High aluminum steel special continuous casting crystallizer casting powder

A continuous casting mold and mold slag technology, which is applied in the field of mold slag, can solve the problems of the surface quality of the slab, many inclusions, and difficulty in meeting actual needs.

Active Publication Date: 2015-06-10
XIXIA LONGCHENG METALLURGICAL MATERIALS CO LTD
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] For the continuous casting of this type of steel, the current domestic mold powder products mainly rely on imports. The existing problems are: (1) The cost of mold powder is high, As a result, the production cost of the product remains high; (2) the imported slag cannot be effectively adjusted in time according to the specific process conditions in our country, and it is difficult to meet the actual needs; (3) due to the large number of inclusions and the It is in the shape of a high melting point, so the quality of mold flux is easy to deteriorate during use, resulting in unsmooth process and many problems with the surface quality of the slab, which increases the production cost of iron and steel enterprises, so a low-cost, high-quality surface is required. Special mold flux for continuous casting mold for high aluminum steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High aluminum steel special continuous casting crystallizer casting powder
  • High aluminum steel special continuous casting crystallizer casting powder
  • High aluminum steel special continuous casting crystallizer casting powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The continuous casting mold powder for high aluminum steel provided in this example is shown in the ingredient list 1

[0021]

[0022] Ingredients list 1

[0023] A steel plant continuous casting process: casting section 220*1600mm 2 , Pulling speed 0.8 ~ 1.2m / min.

[0024] When pouring starts, the mold slag of the present invention is evenly pushed into the crystallizer, and it is required to evenly cover the entire molten steel surface. Between 60mm, keep the black slag operation, and do not expose the molten steel surface.

[0025] After pouring, the liquid steel level fluctuates within 5mm, and the casting speed is stable at 0.95m / min. At this time, the thickness of the liquid slag layer is measured to be about 10mm. After that, measure the liquid slag layer every 20 minutes, and its thickness is 8-12mm. During the casting process, the mold slag spreads well in the crystallizer, there is no crusting and agglomeration, ...

Embodiment 2

[0029] For the high-alumina continuous casting mold flux provided in this example, see ingredient list 2:

[0030]

[0031] Ingredients List 2

[0032] B steel plant continuous casting process: casting section 230*1600mm 2 , Pulling speed 0.9 ~ 1.3m / min.

[0033] When pouring starts, the mold slag of the present invention is evenly pushed into the crystallizer, and it is required to evenly cover the entire molten steel surface. Between 60mm, keep the black slag operation, and do not expose the molten steel surface.

[0034]After pouring, the liquid steel level fluctuated within 3mm, and the casting speed was stable at 1.2m / min. At this time, the thickness of the liquid slag layer was measured to be about 10mm. After that, measure the liquid slag layer every 20 minutes, and its thickness is between 9 and 12 mm. During the casting process, the mold slag spreads well in the crystallizer, there is no crusting and agglomeration, the flame is mode...

Embodiment 3

[0038] For the high-alumina continuous casting mold flux provided in this example, see ingredient list 3:

[0039]

[0040] Ingredients list 3

[0041] C steel plant continuous casting process: casting section 220*1600mm 2 , Pulling speed 0.8 ~ 1.4m / min.

[0042] When pouring starts, the mold slag of the present invention is evenly pushed into the crystallizer, and it is required to evenly cover the entire molten steel surface. Between 60mm, keep the black slag operation, and do not expose the molten steel surface.

[0043] After pouring, the fluctuation of liquid steel level is within 6mm, and the casting speed is stable at 1m / min. At this time, the thickness of liquid slag layer is measured to be about 10mm. After that, measure the liquid slag layer every 20 minutes, and its thickness is 10-12mm. During the casting process, the mold slag spreads well in the crystallizer, there is no crusting and agglomeration, the flame is moderate, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high aluminum steel special continuous casting crystallizer casting powder, and the raw material formula proportion of parts by weight of the high aluminum steel special continuous casting crystallizer casting powder includes the premelting material 7 - 13 parts, fluorite powder 9 - 11 parts, industrial soda ash 4 - 6 parts, carbon black 6 parts, earthy graphite 3 - 6 parts, calcium balls 24 - 31 parts, refining slag 17 - 25 parts, lithium carbonate 3 parts, bauxite 9 - 15 parts, barium carbonate 4 parts, manganese carbonate 3 parts and borax 5 parts. The high aluminum continuous casting powder can effectively overcome the quality defects that more inclusions exist in a high aluminum steel continuous casting process and the melting point is high, and the quality of ordinary casting powder is extremely easy to deteriorate in the using process so that the process is not smooth, and cracks and concave pits are easy to appear on the surface of a casting blank and the production cost of iron and steel enterprises is increased. The high aluminum steel special continuous casting crystallizer casting powder achieves the use value maximally under the same resource conditions.

Description

technical field [0001] The invention belongs to the technical field of mold flux, and in particular relates to mold flux for continuous casting molds specially used for high-aluminum steel. Background technique [0002] At present, many steel types in most domestic steel plants use aluminum deoxidation, but for some steel types, their aluminum content is relatively high, such as low-carbon aluminum-killed steel, 38CrMoAl, aluminum-containing stainless steel, high-aluminum TRIP-based steel, etc. , for continuous casting of these steel grades, Al in molten steel 2 o 3 There are many types of inclusions. Due to the high melting point of such inclusions or complexes, it is easy to increase the melting point and viscosity after the mold slag is adsorbed, resulting in deterioration of the performance of the mold slag and poor use effect, resulting in a decline in product quality. reduce the competitiveness of enterprises. [0003] CN 102389955 A discloses a mold flux for con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/111B22D11/07
Inventor 李晓阳张福杜震宇马帅赵春宝屈党军马晓娜王岩王旭阳
Owner XIXIA LONGCHENG METALLURGICAL MATERIALS CO LTD