kind of preparation method of porous spherical composite humidity-conditioning agent is characterized in that the steps are as follows:
[0023] a. activating the zeolite at 450° C. for 2.5 hours to obtain the activated zeolite;
[0024] b. Take 30 parts of polyacrylic acid in parts by mass, add to 115 parts of sodium hydroxide solution (dissolve 15 parts of sodium hydroxide in 100 parts of distilled water) to neutralize; then add 1.8 parts of sodium carboxymethyl cellulose, 4.5 parts Add the activated zeolite and 0.3 parts of potassium persulfate into the reactor filled with the above solution (the solution obtained after the neutralization of polyacrylic acid and sodium hydroxide solution), and stir the reaction at a temperature of 75 ° C. After about 30 minutes of reaction 1. Dissolve 0.3 parts of aluminum chloride in 10 parts of distilled water to make a solution and add it to the above reactor, then add 0.3 parts of N,N-methylenebisacrylamide, conti...
Embodiment 3
[0028] Embodiment 3: a kind of preparation method of porous spherical composite humidity-conditioning agent, it is characterized in that the steps are as follows:
[0029] a. activating the zeolite at 450° C. for 3 hours to obtain the activated zeolite;
[0030] b. Take 30 parts of polyacrylic acid in parts by mass, add to 115 parts of sodium hydroxide solution (dissolve 15 parts of sodium hydroxide in 100 parts of distilled water) for neutralization; then add 2.7 parts of sodium carboxymethyl cellulose, 6 parts Add the activated zeolite and 0.3 parts of potassium persulfate into the reactor filled with the above solution (the solution obtained after the neutralization of polyacrylic acid and sodium hydroxide solution), and stir the reaction at a temperature of 80 ° C. After about 30 minutes of reaction 1. Dissolve 0.3 parts of aluminum chloride in 10 parts of distilled water to make a solution and add it to the above reactor, then add 0.3 parts of N,N-methylenebisacrylamide, ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com