Multifunctional fully-synthetic cutting fluid and preparation method thereof

A fully synthetic cutting fluid technology, applied in lubricating compositions, petroleum industry, etc., can solve the problems of poor lubricating performance and extreme pressure performance of fully synthetic cutting fluid, affecting the health of operators, and weak antirust ability, etc., to achieve good Environmental friendliness, good cleaning performance, and long cooling effect

Active Publication Date: 2013-10-16
水泽节(山东)环保科技有限公司
View PDF2 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Fully synthetic cutting fluid is composed of a variety of chemical components and does not contain mineral oil. Therefore, the lubricating performance and extreme pressure performance of fully synthetic cutting fluid are relatively poor. Generally, it cannot be used for medium and heavy-duty cutting. In order to achieve the anti-rust effect, Many fully

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Example 1. A preparation method of multifunctional fully synthetic cutting fluid, comprising the steps of:

[0039] (1) Prepare modified vegetable oil, phosphate triethanolamine and other reaction components in the reactor.

[0040] The preparation method of the modified vegetable oil is as follows: add 150kg of vegetable oil into a one-ton reactor, slowly heat it to 90-95°C, and then slowly add 100kg of 20% sodium hydroxide solution for saponification. During the saponification process, slowly Add alcohol amine dropwise to disperse. The total amount of alcohol amine is 200kg. Continue to saponify for one hour to obtain a transparent viscous saponified product. Cool down to 70°C, add 50kg of boric acid, react for one hour, and finally 100kg of deionized water. It can be stored for later use.

[0041] The preparation method of phosphate ester: in a one-ton reaction kettle, add alcohol ether and deionized water (ratio 3:1), stir well, then slowly add phosphorus pentoxid...

Embodiment 2

[0045] Example 2. A preparation method of multifunctional fully synthetic cutting fluid, comprising the steps of:

[0046] (1) Prepare modified vegetable oil, phosphate triethanolamine and other reaction components in the reactor.

[0047] The preparation method of the modified vegetable oil is as follows: add 150kg of vegetable oil into a one-ton reactor, slowly heat it to 90-95°C, and then slowly add 100kg of 20% sodium hydroxide solution for saponification. During the saponification process, slowly Add alcohol amine dropwise to disperse. The total amount of alcohol amine is 200kg. Continue to saponify for one hour to obtain a transparent viscous saponified product. Cool down to 70°C, add 50kg of boric acid, react for one hour, and finally 100kg of deionized water. It can be stored for later use.

[0048] The preparation method of phosphate ester: in a one-ton reaction kettle, add alcohol ether and deionized water (ratio 3:1), stir well, then slowly add phosphorus pentoxid...

Embodiment 3

[0052] Example 3. A preparation method of multifunctional fully synthetic cutting fluid, comprising the steps of:

[0053] (1) Prepare modified vegetable oil, phosphate triethanolamine and other reaction components in the reactor.

[0054] The preparation method of the modified vegetable oil is as follows: add 150kg of vegetable oil into a one-ton reactor, slowly heat it to 90-95°C, and then slowly add 100kg of 20% sodium hydroxide solution for saponification. During the saponification process, slowly Add alcohol amine dropwise to disperse. The total amount of alcohol amine is 200kg. Continue to saponify for one hour to obtain a transparent viscous saponified product. Cool down to 70°C, add 50kg of boric acid, react for one hour, and finally 100kg of deionized water. It can be stored for later use.

[0055] The preparation method of phosphate ester: in a one-ton reaction kettle, add alcohol ether and deionized water (ratio 3:1), stir well, then slowly add phosphorus pentoxid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses multifunctional fully-synthetic cutting fluid and a preparation method thereof. The multifunctional fully-synthetic cutting fluid is prepared from modified vegetable oil, organic carboxylic acid amide, borate, ethanolamine, a polyether activating agent, a non-ferrous metal corrosion inhibitor, triethanolamine oleate, ethanolamine citrate, triethanolamine phosphate, emulsified silicone oil and the like. According to the multifunctional fully-synthetic cutting fluid and the preparation method thereof, an easily-biodegradable special additive combination is adopted, so that the problem that similar products on the market are generally poor in lubricity and rust resistance is solved; a formula does not contain nitrite, benzene and phenol substances, so that waste liquid is easy to process, the destruction to the environment can not be caused, and the environmental friendliness is good; and the multifunctional fully-synthetic cutting fluid can be applied to medium/heavy-load cutting processing and is applicable to automated production equipment, such as numerically-controlled machine tools, processing centers and the like.

Description

technical field [0001] The invention belongs to the technical field of cutting fluid, in particular to a multifunctional fully synthetic cutting fluid and a preparation method thereof. Background technique [0002] The water-based synthetic cutting fluid is in accordance with the national standard GB7631.5-89 "Classification of Lubricants and Related Products (Class L) Part 5; Group M (Metal Processing)", the symbols MAG and MAH correspond to two synthetic cutting fluids. L-MAG type; the concentrate mixed with water is a transparent liquid with anti-rust properties. When used, it is diluted with a certain proportion of water to form a transparent and translucent dilution. It is suitable for various cutting processes such as metal turning and milling. Cooling, antirust; L-MAH type; MAG type concentrate with antifriction and extreme pressure properties. [0003] The national standard GB / T6144-2010 "Synthetic Cutting Fluid" of the People's Republic of China is revised on the b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M173/00C10N40/22
Inventor 郭翠翠
Owner 水泽节(山东)环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap