Precursor of lithographic printing plate, its plate-making method, and polyvalent isocyanate compound

A lithographic printing plate, isocyanate technology, applied in lithographic printing equipment, printing, printing process and other directions, can solve problems such as difficult to solve, poor developability, difficult to obtain printing durability, etc.

Active Publication Date: 2016-06-22
FUJIFILM CORP
View PDF78 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] However, in JP-A-2004-212558, Japanese Patent No. 2938397, JP-A-2000-211262, JP-A-2001-277740, JP-A-2002-29162, JP-A-2002-46361, JP-A -In hitherto known lithographic printing plate precursors described in 2002-137562 and JP-A-2002-326470, the printing durability of the image formed by laser exposure is insufficient and therefore additional improvement is required
In particular, it is difficult to obtain sufficient printing durability in images cured in recording materials capable of being recorded with infrared laser light having a photosensitive wavelength of 760 nm or more
In order to increase printing durability, when using a support with a surface with low hydrophilicity, ink also adheres to non-image areas during printing, resulting in printing smudges
Therefore, in recording materials capable of recording with infrared laser light having a photosensitive wavelength of 760 nm or more, it is a problem to obtain good stain resistance and sufficient printing durability
In particular, in on-press development using dampening water and / or printing ink, since developability is poor compared to a system including development with an alkaline developer, smudges tend to appear, making it more difficult to solve the problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Precursor of lithographic printing plate, its plate-making method, and polyvalent isocyanate compound
  • Precursor of lithographic printing plate, its plate-making method, and polyvalent isocyanate compound
  • Precursor of lithographic printing plate, its plate-making method, and polyvalent isocyanate compound

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0070] [Preparation Method of Polymer Fine Particles]

[0071] The polymer fine particles according to the present invention are composed of a polymer obtained by a reaction between an isocyanate compound and a compound having an active hydrogen atom, and the isocyanate compound includes at least the polyvalent isocyanate compound according to the present invention. Therefore, the polymer fine particles according to the present invention can increase printing durability without concomitantly reducing developability.

[0072] The polymer fine particles according to the present invention can be obtained with as in AsashiKondo, Microcapsule , The Nikkan Kogyo Shimbun, Ltd. (1970) and Tamotsu Kondo et al., Microcapsules, It was prepared in the same manner as a hitherto known method for forming microcapsules described in detail in Sankyo Publishing Co., Ltd. (1977).

[0073] Polymer fines with polyurethane / polyurea walls or polyurethane walls were synthesized by interfacial pol...

Embodiment

[0251] The present invention will be described in more detail with reference to the following examples, but the invention should not be construed as being limited thereto. In the examples, unless specifically stated otherwise, with respect to polymer compounds, the molecular weight is expressed as a weight average molecular weight (Mw) and the ratio of repeating units is expressed as a mole percent.

[0252] [Synthesis examples of polyvalent isocyanate adducts NCO-1 to NCO-21]

Synthetic example 1

[0253] Synthesis Example 1: Synthesis of NCO-1

[0254] In 470.7 g of ethyl acetate containing 355.6 g (1.60 mol) of isophorone diisocyanate ([PDI) and 169.6 g (0.40 mol) of polyhydric phenol compound P-2 having the structure shown below To the suspension, a solution containing 471 mg of tin octoate (STANOCT, manufactured by Yoshitomi Pharmaceutical Co., Ltd.) dissolved in 10 g of ethyl acetate was added dropwise over a period of one hour with stirring. After the dropwise addition was completed, stirring was continued for 2 hours and then stirred at 50° C. for 3 hours. Thus, a solution (concentration: 50% by weight) of polyvalent isocyanate adduct NCO-1 was obtained.

[0255] The terminal isocyanate compound obtained above was dibutyl-ureidized with dibutylamine to determine the weight average molecular weight (as calculated in polystyrene units) and its Mw was 24,400.

[0256] The obtained compound was identified by FT-IR (KBr). The data is shown below. FT-IR(KBr)3416cm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
wavelengthaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

To provide a lithographic printing plate precursor which is capable of undergoing image recording with infrared laser and exhibits high printing durability while maintaining stain resistance and preservation stability, and particularly, to provide a lithographic printing plate precursor capable of undergoing on-press development and a plate making method thereof, the invention is directed to a lithographic printing plate precursor comprising a hydrophilic support having thereon an image-recording layer containing (A) a polymer fine particle, (B) a radical polymerizable compound and (C) an infrared absorbing dye, wherein (A) the polymer fine particle is obtained by a reaction between a polyvalent isocyanate compound which is an adduct of a polyhydric phenol compound having two or more hydroxyl groups in its molecule and isophorone diisocyanate and a compound having an active hydrogen atom.

Description

technical field [0001] The present invention relates to a lithographic printing plate precursor capable of so-called direct plate-making in which direct plate-making is performed using various types of lasers based on digital signals such as from a computer, and in particular, relates to printing durability A lithographic printing plate precursor improved in properties, stain resistance, and storage stability, a plate-making method thereof, and a polyvalent isocyanate compound. Background technique [0002] Solid-state lasers, semiconductor lasers, and gas lasers that emit ultraviolet rays, visible light, or infrared rays having a wavelength of 300 to 1,200 nm having a large output and a small size become readily available, and these lasers are very usable for use based on, for example, data from a computer. Recording light source for data-to-plate. Various studies have been conducted on such various laser beam-sensitive recording materials. In particular, a recording mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G03F7/00B41N1/14G03F7/004G03F7/027G03F7/035
CPCB41C1/1008B41C1/1016B41C2201/02B41C2201/04B41C2201/10B41C2201/14B41C2210/04B41C2210/06B41C2210/08B41C2210/10B41C2210/12B41C2210/20B41C2210/22B41C2210/24
Inventor 青岛俊荣佐藤宪晃仓本守
Owner FUJIFILM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com