Lubricant for wood-plastic composite material and preparation method of lubricant
A technology of wood-plastic composite materials and lubricants, which is applied in the field of lubricant preparation, can solve the problems of unfavorable interface compatibility of hydroxyl groups, etc., and achieve the effects of low toxicity, enhanced adhesion, and simple synthesis process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0031] A lubricant for wood-plastic composite materials, which is prepared by the reaction of the following raw material ratios:
[0032] 12-Hydroxystearic Acid 10g
[0033] Pentaerythritol 5g
[0034] Dibutyltin dilaurate 0.1ml
[0035] Toluene diisocyanate 5ml
[0036] Dimethylformamide 50ml
[0037] Xylene 100ml.
[0038] The preparation method of this lubricant comprises the following steps:
[0039] (1) Put 12-hydroxystearic acid in a flask, add xylene, and heat it to 70°C to completely dissolve 12-hydroxystearic acid in xylene;
[0040] (2) Add dibutyltin dilaurate dropwise to the product of step (1), keep the temperature at 70°C, then stir it evenly, then add toluene diisocyanate dropwise, and react at a temperature of 75°C for 0.5h;
[0041] (3) Dissolve pentaerythritol in dimethylformamide, and after it has completely reacted, add the product dropwise to the flask in step (2) to make it react with the product in step (2). Control the dripping within 0.8h. After...
Embodiment 2
[0048] A lubricant for wood-plastic composite materials, which is prepared by the reaction of the following raw material ratios:
[0049] 12-Hydroxystearic Acid 15g
[0050] Pentaerythritol 8g
[0051] Dibutyltin dilaurate 0.3ml
[0052] Toluene diisocyanate 8ml
[0053] Dimethylformamide 75ml
[0054] Xylene 125ml.
[0055] The preparation method of this lubricant comprises the following steps:
[0056] (1) Put 12-hydroxystearic acid in a flask, add xylene, and heat it to 90°C to completely dissolve 12-hydroxystearic acid in xylene;
[0057] (2) Add dibutyltin dilaurate dropwise to the product of step (1), keep the temperature at 90°C, then stir it evenly, then add toluene diisocyanate dropwise, and react at a temperature of 85°C for 1 hour;
[0058] (3) Dissolve pentaerythritol in dimethylformamide, and after it has completely reacted, add the product dropwise to the flask in step (2) to make it react with the product in step (2). Control the dripping within 1.2h. Aft...
Embodiment 3
[0065] A lubricant for wood-plastic composite materials, which is prepared by the reaction of the following raw material ratios:
[0066] 12-hydroxystearic acid 20g
[0067] Pentaerythritol 10g
[0068] Dibutyltin dilaurate 0.5ml
[0069] Toluene diisocyanate 10ml
[0070] Dimethylformamide 100ml
[0071] Xylene 150ml.
[0072] The preparation method of this lubricant comprises the following steps:
[0073] (1) Put 12-hydroxystearic acid in a flask, add xylene, and heat it to 100°C to completely dissolve 12-hydroxystearic acid in xylene;
[0074] (2) Add dibutyltin dilaurate dropwise to the product of step (1), keep the temperature at 100°C, then stir it evenly, then add toluene diisocyanate dropwise, and react at a temperature of 95°C for 2 hours;
[0075] (3) Dissolve pentaerythritol in dimethylformamide, and after it has completely reacted, add the product dropwise to the flask in step (2) to make it react with the product in step (2). Control the dripping within 1.5...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap