Electroplating PC/ABS (polycarbonate/acrylonitrile-butadiene-styrene) alloy material and preparation method thereof

A technology of alloy materials and ABS resin, which is applied in the field of PC/ABS alloy materials and its preparation, can solve the problems of poor adhesion between the coating and plastic parts, large and sparse particles, low riveting effect of the coating on the surface of plastic parts, etc., and achieve excellent mechanical properties. performance, good molding processability, and the effect of good heat resistance

Active Publication Date: 2015-05-06
中广核俊尔(上海)新材料有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The content of B particles is too small and the particles are large and sparse, or its content is too large and too dense, which will lead to low riveting effect of the coating on the surface of the plastic part, and poor adhesion between the coating and the plastic part.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electroplating PC/ABS (polycarbonate/acrylonitrile-butadiene-styrene) alloy material and preparation method thereof
  • Electroplating PC/ABS (polycarbonate/acrylonitrile-butadiene-styrene) alloy material and preparation method thereof
  • Electroplating PC/ABS (polycarbonate/acrylonitrile-butadiene-styrene) alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-5

[0030] The PC resin, ABS resin, and various additives are added to the high-mixer and mixed at high speed for 2 minutes, then added to the main feeder of the extruder, and then added to the twin-screw extruder for basic granulation. The temperature distribution of the extruder is as follows: from the feed section to the die: 240℃, 260℃, 260℃, 260℃, 255℃, 250℃, 250℃, 250℃, 250℃, die head: 260℃ After the material is extruded, it is water-cooled, pelletized, and then packaged. The pellets were dried in a blast drying oven at 90°C for 4 hours, and then test specimens were prepared by an injection molding machine.

[0031] See Table 1 for the weight parts of each raw material in Examples 1 to 5.

[0032] Table 1 Parts by weight of raw materials in Examples 1 to 5

[0033]

[0034]

[0035] Note: DENKA IP MS-NB is an SMI copolymer, that is, a copolymer of styrene, N-phenylmaleimide, and maleic anhydride. The grade is MS-NB; antioxidant 1010 (four [β-(3 , 5-di-tert-butyl-4-hydroxyphenyl)...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an electroplating PC / ABS (polycarbonate / acrylonitrile-butadiene-styrene) alloy material and a preparation method thereof. The electroplating PC / ABS alloy material comprises the following components in parts by weight: 30-70 parts of PC, 40-60 parts of ABS, 5-30 parts of styrene-acrylonitrile copolymer, 5-30 parts of butadiene graft rubber, 1-3 parts of compatilizer, 1-10 parts of heat-resistance modifier and 0.5-1 part of processing assistant. The alloy material provided by the invention has the advantages of favorable electroplating properties, excellent mechanical properties and favorable heat resistance, and can be used for designing automobile internal and external ornaments, including heat dissipation grids, door grips, vehicle logos, instrument panel decorating strips and the like.

Description

Technical field [0001] The invention relates to a PC / ABS alloy material and a preparation method thereof. Background technique [0002] Polycarbonate (PC) is an engineering plastic with excellent performance. It has the advantages of outstanding impact toughness, wide operating temperature range, good electrical insulation and dimensional stability. It has been used in the automotive and electronic and electrical industries. widely used. However, PC melt viscosity is high, processing and molding are difficult, especially large products are prone to stress cracking, chemical resistance is poor, and the price is relatively high. These shortcomings restrict the application of PC to a certain extent. The performance of styrene-butadiene-acrylonitrile copolymer resin (ABS) is between engineering plastics and general-purpose plastics. It has good impact resistance and processing performance, and the price is relatively cheap, so it has been widely used. However, its heat resistance a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L69/00C08L55/02C08L25/12C08L33/10C08L35/06C08K5/00
Inventor 杨燕黄志杰左绍文顾伟杨仓先
Owner 中广核俊尔(上海)新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com