Method for preparing YBCO (yttrium barium copper oxide) film by taking ethanol as solvent through low-fluorine MOD (metal organic deposition) method

A technology of ethanol solution and ethanol, applied in the field of materials, can solve problems such as environmental hazards of trifluoroacetic acid gas, and achieve the effects of good application prospect, accelerated process and little environmental pollution
CN103352212BInactive Publication Date: 2015-06-17NORTHEASTERN UNIV LIAONING
3 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Patents(China)
Current Assignee / Owner
NORTHEASTERN UNIV LIAONING
Publication Date
2015-06-17
Estimated Expiration
Not applicable · inactive patent

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention discloses a method for preparing a YBCO (yttrium barium copper oxide) film by taking ethanol as a solvent through a low-fluorine MOD (metal organic deposition) method, and belongs to the technical field of materials. The method comprises the following steps: (1) dissolving yttrium acetate and barium trifluoroacetate in water to prepare a yttrium barium solution, boiling and concentrating; (2) adding ethanol, boiling and concentrating; (3) repeating the step (2) for 4-6 times to prepare a yttrium barium ethanol solution; (4) dissolving copper isocaprylate in ethanol to prepare a copper ethanol solution; (5) mixing the copper ethanol solution with the yttrium barium ethanol solution, filtering, reheating and concentrating to prepare a precursor solution; (6) applying the precursor solution to a substrate by spin coating, pyrolyzing and crystallizing. The method has the advantages of low environmental pollution, high production efficiency and the like, and has a good application prospect.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention belongs to the technical field of materials, and in particular relates to a method for preparing YBCO membranes by using ethanol as a solvent and a low-fluorine MOD method. Background technique

[0002] YB 2 Cu 3 o 7-x (YBCO) film is a promising high-temperature superconducting material, which has broad application prospects in electronic devices and other fields; superconducting motors, superconducting strong magnets and high-temperature super tapes, etc., developed based on YBCO film-making technology, It has received more and more attention from research groups in various countries.

[0003] There are many methods for preparing YBCO membranes, which can be roughly divided into two categories: physical methods and chemical methods. Physical methods mainly include pulsed laser deposition (PLD, Pulsed Laser Deposition), ion beam assisted deposition (IBAD, ion beam assisted deposition), direct current sputtering (DCS, direct current sp...